Process for treating surface of copper foil
Assignee: Mitsui Kinzoku Co Ltd
•
Filing: 1990-02-28
•
Granted: 1992-03-17
•
Expires: 2010-02-28
Abstract
Abstract The present invention relates to a process for treating a surface of a copper foil for producing the copper foil for a printed circuit board in which a zinc layer, a copper layer and a chromate layer are formed in turn on the copper foil. The product of the present invention is excellent in heat resistance and hydrochloric acid resistance and the process according to the present invention does not require the use of dangerous chemicals and is free from any problems on safety.
Inventors
- 👤 Nobuo Kitamura
- 👤 Makoto Fujiki
- 👤 Yukio Kodama
- 👤 Katsuhiro Yoshimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:38
CPC Classifications
C; C23; C23C; C23C28/00; C23C28/30; C23C28/32; C23C28/322; C23C28/3225; C23C28/34; C23C28/345; C23C28/3455; C25; C25D; C25D5/00; C25D5/10; C25D5/627; H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/282; H05K3/38; H05K3/382; H05K3/384; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2203/00; H05K2203/03; H05K2203/0307; H05K2203/07; H05K2203/0703; H05K2203/0723
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
89 words
A process for treating a surface of a copper foil for producing the copper foil for a printed circuit board, comprising the steps of forming in turn a zinc layer, a copper layer and a chromate rust resistant layer on the surface of the copper foil, the surface of the copper foil being made roughened by electrically depositing a granular copper layer on said surface by burned plating; and then applying a smooth copper plating on said surface at less than or equal to a given limiting current density.
Claim 2
Dependent Claim
89 words
A process for treating a surface of a copper foil for producing the copper foil for a printed circuit board, comprising the steps of forming in turn a zinc layer, a copper layer and a chromate rust resistant layer on the surface of the copper foil, the surface of the copper foil being made roughened by electrically depositing a granular copper layer on said surface by burned plating; and then applying a smooth copper plating on said surface at less than or equal to a given limiting current density.
Claim 3
Dependent Claim
31 words
The process for treating the surface of the copper foil according to claim 1, wherein a zinc layer is additionally formed between the copper layer and the chromate rust resistant layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-17 | 1995-09-16 | 1996-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-17 | 1999-09-16 | 2000-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-17 | 2003-09-16 | 2004-03-17 | $7700.00 | Window Closed / Lapsed |