Process for producing copper-clad laminate
Assignee: Meiko Electronics Co Ltd
•
Filing: 1990-06-22
•
Granted: 1992-03-17
•
Expires: 2010-06-22
Abstract
Abstract A process for producing a copper-clad laminate is disclosed which includes the steps of (a) contacting the surface of a conductive carrier with a catalyst liquid containing at least one noble metal selected from the group consisting of Pd, Pt, Ru, Au, and Ag; (b) subsequently forming a copper foil layer on the treated surface of the conductive carrier by copper electroplating; (c) laminating an insulating base on the copper foil layer by hot-press bonding; and (d) separating the conductive carrier from the resulting laminate. The copper foil layer in the resulting copper-clad laminate has reduced pinholes and exhibits isotropic mechanical characteristics.
Inventors
- 👤 Norio Kawachi
- 👤 Katsurou Aoshima
- 👤 Tatsuo Wada
- 👤 Toshiro Miki
- 👤 Takeharu Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 16:49
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/02; H05K3/022; H05K3/025; H05K2203/00; H05K2203/01; H05K2203/0147; H05K2203/0152; H05K2203/03; H05K2203/0307; H05K2203/07; H05K2203/0703; H05K2203/0716; H05K2203/0723; H05K2203/0726
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
88 words
A process for producing a copper-clad laminate comprising the steps of: (a) contacting the surface of a conductive carrier with a catalyst liquid comprising at least one noble metal selected from the group consisting of Pd, Pt, Ru, Rh, Au and Ag; (b) subsequently forming a copper foil layer on the surface of the conductive carrier by copper electroplating; (c) laminating an insulating base on the copper foil layer by hot-press bonding; and (d) separating the conductive carrier from the copper foil layer to provide a copper-clad laminae.
Claim 2
Dependent Claim
88 words
A process for producing a copper-clad laminate comprising the steps of: (a) contacting the surface of a conductive carrier with a catalyst liquid comprising at least one noble metal selected from the group consisting of Pd, Pt, Ru, Rh, Au and Ag; (b) subsequently forming a copper foil layer on the surface of the conductive carrier by copper electroplating; (c) laminating an insulating base on the copper foil layer by hot-press bonding; and (d) separating the conductive carrier from the copper foil layer to provide a copper-clad laminae.
Claim 3
Dependent Claim
31 words
The method as claimed in claim 1, wherein said catalyst liquid in step (a) comprises a colloidal catalyst liquid comprising a dispersion of metallic noble metal particles in a protective colloid.
Claim 4
Dependent Claim
20 words
The method as claimed in claim 1, wherein said catalyst liquid in step (a) comprises a colloidal Pd-Sn catalyst liquid.
Claim 5
Dependent Claim
28 words
The method as claimed in claim 2, wherein in step (a) said colloidal catalyst liquid uniformly deposits fine particles of said noble metal on said conductive carrier surface.
Claim 6
Dependent Claim
34 words
The method as claimed in claim 4, wherein after said step (a) and prior to said step (b) said conductive carrier surface contacted with said catalyst liquid is washed with hydrochloric acid or water.
Claim 7
Dependent Claim
24 words
The method as claimed in claim 1, wherein said catalyst liquid comprises said noble metal in a concentration of from 100 to 150 ppm.
Claim 8
Dependent Claim
22 words
The method as claimed in claim 1, wherein prior to said step (a) said conductive carrier surface is degreased and washed water.
Claim 9
Dependent Claim
28 words
The method as claimed in claim 6, wherein said conductive carrier surface is contacted with said catalyst liquid for a period of from about 30 to 60 seconds.
Claim 10
Dependent Claim
22 words
The method as claimed in claim 1, wherein said conductive carrier has a surface roughness of from about 0.1 to 1 μm.
Claim 11
Dependent Claim
31 words
The method as claimed in claim 1, wherein said copper foil layer is formed by a high-speed plating method providing a copper foil layer build-up of at least about 15 m/min.
Claim 12
Dependent Claim
55 words
The method as claimed in claim 1, wherein the surface of copper foil layer produced in step (b) that is not adhered to said conductive carrier is subjected to electroplating using an acidic copper electroplating solution containing a chelating agent to form a profile layer having a surface roughness of at most about 7 μm.
Claim 13
Dependent Claim
37 words
The method as claimed in claim 11, wherein said profile layer surface has a surface roughness of about 1 to 5 μm, and a variation in surface roughness of about ±0.5 μm of the average surface roughness.
Claim 14
Dependent Claim
34 words
The method as claimed in claim 11, wherein said acidic electroplating solution further contains a least one compound selected from the group consisting of a zinc compound, a tin compound and a cobalt compound.
Claim 15
Dependent Claim
79 words
The method as claimed in claim 13, wherein said acidic electroplating solution comprises about 110 to 130 g/l of copper sulfate pentahydrate; from about 55 to 65 g/l of sulfuric acid; from about 21 to 24 g/l of a nitrate ion; from about 200 to 1,000 ppm of at least one compound selected from the group consisting of a zinc compound, a tin compound and a cobalt compound; and from about 5 to 20 g/l of a chelating agent.
Claim 16
Dependent Claim
67 words
The method as claimed in claim 14, wherein said copper electroplating solution comprises from about 115 to 120 g/l of copper sulfate pentahydrate; form about 55 to 60 g/l of sulfuric acid; from about 21 to 24 g/l of a nitrate ion; from about 250 to 500 ppm of said zinc compound, tin compound or cobalt compound; and about 5 to 10 g/l of said chelating agent.
Claim 17
Dependent Claim
40 words
The method as claimed in claim 11, wherein said acidic electroplating solution is contacted with said surface of copper foil layer produced in step (b) in a turbulent flow at a flow rate of from about 0.3 to 0.7 m/sec.
Claim 18
Dependent Claim
37 words
The method as claimed in claim 16, wherein said acidic copper electroplating solution is contacted with said surface of copper foil layer produced in step (b) at a flow rate of from about 0.35 to 0.45 m/sec.
Claim 19
Dependent Claim
24 words
The method as claimed in claim 11, wherein said electroplating is performed at current density of from about 30 to 55 A/dm 2 .
Claim 20
Dependent Claim
21 words
The method as claimed in claim 11, wherein said electroplating is at a temperature of from about 20° to 22° C.
References Cited (Backward Citations)
US2984595A
Cited
US3152938A
Cited
US3099608A
Cited
US4715116A
Cited
EP0258452A1
Cited
US4790902A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-17 | 1995-09-16 | 1996-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-17 | 1999-09-16 | 2000-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-17 | 2003-09-16 | 2004-03-17 | $7700.00 | Window Closed / Lapsed |