Wear resistant ceramic with a high alpha-content silicon nitride phase

Claim 2

In a sintered ceramic product consisting essentially of (a) from about 40 to about 98 percent silicon nitride, (b) from about 2 to about 60 percent of silicides of at least one metal selected from the group consisting of iron, nickel and cobalt, and (c) up to about 20 percent of at least one oxide, nitride or silicate of an element selected from IUPAC group 2, 3, 4, 13 or the lanthanide series, all percentages being by weight based on the total weight of the product, the improvement comprising an alpha-to-beta ratio of silicon nitride in the sintered ceramic product that falls within area A of FIG. 1 and a content of high metal-content silicides in the sintered ceramic product that is at least 50% by weight of the silicides present.

Claim 3

The sintered product of claim 1 wherein up to 50% by weight of the silicon nitride is replaced by at least one refractory carbide, nitride other than silicon nitride, or boride.

Claim 4

In a process for preparing a sintered ceramic product comprising (1) intimately mixing a powder mixture consisting essentially of (a) from about 50 to about 98 percent silicon nitride, (b) from about 1 to about 50 percent of at least one metal selected from the group consisting of iron, nickel and cobalt, or an oxide or alloy thereof, and (c) from 0.02 to about 20 percent of at least one oxide, nitride or silicate of an element selected from IUPAC group 2, 3, 4, 13 or the lanthanide series, all percentages being by weight based on the total weight of the powder mixture, (2) reacting the components of the powder mixture by heating to a temperature of 1300°-1700° C. in a non-oxidizing atmosphere until component 1(b) is completely converted to its corresponding silicides, and (3) maintaining the powder mixture at a temperature of 1300°-1700° C. in the non-oxidizing atmosphere until the composition formed in (2) densifies, the improvement comprising reacting the components of the powder mixture until the alpha-to-beta ratio of silicon nitride in the sintered ceramic product falls within area A of FIG. 1 and at least 50% by weight of the silicides in the sintered ceramic product are high metal-content silicides.

Claim 5

In a process for preparing a sintered ceramic product comprising (1) intimately mixing a powder mixture consisting essentially of (a) from about 50 to about 98 percent silicon nitride, (b) from about 1 to about 50 percent of at least one metal selected from the group consisting of iron, nickel and cobalt, or an oxide or alloy thereof, and (c) from 0.02 to about 20 percent of at least one oxide, nitride or silicate of an element selected from IUPAC group 2, 3, 4, 13 or the lanthanide series, all percentages being by weight based on the total weight of the powder mixture, (2) reacting the components of the powder mixture by heating to a temperature of 1300°-1700° C. in a non-oxidizing atmosphere until component 1(b) is completely converted to its corresponding silicides, and (3) maintaining the powder mixture at a temperature of 1300°-1700° C. in the non-oxidizing atmosphere until the composition formed in (2) densifies, the improvement comprising reacting the components of the powder mixture until the alpha-to-beta ratio of silicon nitride in the sintered ceramic product falls within area A of FIG. 1 and at least 50% by weight of the silicides in the sintered ceramic product are high metal-content silicides.

Claim 6

The process of claim 3 wherein the heating of the powder mixture is carried out at a pressure of at least 500 psi.

Claim 7

The process of claim 4 wherein the pressure is 2000-6000 psi.

Claim 8

The process of claim 3 wherein the non-oxidizing atmosphere is a nitrogen atmosphere.

Claim 9

The process of claim 3 wherein up to 50% by weight of the silicon nitride is replaced by at least one refractory carbide, nitride other than silicon nitride, or boride.

Claim 10

The process of claim 3 wherein the powder mixture comprises 50-93% by weight of silicon nitride, 5-25% by weight of at least one metal selected from the group consisting of iron, nickel and cobalt, 1-10% by weight of at least one oxide of IUPAC group 3 elements or the lanthanide series, and 1-5% by weight of aluminum oxide.

Claim 11

The process of claim 8 wherein fully stabilized zirconium oxide, partially stabilized zirconium oxide or hafnium oxide is substituted for all or part of the oxide of IUPAC group 3 elements or the lanthanide series.

Claim 12

The process of claim 3 wherein the powder mixture comprises 50-93% by weight of silicon nitride, 5-25% by weight of at least one metal selected from the group consisting of iron, nickel and cobalt, 1-10% by weight of at least one oxide of IUPAC group 2 elements, and 1-5% by weight of aluminum oxide.

Claim 13

The process of claim 10 wherein fully stabilized zirconium oxide or hafnium oxide is substituted for all or part of the oxide of IUPAC group 2 elements.

Claim 14

A wear resistant cutting tool prepared from the sintered ceramic product of claim 1.

Claim 15

A wear resistant cutting tool prepared from the sintered ceramic product of claim 2.