Polyurethane flexible foam and method for its production
Assignee: AGC Inc
•
Filing: 1989-10-18
•
Granted: 1992-03-03
•
Expires: 2009-10-18
Abstract
Abstract PCT No. PCT/JP89/01067 Sec. 371 Date Aug. 15, 1990 Sec. 102(e) Date Aug. 15, 1990 PCT Filed Oct. 18, 1989 PCT Pub. No. WO90/04613 PCT Pub. Date May 3, 1990.The present invention relates to a polyurethane flexible foam having a resonant frequency of not higher than 3.5 Hz and a method for producing such a polyurethane flexible foam. The polyurethane flexible foam of the present invention is obtained by using at least one member selected from a specific polyoxyalkylene polyol and a polymer-dispersed polyol containing said polyoxyalkylene polyol as the matrix and a polyisocyanate compound as the main reactive materials, and it is a polyurethane flexible foam having a resonant frequency of not higher than 3.5 Hz. Such a polyurethane flexible foam is obtained by using a polyoxyalkylene polyol with both the hydroxyl value (X mgKOH/g) and the total unsaturation degree (Y meq/g) being particularly low, or a polymer-dispersed polyol containing such a polyoxyalkylene polyol as the matrix. Namely, it is obtained by using as the above polyoxyalkylene polyol, a polyoxyalkylene polyol having a hydroxyl value (X mg/KOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.07, and both being in the following relation: Y</=0.9/(X-10) As such a polyoxyalkylene polyol, a polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight and an oxyethylene group content of at least 5% by weight, is preferred. Further, it is preferred to use a small amount of a crosslinking agent together with the above polyoxyalkylene polyol. The polyurethane flexible foam of the present invention has a vibration characteristic suitable for seat cushions for automobiles. Accordingly, a comfortable ride in an automobile can be improved by using the polyurethane flexible foam of the present invention for a seat cushion of the automobile.
Inventors
- 👤 Hiromitsu Takeyasu
- 👤 Tsunehisa Sonobe
- 👤 Yoshiyuki Yamaguchi
- 👤 Takao Doi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:31
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/63; C08G18/632; C08G18/48; C08G18/4833; C08G18/4837; C08G18/4866; C08G18/67; C08G18/671; C08G18/672; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/005; C08G2110/0083
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
124 words
A method for producing a polyurethane flexible foam, which comprises reacting at least one high molecular weight polyol selected from the group consisting of the following polyoxyalkylene polyol and a polymer-dispersed polyol containing the following polyoxyalkylene polyol as the matrix, an optional crosslinking agent and a polyisocyanate compound in the presence of assisting agents selected from the group consisting of a catlyst, a foaming agent and a foam stabilizer or a mixture thereof: Polyoxyalkylene polyol: A polyoxyalkylene polyol with the hydroxy value (X mgKOH/g) and the total unsaturation degree (Y meq/g) being in the following relation, with Y being not more than 0.07, the hydroxyl value (X) being from 5 to 38 and the number of hydroxyl groups being from 2 to 8: Y≦0.9/(X-10)
Claim 2
Independent Claim
124 words
A method for producing a polyurethane flexible foam, which comprises reacting at least one high molecular weight polyol selected from the group consisting of the following polyoxyalkylene polyol and a polymer-dispersed polyol containing the following polyoxyalkylene polyol as the matrix, an optional crosslinking agent and a polyisocyanate compound in the presence of assisting agents selected from the group consisting of a catlyst, a foaming agent and a foam stabilizer or a mixture thereof: Polyoxyalkylene polyol: A polyoxyalkylene polyol with the hydroxy value (X mgKOH/g) and the total unsaturation degree (Y meq/g) being in the following relation, with Y being not more than 0.07, the hydroxyl value (X) being from 5 to 38 and the number of hydroxyl groups being from 2 to 8: Y≦0.9/(X-10)
Claim 3
Dependent Claim
31 words
The method according to claim 1, wherein the polyoxyalkylene polyol has a hydroxyl value (X) of from 5 to 28 and a total unsaturation degree (Y) of not more than 0.04.
Claim 4
Dependent Claim
30 words
The method according to claim 1, wherein the polyoxyalkylene polyol is a polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight and optionally containing oxyethylene groups.
Claim 5
Dependent Claim
24 words
The method according to claim 3, wherein the polyoxyalkylene polyol is a polyoxyalkylene polyol containing at least 5% by weight of terminal oxyethylene groups.
Claim 6
Dependent Claim
21 words
The method according to claim 1, wherein the polymer-dispersed polyol contains from 1 to 40% by weight of fine polymer particles.
Claim 7
Dependent Claim
18 words
The method according to claim 5, wherein the fine polymer particles are fine particles of a vinyl polymer.
Claim 8
Dependent Claim
31 words
The method according to claim 1, wherein the crosslinking agent is used in an amount of from 0.2 to 10 parts by weight per 100 parts by weight of the polyol.
Claim 9
Dependent Claim
33 words
The method according to claim 1, wherein the crosslinking agent is a polyol having a molecular weight of not higher than 600 per hydroxyl group and having from 2 to 8 hydroxyl groups.
Claim 10
Dependent Claim
14 words
The method according to claim 1, wherein the polyisocyanate compound is an aromatic polyisocyanate.
Claim 11
Dependent Claim
35 words
The method according to claim 9, wherein the aromatic polyisocyanate is at least one member selected from the group consisting of tolylene diisocyanate, diphenylmethane diisocyanate, crude diphenylmethane diisocyanate and at least one modified product thereof.
Claim 12
Dependent Claim
50 words
The method according to claim 10, wherein the aromatic polyisocyanate is a mixture comprising at least one member selected from the group consisting of tolylene isocyanate and modified products thereof and at least one member selected from the group consisting of diphenylmethane diisocyanate, crude diphenylmethane diisocyanate and modified products thereof.
Claim 13
Dependent Claim
21 words
The method according to claim 1, wherein the foaming agent is water, or water and a low boiling point halogenated hydrocarbon.
Claim 14
Independent Claim
168 words
A method for producing a polyurethane flexible foam, which comprises reacting a polymer-dispersed polyol wherein the matrix is the following polyoxyalkylene polyol and fine polymer particles are dispersed stably in the matrix, from 0.2 to 10 parts by weight, per 100 parts by weight of the polymer-dispersed polyol, of a crosslinking agent and an aromatic polyisocyanate in an amount of from 0.8 to 1.3 equivalent per equivalent of the total amount of the polymer-dispersed polyol, the crosslinking agent and water when a foaming agent contains water, in the presence of a catalyst, a foaming agent and a foam stabilizer: Polyoxyalkylene polyol: A polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight, a terminal oxyethylene group content of at least 5% by weight, a number of hydroxyl groups of from 2 to 8, a hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.07, with X and Y being in the following relation: Y≦0./9/(X-10).
Claim 15
Independent Claim
168 words
A method for producing a polyurethane flexible foam, which comprises reacting a polymer-dispersed polyol wherein the matrix is the following polyoxyalkylene polyol and fine polymer particles are dispersed stably in the matrix, from 0.2 to 10 parts by weight, per 100 parts by weight of the polymer-dispersed polyol, of a crosslinking agent and an aromatic polyisocyanate in an amount of from 0.8 to 1.3 equivalent per equivalent of the total amount of the polymer-dispersed polyol, the crosslinking agent and water when a foaming agent contains water, in the presence of a catalyst, a foaming agent and a foam stabilizer: Polyoxyalkylene polyol: A polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight, a terminal oxyethylene group content of at least 5% by weight, a number of hydroxyl groups of from 2 to 8, a hydroxyl value (X mgKOH/g) of from 5 to 38 and a total unsaturation degree (Y meq/g) of not more than 0.07, with X and Y being in the following relation: Y≦0./9/(X-10).
Claim 16
Dependent Claim
21 words
The method according to claim 13, wherein the polymer-dispersed polyol contains from 1 to 40% by weight of fine polymer particles.
Claim 17
Dependent Claim
18 words
The method according to claim 14, wherein the fine polymer particles are fine particles of a vinyl polymer.
Claim 18
Dependent Claim
29 words
The method according to claim 13, wherein the polyoxyalkylene polyol has a hydroxyl value of from 5 to 28 and a total unsaturation degree of not more than 0.04.
Claim 19
Dependent Claim
37 words
The method according to claim 13, wherein the crosslinking agent is a polyoxyalkylene polyol having a molecular weight of not higher than 300 per hydroxyl group and a number of hydroxyl groups of from 3 to 8.
Claim 20
Dependent Claim
58 words
A polyurethane flexible foam obtained by using at least one polyol selected from a polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight and a polymer-dispersed polyol containing said polyoxyalkylene polyol as the matrix and a polyisocyanate compound as the main reactive materials, and having a resonant frequency of not higher than 3.5 Hz.
Claim 21
Dependent Claim
58 words
A polyurethane flexible foam obtained by using at least one polyol selected from a polyoxyalkylene polyol having an oxypropylene group content of at least 70% by weight and a polymer-dispersed polyol containing said polyoxyalkylene polyol as the matrix and a polyisocyanate compound as the main reactive materials, and having a resonant frequency of not higher than 3.5 Hz.
Claim 22
Dependent Claim
19 words
The polyurethane flexible foam according to claim 18, wherein the impact resilience of the core is at least 70%.
Claim 23
Dependent Claim
12 words
A polyurethane flexible foam obtained by the method according to claim 1.
Claim 24
Dependent Claim
18 words
The polyurethane flexible foam according to claim 20, wherein the resonant frequency is not higher than 3.5 Hz.
Claim 25
Dependent Claim
12 words
A polyurethane flexible foam obtained by the method according to claim 13.
Claim 26
Dependent Claim
18 words
The polyurethane flexible foam according to claim 22, wherein the resonant frequency is not higher than 3.5 Hz.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-03 | 1995-09-02 | 1996-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-03 | 1999-09-02 | 2000-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-03 | 2003-09-02 | 2004-03-03 | $7700.00 | Window Closed / Lapsed |