Semiconductor-containing glass and method of producing the same
Assignee: Hoya Corp
•
Filing: 1991-03-04
•
Granted: 1992-03-03
•
Expires: 2011-03-04
Abstract
Abstract The semiconductor-containing glass disclosed herein is a semiconductor-containing glass which is produced by a sol-gel technique and which includes a semiconductor-containing glass characterized in the composition of a glass matrix and a semiconductor-containing glass characterized in the composition of a semiconductor. Either a semiconductor-containing glass has useful properties as a non-linear optical material. The method of producing semiconductor-containing glass disclosed herein is a method in which oxidization, volatilization or decomposition of a compound semiconductor or volatilization of a constituent element of the compound semiconductor by heat treatment for forming glass from a gel solid can be suppressed when a semiconductor-containing glass in which the compound semiconductor is dispersively precipitated is produced by a sol-gel technique. That is, the method disclosed herein is a method in which a semiconductor-containing glass containing a compound semiconductor dispersively precipitated therein at a high concentration can be produced. The method is characterized in the technique of dispersively precipitating a compound semiconductor.
Inventors
- 👤 Masayuki Nogami
- 👤 Shinichi Ogawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:04
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/006; C03C14/00; C03C14/006; C03C3/00; C03C3/04; C03C3/06; C03C3/076; C03C3/078; C03C3/083; C03C3/085; C03C3/089; C03C3/095; C09; C09K; C09K11/00; C09K11/02; C09K11/08; C09K11/56; C09K11/562; C09K11/565; C09K11/61; C09K11/615; C09K11/66; C09K11/661; C09K11/88; C09K11/881; C09K11/883; C03C2201/00; C03C2201/06; C03C2201/08; C03C2201/10; C03C2201/20; C03C2201/28; C03C2201/30; C03C2201/32; C03C2201/40; C03C2203/00; C03C2203/20; C03C2203/24; C03C2214/00; C03C2214/16; C03C2214/32
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
128 words
A semiconductor-containing glass, which comprises: a multicomponent glass as a glass matrix, said multicomponent glass being produced by a sol-gel method and containing SiO 2 as a main component and at least one member selected from the group consisting of ZrO 2 , TiO 2 , Al 2 O 3 , Na 2 O, K 2 O, Li 2 O, MgO, ZnO, CaO, PbO, BaO, B 2 O 3 , P 2 O 5 , SrO and La 2 O 3 as a subsidiary component; and at least one compound semiconductor selected from the group consisting of CdS, PbS, ZnS, CdSe, ZnSe, PbSe, CdTe, PbTe, ZnTe and CuCl, said compound semiconductor being dispersively crystallized in said glass matrix in an amount of not smaller than 0.1% by weight.
Claim 2
Dependent Claim
128 words
A semiconductor-containing glass, which comprises: a multicomponent glass as a glass matrix, said multicomponent glass being produced by a sol-gel method and containing SiO 2 as a main component and at least one member selected from the group consisting of ZrO 2 , TiO 2 , Al 2 O 3 , Na 2 O, K 2 O, Li 2 O, MgO, ZnO, CaO, PbO, BaO, B 2 O 3 , P 2 O 5 , SrO and La 2 O 3 as a subsidiary component; and at least one compound semiconductor selected from the group consisting of CdS, PbS, ZnS, CdSe, ZnSe, PbSe, CdTe, PbTe, ZnTe and CuCl, said compound semiconductor being dispersively crystallized in said glass matrix in an amount of not smaller than 0.1% by weight.
Claim 3
Dependent Claim
44 words
A semiconductor-containing glass according to claim 1, wherein the energy gap value of said a semiconductor-containing glass calculated from an absorption end of light absorption spectra is larger than that of a single crystal of the compound semiconductor dispersively crystallized in said semiconductor-containing glass.
Claim 4
Dependent Claim
23 words
A semiconductor-containing glass according to claim 1, wherein the dispersively crystallized compound semiconductor has a particle diameter of not larger than 1000 Å.
Claim 5
Dependent Claim
57 words
A semiconductor-containing glass, which comprises: a silica glass as a glass matrix produced by a sol-gel method; and at least one compound semiconductor selected from the group consisting of PbS, ZnSe, PbSe, PbTe, ZnTe, CuBr and CuI, said compound semiconductor being dispersively crystallized in said glass matrix in an amount of not smaller than 0.1% by weight.
Claim 6
Dependent Claim
57 words
A semiconductor-containing glass, which comprises: a silica glass as a glass matrix produced by a sol-gel method; and at least one compound semiconductor selected from the group consisting of PbS, ZnSe, PbSe, PbTe, ZnTe, CuBr and CuI, said compound semiconductor being dispersively crystallized in said glass matrix in an amount of not smaller than 0.1% by weight.
Claim 7
Dependent Claim
43 words
A semiconductor-containing glass according to claim 4, wherein the energy gap value of said semiconductor-containing glass calculated from an absorption end of light absorption spectra is larger than that of a single crystal of the compound semiconductor dispersively crystallized in said semiconductor-containing glass.
Claim 8
Dependent Claim
23 words
A semiconductor-containing glass according to claim 4, wherein the compound semiconductor dispersively crystallized has a particle diameter of not larger than 1000 Å.
Claim 9
Independent Claim
110 words
A method of producing a semiconductor-containing glass comprising: a first step of preparing a gel solid which contains at least one metal element as a raw material for a compound semiconductor and which will later form a glass by heat treatment; and a second step of exposing said gel solid to a gas after heating said gel solid to a temperature of from 400° to 1150° C. to form a glass or while heating said gel solid to a temperature of from 400° to 1150° C. to form a glass, said gas containing at least one non-metal element which reacts with said metal element to thereby produce a compound semiconductor.
Claim 10
Independent Claim
110 words
A method of producing a semiconductor-containing glass comprising: a first step of preparing a gel solid which contains at least one metal element as a raw material for a compound semiconductor and which will later form a glass by heat treatment; and a second step of exposing said gel solid to a gas after heating said gel solid to a temperature of from 400° to 1150° C. to form a glass or while heating said gel solid to a temperature of from 400° to 1150° C. to form a glass, said gas containing at least one non-metal element which reacts with said metal element to thereby produce a compound semiconductor.
Claim 11
Dependent Claim
83 words
A method of producing a semiconductor-containing glass according to claim 7, wherein said metal element as a raw material for a compound semiconductor is selected from the group consisting of Cd, Zn, Pb, Cu, Hg, Ag, Ni, Pd, Mn, Co, Ga, Bi, As, In and Al; and said gas containing at least one non-metal element is selected from the group consisting of H 2 S gas, HCl gas, H 2 Se gas, H 2 Te gas, AsH 3 gas and SbH 3 gas.
Claim 12
Dependent Claim
55 words
A method of producing a semiconductor-containing glass according to claim 7, wherein said first step includes the steps of: preparing a sol solution for a glass matrix, said sol solution containing a metal element as a raw material for a compound semiconductor; and gelating and drying said sol solution to thereby prepare said gel solid.
Claim 13
Dependent Claim
67 words
A method of producing a semiconductor-containing glass according to claim 7, wherein said first step includes the steps of: preparing a wet gel from a sol solution for a glass matrix; impregnating said wet gel with a solution containing at least one metal element as a raw material for a compound semiconductor; and drying said wet gel impregnated with said solution to thereby prepare said gel solid.
Claim 14
Dependent Claim
53 words
A method of producing a semiconductor-containing glass according to claim 7, wherein said first step includes the steps of: preparing a gel solid from a sol solution for a glass matrix; and impregnating said gel solid with a solution containing at least one metal element as a raw material for a compound semiconductor.
Claim 15
Dependent Claim
59 words
A method of producing a semiconductor-containing glass according to claim 7, wherein the microcrystal size of said compound semiconductor dispersively crystallized is controlled by at least one of the conditions for forming a glass from said gel solid and the condition for exposing said gel solid to said gas containing at least one non-metal element, in said second step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-03 | 1995-09-02 | 1996-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-03 | 1999-09-02 | 2000-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-03 | 2003-09-02 | 2004-03-03 | $7700.00 | Window Closed / Lapsed |