Resin composition
Assignee: Mitsubishi Chemical Corp
•
Filing: 1990-08-23
•
Granted: 1992-02-25
•
Expires: 2010-08-23
Abstract
Abstract There is disclosed a resin composition comprising: (a) 28 to 78% by weight of a polyamide resin, (b) 20 to 70% by weight of a polyphenylene ether resin, (c) 2 to 40% by weight of a block copolymer composed of an alkenyl aromatic polymer and a conjugated diene polymer wherein a content of an alkenyl aromatic polymer structure unit is 10 to 45% by weight and at least 50% of a conjugated diene polymer structure unit is hydrogenated and (d) at least one compound selected from the group consisting of α,β-unsaturated dicarboxylic acid, an acid anhydride and derivatives thereof with an amount of 0.01 to 10 parts by weight based on 100 parts by weight of the sum of Components (a), (b) and (c), which has a specific dispersion state. The resin composition has excellent thermal stability and also good balance between impact strength, rigidity and high temperature rigidity with high degree.
Inventors
- 👤 Yusuke Arashiro
- 👤 Shinichi Yamauchi
- 👤 Hironari Sano
- 👤 Takayuki Inoue
- 👤 Koji Nishida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:35
CPC Classifications
C; C08; C08L; C08L77/00; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
184 words
A resin composition comprising: (a) 28 to 78% by weight of a polyamide resin, (b) 20 to 70% by weight of a polyphenylene ether resin, (c) 2 to 40% by weight of a block copolymer composed of an alkenyl aromatic polymer and a conjugated diene polymer wherein a content of an alkenyl aromatic polymer structure unit is 10 to 45% by weight and at least 50% of a conjugated diene polymer structure unit is hydrogenated and (d) at least one compound selected from the group consisting of α, β-unsaturated dicarboxylic acid, an acid anhydride and derivatives thereof with an amount of 0.01 to 10 parts by weight based on 100 parts by weight of the sum of Components (a), (b) and (c), Component (b) being present in Component (a) as a primary dispersed phase, Component (c) forming a secondary dispersed phase in Component (b), an average particle size of Component (c) being in the range of 0.01 to 3 microns and a melt viscosity ratio (η c /η b ) of Component (c) and Component (b) being in the range of 0.09 to 5.
Claim 2
Dependent Claim
184 words
A resin composition comprising: (a) 28 to 78% by weight of a polyamide resin, (b) 20 to 70% by weight of a polyphenylene ether resin, (c) 2 to 40% by weight of a block copolymer composed of an alkenyl aromatic polymer and a conjugated diene polymer wherein a content of an alkenyl aromatic polymer structure unit is 10 to 45% by weight and at least 50% of a conjugated diene polymer structure unit is hydrogenated and (d) at least one compound selected from the group consisting of α, β-unsaturated dicarboxylic acid, an acid anhydride and derivatives thereof with an amount of 0.01 to 10 parts by weight based on 100 parts by weight of the sum of Components (a), (b) and (c), Component (b) being present in Component (a) as a primary dispersed phase, Component (c) forming a secondary dispersed phase in Component (b), an average particle size of Component (c) being in the range of 0.01 to 3 microns and a melt viscosity ratio (η c /η b ) of Component (c) and Component (b) being in the range of 0.09 to 5.
Claim 3
Dependent Claim
56 words
The resin composition according to claim 1, wherein said composition comprises 35 to 75% by weight of Component (a), 20 to 60% by weight of Component (b), 5 to 35% by weight Component (c), and 0.05 to 5 parts by weight of Component (d) based on 100 parts by weight of Components (a), (b) and (c).
Claim 4
Dependent Claim
56 words
The resin composition according to claim 1, wherein said composition comprises 40 to 70% by weight of Component (a), 25 to 50% by weight of Component (b), 7 to 30% by weight Component (c), and 0.2 to 2 parts by weight of Component (d) based on 100 parts by weight of Components (a), (b) and (c).
Claim 5
Dependent Claim
31 words
The resin composition according to claim 1, wherein a melt viscosity ratio (η c /η b ) of Component (c) to Component (b) is in the range of 0.3 to 3.0.
Claim 6
Dependent Claim
20 words
The resin composition according to claim 1, wherein Component (d) is at least one of maleic anhydride and maleic acid.
Claim 7
Dependent Claim
39 words
The resin composition according to claim 1, wherein said composition is obtained by melting and kneading Components (b), (c) and (d), or Components (b), (c), (d) and a part of Component (a) and then kneading the remaining Component (a).
Claim 8
Dependent Claim
43 words
The resin composition according to claim 1, wherein said composition is obtained by melting and kneading Components (b), (c), (d), and 5 to 20% by weight of Component (a) based on total amount to be formulated and then kneading the remaining Component (a).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-24 | 1995-08-26 | 1996-02-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-24 | 1999-08-26 | 2000-02-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-24 | 2003-08-26 | 2004-02-25 | $7700.00 | Window Closed / Lapsed |