Abstract
Abstract A chlorinated ethylene-propylene copolymer having a chlorine content of 20 to 45% by weight and a Mooney viscosity (ML 1+4 , 100° C.) of 10 to 150 is produced by chlorinating in two or three stages, by contact with chlorine gas in an aqueous suspension, an ethylene-propylene copolymer having a propylene content of 15 to 40% by weight, a melt flow index of 0.01 to 5.0 g/10 minutes, a melting peak as measured by differential scan calorimeter (DSC) of 80° C. or more, a crystallinity as measured by X-rays of 3% or more, an index M W /M N of the distribution of molecular weight, determined by gel permeation chromatography (GPC), of greater than 4, and a Mooney visocisty (ML 1+4 , 100° C.) of 10 to 180. A vulcanizable composition having superior physical properties may be obtained by formulating with (A) the chlorinated ethylene-propylene copolymer, (B) a thiourea compound, (C) sulfur and/or a sulfur donor, (D) a metal compound, and furthur, if necessary, (E) a dicarbamate or (F) a mercaptotriadizine compound. Furthur, a cross-linkable composition having superior physical properties may be obtained by formulating (A) the chlorinated ethylene-propylene copolymer with (G) an organic peroxide.
Inventors
- 👤 Naotoshi Watanabe
- 👤 Tsuyoshi Masukawa
- 👤 Kenji Ozaki
- 👤 Noboru Moriwaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 17:55
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/14; C08F; C08F8/00; C08F8/18; C08F8/20; C08F8/22; C08K3/00; C08K3/02; C08K3/06; C08K5/36; C08K5/39; C08K5/405
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
266 words
A method for producing a chlorinated ethylene-propylene copolymer comprising contacting a starting ethylene-propylene copolymer, wherein the propylene content is 20 to 38% by weight, the melt flow index is 0.01 to 5.0 g/10 minutes, the melting peak as measured by differential scan calorimetry (DSC) is 80° C. or more, the crystallinity as measured by X-rays is 3 to 45%, the index M W /M N of the distribution of molecular weight, determined by gel permeation chromatography (GPC), is greater than 4, and the Mooney viscosity (ML 1+4 , 100° C.) is 10 to 180, with chlorine gas in an aqueous suspension, to produce a chlorinated ethylene-propylene copolymer having a chlorine content of 20 to 45% by weight and a Mooney viscosity (ML 1+4 , 100° C.) of 10 to 150, wherein at a first stage, 20 to 60% of the total chlorination amount is chlorinated at a temperature at least 25° C. below the melting point of the ethylene-propylene copolymer but higher than 50° C., at a second stage, at least 30% of the remaining chlorination amount is chlorinated at a temperature 10° C. or more higher than the chlorination temperature at the first stage but at a temperature 5° to 15° C. lower than the melting point of said ethylene-propylene copolymer, with 60 to 90% of the total chlorination amount chlorinated up to that Stage, and at a third stage, at least 10% of the total chlorination amount is chlorinated at a temperature less than the melting point of the ethylene-propylene copolymer but not less than a temperature of the melting point minus 2° C.
Claim 2
Independent Claim
266 words
A method for producing a chlorinated ethylene-propylene copolymer comprising contacting a starting ethylene-propylene copolymer, wherein the propylene content is 20 to 38% by weight, the melt flow index is 0.01 to 5.0 g/10 minutes, the melting peak as measured by differential scan calorimetry (DSC) is 80° C. or more, the crystallinity as measured by X-rays is 3 to 45%, the index M W /M N of the distribution of molecular weight, determined by gel permeation chromatography (GPC), is greater than 4, and the Mooney viscosity (ML 1+4 , 100° C.) is 10 to 180, with chlorine gas in an aqueous suspension, to produce a chlorinated ethylene-propylene copolymer having a chlorine content of 20 to 45% by weight and a Mooney viscosity (ML 1+4 , 100° C.) of 10 to 150, wherein at a first stage, 20 to 60% of the total chlorination amount is chlorinated at a temperature at least 25° C. below the melting point of the ethylene-propylene copolymer but higher than 50° C., at a second stage, at least 30% of the remaining chlorination amount is chlorinated at a temperature 10° C. or more higher than the chlorination temperature at the first stage but at a temperature 5° to 15° C. lower than the melting point of said ethylene-propylene copolymer, with 60 to 90% of the total chlorination amount chlorinated up to that Stage, and at a third stage, at least 10% of the total chlorination amount is chlorinated at a temperature less than the melting point of the ethylene-propylene copolymer but not less than a temperature of the melting point minus 2° C.
Claim 3
Independent Claim
248 words
A method for producing a chlorinated ethylene-propylene copolymer comprising contacting a starting ethylene-propylene copolymer, wherein the propylene content is 20 to 38% by weight, the melt flow index is 0.01 is 5.0 g/10 minutes, the melting peak as measured by differential scan calorimetry (DSC) is 80° C. or more, the crystallinity as measured by X-rays is 3% to 6.2%, the index M W /M N of the distribution of molecular weight, determined by gel permeation chromatography (GPC), is greater than 4 but not more than 8, and the Mooney viscosity (ML 1+4 , 100° C.) is 10 to 150, with chlorine gas in an aqueous suspension, to produce a chlorinated ethylene-propylene copolymer having a chlorine content of 20 to 45% by weight, a Mooney viscosity (ML 1+4 , 100° C.) of 10 to 100 and a melt flow index of 1 to 100 g.10 minutes, wherein at a first stage, 20 to 60% of the total chlorination amount is chlorinated at a temperature at least 25° C. below the melting point of the ethylene-propylene copolymer but higher than 50° C., at a second stage, the temperature is raised to 1° to 7° C. higher than the melting point of the ethylene-propylene copolymer, at which temperature the process comprises annealing the ethylene propylene copolymer for 10 to 60 minutes without introduction of chlorine gas, and at a third stage, at a temperature 2° to 25° C. lower than the melting point of the ethylene-propylene copolymer, performing the remaining chlorination.
Claim 4
Independent Claim
248 words
A method for producing a chlorinated ethylene-propylene copolymer comprising contacting a starting ethylene-propylene copolymer, wherein the propylene content is 20 to 38% by weight, the melt flow index is 0.01 is 5.0 g/10 minutes, the melting peak as measured by differential scan calorimetry (DSC) is 80° C. or more, the crystallinity as measured by X-rays is 3% to 6.2%, the index M W /M N of the distribution of molecular weight, determined by gel permeation chromatography (GPC), is greater than 4 but not more than 8, and the Mooney viscosity (ML 1+4 , 100° C.) is 10 to 150, with chlorine gas in an aqueous suspension, to produce a chlorinated ethylene-propylene copolymer having a chlorine content of 20 to 45% by weight, a Mooney viscosity (ML 1+4 , 100° C.) of 10 to 100 and a melt flow index of 1 to 100 g.10 minutes, wherein at a first stage, 20 to 60% of the total chlorination amount is chlorinated at a temperature at least 25° C. below the melting point of the ethylene-propylene copolymer but higher than 50° C., at a second stage, the temperature is raised to 1° to 7° C. higher than the melting point of the ethylene-propylene copolymer, at which temperature the process comprises annealing the ethylene propylene copolymer for 10 to 60 minutes without introduction of chlorine gas, and at a third stage, at a temperature 2° to 25° C. lower than the melting point of the ethylene-propylene copolymer, performing the remaining chlorination.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 1, wherein the melt flow index of the starting copolymer is 0.05 to 5.0 g/10 minutes.
Claim 6
Dependent Claim
20 words
A method as claimed in claim 1, wherein the melting peak of the starting copolymer is 85° to 125° C.
Claim 7
Dependent Claim
27 words
A method as claimed in claim 1, wherein the index M W /M N of the starting copolymer is greater than 4 but not greater than 8.
Claim 8
Dependent Claim
24 words
A method as claimed in claim 1, wherein the Mooney viscosity (ML 1+4 , 100° C.) of the starting copolymer is 10 to 150.
Claim 9
Dependent Claim
25 words
A method as claimed in claim 1, wherein the chlorine content of the chlorinated copolymer at the first stage is 8 to 20% by weight.
References Cited (Backward Citations)
US3192188A
Cited
US3759888A
Cited
US3935181A
Cited
JPS58145703A
Cited
US4547554A
Cited
EP0184212A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-10 | 1995-08-12 | 1996-02-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-10 | 1999-08-12 | 2000-02-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-10 | 2003-08-12 | 2004-02-11 | $7700.00 | Window Closed / Lapsed |