US5082906A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Catalyst for the synthesis of crystalline 3,4-polyisoprene
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1990-10-24
•
Granted: 1992-01-21
•
Expires: 2010-10-24
Abstract
Abstract Crystallizable 3,4-polyisoprene can be synthesized in organic solvents to quantitative yields after short polymerization times by utilizing the catalyst systems of this invention. The 3,4-polyisoprene made utilizing this catalyst system is strain crystallizable and can be employed in tire treads which provide improved traction and improved cut growth resistance. This invention specifically discloses a process for the synthesis of 3,4-polyisoprene which comprises polymerizing isoprene monomer in an organic solvent at a temperature which is within the range of about -10° C. to about 100° C. in the presence of a catalyst system which is composed of (a) an organoiron compound, (b) an organoaluminum compound, (c) a chelating aromatic amine, and (d) a protonic compound; wherein the molar ratio of the chelating amine to the organoiron compound is within the range of about 0.1:1 to about 1:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 5:1 to about 200:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.001:1 to about 0.2:1.
Inventors
- 👤 Wen-Liang Hsu
- 👤 Adel F. Halasa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:26
CPC Classifications
C; C08; C08F; C08F4/00; C08F4/42; C08F4/44; C08F4/60; C08F4/602; C08F136/00; C08F136/02; C08F136/04; C08F136/08; C08F2410/00; C08F2410/01; Y; Y10; Y10S; Y10S152/00; Y10S152/905
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
139 words
A process for the synthesis of 3,4-polyisoprene which comprises polymerizing isoprene monomer in an organic solvent at a temperature which is within the range of about -10° C. to about 100° C. in the presence of a catalyst system which is comprised of (a) an organoiron compound, (b) an organoaluminum compound, (c) a chelating aromatic amine, and (d) a protonic compound selected from the group consisting of water, alcohols and carboxylic acids; wherein the molar ratio of the chelating amine to the organoiron compound is within the range of about 0.1:1 to about 1:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 5:1 to about 200:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.001:1 to about 0.2:1.
Claim 2
Dependent Claim
139 words
A process for the synthesis of 3,4-polyisoprene which comprises polymerizing isoprene monomer in an organic solvent at a temperature which is within the range of about -10° C. to about 100° C. in the presence of a catalyst system which is comprised of (a) an organoiron compound, (b) an organoaluminum compound, (c) a chelating aromatic amine, and (d) a protonic compound selected from the group consisting of water, alcohols and carboxylic acids; wherein the molar ratio of the chelating amine to the organoiron compound is within the range of about 0.1:1 to about 1:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 5:1 to about 200:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.001:1 to about 0.2:1.
Claim 3
Dependent Claim
16 words
A process as specified in claim 1 wherein the organic solvent is an aliphatic organic solvent.
Claim 4
Dependent Claim
22 words
A process as specified in claim 2 wherein the aliphatic organic solvent is selected from the group consisting of hexane and cyclohexane.
Claim 5
Dependent Claim
29 words
A process as specified in claim 1 wherein the organoiron compound is utilized at a level which is within the range of about 0.001 phm to about 1 phm.
Claim 6
Dependent Claim
29 words
A process as specified in claim 1 wherein the organoiron compound is employed at a level which is within the range of about 0.005 phm to about 0.1 phm.
Claim 7
Dependent Claim
29 words
A process as specified in claim 1 wherein the organoiron compound is employed at a level which is within the range of about 0.01 phm to about 0.03 phm.
Claim 8
Dependent Claim
29 words
A process as specified in claim 4 wherein said polymerization is carried out at a temperature which is within the range of about 0° C. to about 50° C.
Claim 9
Dependent Claim
29 words
A process as specified in claim 5 wherein said polymerization is carried out at a temperature which is within the range of about 10° C. to about 30° C.
Claim 10
Dependent Claim
150 words
A process for the synthesis of 3,4-polyisoprene which comprises: (1) adding a catalyst system which is comprised of (a) an organoiron compound, (b) an organoaluminum compound, (c) a chelating aromatic amine, and (d) a protonic compound selected from the group consisting of water, alcohols and carboxylic acids; wherein the molar ratio of the chelating amine to the organoiron compound is within the range of about 0.1:1 to about 1:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 5:1 to about 200:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.001:1 to about 0.2:1 to a polymerization medium containing isoprene monomer and an aliphatic organic solvent, and (2) allowing the isoprene monomer to polymerize at a temperature which is within the range of about -10° C. to about 100° C.
Claim 11
Dependent Claim
150 words
A process for the synthesis of 3,4-polyisoprene which comprises: (1) adding a catalyst system which is comprised of (a) an organoiron compound, (b) an organoaluminum compound, (c) a chelating aromatic amine, and (d) a protonic compound selected from the group consisting of water, alcohols and carboxylic acids; wherein the molar ratio of the chelating amine to the organoiron compound is within the range of about 0.1:1 to about 1:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 5:1 to about 200:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.001:1 to about 0.2:1 to a polymerization medium containing isoprene monomer and an aliphatic organic solvent, and (2) allowing the isoprene monomer to polymerize at a temperature which is within the range of about -10° C. to about 100° C.
Claim 12
Dependent Claim
40 words
A process as specified in claim 9 wherein the organoiron compound component and the chelating aromatic amine component of the catalyst system are added first followed by addition of the organoaluminum compound which has been preformed with the protonic compound.
Claim 13
Dependent Claim
16 words
A process as specified in claim 1 wherein the organoaluminum compound is a trialkyl aluminum compound.
Claim 14
Dependent Claim
41 words
A process as specified in claim 11 wherein the organoiron compound is selected from the group consisting of ferric benzoate, ferric acetate, ferric naphthenate, ferric octanoate, ferric neodecanoate, ferric palmitate, ferric stearate, ferric acetylacetonate, ferric salicaldehyde, ferric diglyoxime, and ferric tetracarbonyl.
Claim 15
Dependent Claim
23 words
A process as specified in claim 12 wherein the chelating aromatic amine is selected from the group consisting of 1,10-phenanthroline, 2,2-dipyridyl, and 1,4-phenylenediamine.
Claim 16
Dependent Claim
27 words
A process as specified in claim 13 wherein the protonic compound is selected from the group consisting of water, methanol, ethanol, isopropyl alcohol and normal propyl alcohol.
Claim 17
Dependent Claim
75 words
A process as specified in claim 14 wherein the molar ratio of the chelating aromatic amine to the organoiron compound is within the range of about 0.2:1 to about 0.5:1, wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 20:1 to about 100:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.005:1 to about 0.1:1.
Claim 18
Dependent Claim
28 words
A process as specified in claim 15 wherein the trialkyl aluminum compound is selected from the group consisting of triethyl aluminum, tri-n-propyl aluminum, triisobutyl aluminum and trihexyl aluminum.
Claim 19
Dependent Claim
52 words
A process as specified in claim 16 wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 40:1 to about 60:1; and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.01:1 to about 0.07:1.
Claim 20
Dependent Claim
74 words
A process as specified in claim 7 wherein the molar ratio of the chelating diamine to the organoiron compound is within the range of about 0.2:1 to about 0.5:1; wherein the molar ratio of the organoaluminum compound to the organoiron compound is within the range of about 40:1 to about 60:1, and wherein the molar ratio of the protonic compound to the organoaluminum compound is within the range of about 0.01:1 to about 0.07:1.
Claim 21
Dependent Claim
36 words
A process as specified in claim 18 wherein the organoaluminum compound is triisobutyl aluminum, wherein the organoiron compound is ferric acetyl acetonate, wherein the chelating aromatic amine is 1,10-phenanthroline, and wherein the protonic compound is water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-20 | 1995-07-22 | 1996-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-20 | 1999-07-22 | 2000-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-20 | 2003-07-22 | 2004-01-21 | $7700.00 | Window Closed / Lapsed |