High-strength alumina sintered body and process for preparation thereof
Assignee: Kyocera Corp
•
Filing: 1988-12-20
•
Granted: 1992-01-21
•
Expires: 2008-12-20
Abstract
Abstract Disclosed is a high-strength alumina sintered body which consists of 1 to 30% by weight, based on Al 2 O 3 and ZrO 2 , of ZrO 2 and 99 to 70% by weight, based on Al 2 O 3 and ZrO 2 , of Al 2 O 3 , and unavoidable impurities, said sintered body having a peak based on ZrO 2 at a position of a wave body having a peak based on ZrO 2 at a position of a wave number of 600±10 cm -1 in a measurement chart of the laser Raman spectrum analysis. This sintered body has a high flexural strength and a high breaking toughness in combination.
Inventors
- 👤 Katsura Hayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:51
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/119
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
81 words
A high-strength alumina sintered body consisting of: 1 to 30% by weight, based on Al 2 O 3 and ZrO 2 , of ZrO 2 ; 99 to 70% by weight, based on Al 2 O 3 and ZrO 2 , of Al 2 O 3 ; and unavoidable impurities; said sintered body having a peak based on ZrO 2 at a position of a wave number of 600±10 cm -1 in a measurement chart of the laser Raman spectrum analysis.
Claim 2
Dependent Claim
81 words
A high-strength alumina sintered body consisting of: 1 to 30% by weight, based on Al 2 O 3 and ZrO 2 , of ZrO 2 ; 99 to 70% by weight, based on Al 2 O 3 and ZrO 2 , of Al 2 O 3 ; and unavoidable impurities; said sintered body having a peak based on ZrO 2 at a position of a wave number of 600±10 cm -1 in a measurement chart of the laser Raman spectrum analysis.
Claim 3
Dependent Claim
77 words
A sintered body as set forth in claim 1, wherein the peak heigh ratio defined by the formula of (Hc/Ha)×100, in which Hc stands for the height of the peak based on ZrO 2 at a position of a wave number of 600+10 cm -1 and Ha stands for the height of the peak based on Al 2 O 3 at a wave number of 415 cm -1 or in the vicinity thereof, is at least 10.0.
Claim 4
Dependent Claim
18 words
A sintered body as set forth in claim 2, wherein the peak height ratio is at least 20.0.
Claim 5
Dependent Claim
84 words
A sintered body as set forth in claim 1, which satisfies the requirements of H63/H28>0.1 and H60/H43>0.07, in which H60 stands for the peak height at 2θ=59.5° to 61° in the X-ray diffractometry using Cu-K rays, H63 stands the peak height at 2θ=62.0° to 63.5°, H43 stands for the height of the main peak of α-Al 2 O 3 at 2θ=43° or in the vicinity thereof, and H28 stands for the peak height of monoclinic ZrO 2 at 2θ=28° or in the vicinity thereof.
Claim 6
Dependent Claim
37 words
A sintered body as set forth in claim 4, wherein the value of H63/H28 is in the range of from 1.00 to 2.30 and the value of H60/H43 is in the range of from 0.20 to 0.40.
Claim 7
Dependent Claim
29 words
A sintered body as set forth in claim 1, which has a breaking toughness of at least 4.2 MN/m 3/2 and a flexural strength of 90 kg/mm 2 .
Claim 8
Dependent Claim
64 words
A sintered body as set forth in claim 1, wherein the sintered body has a polycrystalline structure in which zirconia is present in the form of particles having an average size smaller than 0.5 μm and alumina is present in the form of particles having an average particle size smaller than 1.3 μm, and an intergranular mutual stress is present in the polycrystalline structure.
Claim 9
Dependent Claim
42 words
A sintered body as set forth in claim 7, wherein the intensity of the intergranular mutual stress is such that when the sintered body is heat-treated at 1200° to 1600° C., deformation is caused in at least some of the alumina particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-20 | 1995-07-22 | 1996-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-20 | 1999-07-22 | 2000-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-20 | 2003-07-22 | 2004-01-21 | $7700.00 | Window Closed / Lapsed |