Polystyrene foam sheet manufacture
Assignee: Fuji Seal International Inc
•
Filing: 1990-06-14
•
Granted: 1992-01-21
•
Expires: 2010-06-14
Abstract
Abstract The method of making polystyrene foam for foam products which includes utilizing atmospheric gases as the blowing agents or preferably mixing one or more of these gases and a blending agent which is non-volatile at the extrusion temperatures, introducing the mixture to a molten thermoplastic polystyrene resin containing nucleating agents such as sodium bicarbonate and citric acid and extruding the thermoplastic in the form of a foam. The resultant foam has substantially no residual blowing agent, is dimensionally stable at ambient temperatures and when used with a non-volatile blending agent can be made with small amounts of blowing agent permitting cooling of the melt without high loading on the extruder. The foam may be coextruded with one or more layers of thermoplastic films so that the resultant product is adpated for use for plates, cups, food containers or packaging and for labells for containers such as glass and plastic containers and for labels that are shrunk in place on a container.
Inventors
- 👤 James A. Karabedian
- 👤 Maurice W. Blackwelder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:07
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/3415; B29C44/3419; B29C44/3402; B29C44/3442; B29C44/36; B29C44/46; B29C44/50; B29C44/507; B29C44/56; B29C44/5609; B29C48/00; B29C48/03; B29C48/09; B29C48/10; B29C48/25; B29C48/78; B29C48/80; B29C48/83; B29C48/832; C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/122; B29L; B29L2031/00; B29L2031/712; B29L2031/7132; B29L2031/744; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
167 words
The method of making foam sheet material which comprises introducing atmospheric gas as the blowing agent into a molten thermoplastic resin, extruding the thermoplastic through an extruder in the form of a frustoconical tubular web at an angle of at least 45° to the axis of the extruder, passing said frustoconical web over an internal cooling mandrel to cool the interior of the web, simultaneously continuously applying cooling air axially to the outside of said frustoconical web at an acute tangentially to the web whereby the cooling air moves in a direction parallel to the frustoconical web from adjacent the extruder to adjacent the internal cooling mandrel such that the external surface of the frusto conical web is cooled by the cooling air and by the additional ambient air drawn by the cooling air against the external surface of the frustoconical web and such that the resultant foam has substantially no residual blowing agent and is substantially dimensionally stable at ambient temperatures and has substantially no corrugations.
Claim 2
Independent Claim
167 words
The method of making foam sheet material which comprises introducing atmospheric gas as the blowing agent into a molten thermoplastic resin, extruding the thermoplastic through an extruder in the form of a frustoconical tubular web at an angle of at least 45° to the axis of the extruder, passing said frustoconical web over an internal cooling mandrel to cool the interior of the web, simultaneously continuously applying cooling air axially to the outside of said frustoconical web at an acute tangentially to the web whereby the cooling air moves in a direction parallel to the frustoconical web from adjacent the extruder to adjacent the internal cooling mandrel such that the external surface of the frusto conical web is cooled by the cooling air and by the additional ambient air drawn by the cooling air against the external surface of the frustoconical web and such that the resultant foam has substantially no residual blowing agent and is substantially dimensionally stable at ambient temperatures and has substantially no corrugations.
Claim 3
Dependent Claim
40 words
The method set forth in claim 1 including the step of positioning a cooling ring adjacent the internal cooling mandrel and the step of passing said tubular web into contact over said cooling ring before it passes to the mandrel.
Claim 4
Dependent Claim
29 words
The method set forth in claim 2 including the step of creating a differential pressure at said cooling ring causing the extruded material to maintain contact with said ring.
Claim 5
Dependent Claim
26 words
The method set forth in claim 3 wherein said step of creating a differential pressure comprises creating a vacuum at the surface of the cooling ring.
Claim 6
Dependent Claim
41 words
The method set forth in claim 4 wherein said step of creating a vacuum comprises providing a passage from the surface of the mandrel to the atmosphere such that the movement of the extruded material over the passage creates a vacuum.
Claim 7
Dependent Claim
73 words
The method set forth in claim 1 including the step of passing a web of the material over a drive roller and between a winding roller and driver roller, thereafter over a winding roller to be wound on said winding roller including the step of providing a compressive force on said winding roller toward said driver roller such as to subject the width of said web with sufficient force to minimize gauge bands.
Claim 8
Dependent Claim
28 words
The method set forth in claim 1 including the step of introducing into the molten thermoplastic resin a blending agent which is substantially non-volatile at the extrusion temperatures.
Claim 9
Dependent Claim
17 words
The method set forth in claim 7 wherein said blending agent comprises a high molecular weight material.
Claim 10
Dependent Claim
16 words
The method set forth in claim 8 wherein said non-volatile material is of the ester type.
Claim 11
Dependent Claim
24 words
The method set forth in claim 8 wherein said ester is selected from the group consisting of diisodecyl adipate, ditridecyl adipate and trioctyl trimellitate.
Claim 12
Dependent Claim
21 words
The method set forth in claim 10 wherein said non-volatile high molecular weight material has a molecular weight at least 350.
Claim 13
Dependent Claim
21 words
The method set forth in claim 7 wherein said non-volatile material comprises 3% or less by weight of the molten resin.
Claim 14
Dependent Claim
18 words
The method set forth in claim 1 including the step of coextruding a plastic film with said foam.
Claim 15
Dependent Claim
23 words
The method set forth in claim 1 wherein the amount of atmospheric gas is less than 3% by weight of the molten resin.
Claim 16
Dependent Claim
19 words
The method set forth in claim 1 wherein said angle of the tubular web ranges between 45° and 90°.
Claim 17
Independent Claim
15 words
The method set forth in any one of claims 1-15 wherein said resin comprises polystyrene.
Claim 18
Independent Claim
15 words
The method set forth in any one of claims 1-7 wherein said resin comprises polyolefin.
References Cited (Backward Citations)
AU529339A
Cited
US3796779A
Cited
US3985931A
Cited
US4049768A
Cited
US4424287A
Cited
US4436629A
Cited
US4436679A
Cited
US4470938A
Cited
US4486366A
Cited
US4663107A
Cited
US4657715A
Cited
US4757983A
Cited
US4747983A
Cited
EP0411923A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-20 | 1995-07-22 | 1996-01-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-20 | 1999-07-22 | 2000-01-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-20 | 2003-07-22 | 2004-01-21 | $7700.00 | Window Closed / Lapsed |