Method of making a magnetoresistive read transducer having hard magnetic bias
Assignee: International Business Machines Corp
•
Filing: 1990-12-18
•
Granted: 1992-01-07
•
Expires: 2010-12-18
Abstract
Abstract A magnetoresistive (MR) read transducer having passive end regions separated by a central active region in which an MR layer is formed which extends over substantially only the central active region and in which a hard magnetic layer is formed in each end region. The hard magnetic layers form an abutting junction having electrical and magnetic continuity with the MR layer to produce a longitudinal bias in the MR sensor. The transducer is produced by a method in which the same stencil defines the extent of both the MR layer and the hard magnetic layers so that the abutting junctions are formed easily and reliably.
Inventors
- 👤 Mohamad T. Krounbi
- 👤 Otto Voegeli
- 👤 Po-Kang Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:37
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/127; G11B5/33; G11B5/39; G11B5/3903; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/4902; Y10T29/49021; Y10T29/49032; Y10T29/49036; Y10T29/49043; Y10T29/49044; Y10T29/49046; Y10T29/49067
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
137 words
A method for making a magnetoresistive read transducer having passive end regions separated by a central active region comprising the steps of: depositing a thin magnetoresistive layer of ferromagnetic material over at least the central active ion of said transducer; producing a stencil covering the central active region of said transducer; etching away the part of said magnetoresistive material not covered by said stencil to form the central active region of said transducer; depositing a film of hard magnetic material over regions of said transducer not covered by said stencil to produce the passive end regions of said transducer, said hard magnetic material in said end regions forming an abutting junction with one end of said layer of magnetoresistive material so that a longitudinal bias is produced in each of said passive end regions of said transducer.
Claim 2
Independent Claim
137 words
A method for making a magnetoresistive read transducer having passive end regions separated by a central active region comprising the steps of: depositing a thin magnetoresistive layer of ferromagnetic material over at least the central active ion of said transducer; producing a stencil covering the central active region of said transducer; etching away the part of said magnetoresistive material not covered by said stencil to form the central active region of said transducer; depositing a film of hard magnetic material over regions of said transducer not covered by said stencil to produce the passive end regions of said transducer, said hard magnetic material in said end regions forming an abutting junction with one end of said layer of magnetoresistive material so that a longitudinal bias is produced in each of said passive end regions of said transducer.
Claim 3
Dependent Claim
24 words
The method for making a magnetoresistive read transducer according to claim 1 wherein said etching step comprises the use of a directional etching method.
Claim 4
Dependent Claim
21 words
The method for making a magnetoresistive read transducer according to claim 2 wherein said directional etching method comprises ion beam milling.
Claim 5
Dependent Claim
26 words
The method for making a magnetoresistive read transducer according to claim 2 wherein said directional etching method is carried out at an angle to said transducer.
Claim 6
Dependent Claim
24 words
The method for making a magnetoresistive read transducer according to claim 4 wherein said angle is within the range of 70 to 80 degrees.
Claim 7
Dependent Claim
28 words
The method for making a magnetoresistive read transducer according to claim 4 wherein said transducer is rotated in a plane normal to said angle during said etching step.
Claim 8
Dependent Claim
19 words
The method for making a magnetoresistive read transducer according to claim 5 wherein said stencil comprises a photoresist material.
Claim 9
Dependent Claim
25 words
The method for making a magnetoresistive read transducer according to claim 7 wherein said photoresist material comprises a thin underlayer and a thick imaging layer.
Claim 10
Dependent Claim
18 words
The method for making a magnetoresistive read transducer according to claim 8 wherein said thin underlayer is undercut.
Claim 11
Dependent Claim
34 words
The method for making a magnetoresistive read transducer according to claim 1 additionally comprising the step of depositing means for producing a transverse bias in at least a part of said central active region.
Claim 12
Dependent Claim
30 words
The method for making a magnetoresistive read transducer according to claim 10 wherein said means for producing a transverse bias comprises a soft magnetic film spaced from said magnetoresistive layer.
References Cited (Backward Citations)
US4940511A
Cited
US4992901A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-06 | 1995-07-08 | 1996-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-06 | 1999-07-08 | 2000-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-06 | 2003-07-08 | 2004-01-07 | $7700.00 | Window Closed / Lapsed |