Electronic package comprising aluminum nitride and aluminum nitride-borosilicate glass composite
Assignee: WR Grace and Co Conn
•
Filing: 1990-08-01
•
Granted: 1991-12-17
•
Expires: 2010-08-01
Abstract
Abstract An electronic package comprising dielectric layers including a densified aluminum nitride (AlN) base layer and at least one densified AlN-borosilicate glass composite layer bonded thereto is described. Any of the dielectric layers may be metallized with conductive circuit patterns and can contain conductive vias. Production of this package is accomplished by hot pressing a greenware laminate comprising a densified base (e.g., AlN); at least one green sinterable sheet (e.g., AlN-borosilicate glass composite); and a green sheet of non-sinterable material (e.g., boron nitride [BN]). The respective green sheets comprise homogeneous mixtures of the ceramic powders and a binder, e.g., polyethylene. The polyethylene is burnt off during the hot press operation. Residual BN is removed by brushing and/or grit blasting, leaving the finished electronic package, all ceramic elements of which are densified. The package provides superior thermal conductivity, strength, dielectric properties, and silicon-compatibility.
Inventors
- 👤 Jack H. Enloe
- 👤 John W. Lau
- 👤 Roy W. Rice
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:56
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/581; C04B35/01; C04B35/10; C04B35/111; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/64; C04B35/645; H; H01; H01B; H01B3/00; H01B3/02; H01B3/08; H01B3/087; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/095; H10W70/60; H10W70/67; H10W70/69; H10W70/692; H10W99/00; H05K3/00; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629; Y; Y10; Y10S; Y10S156/00; Y10S156/918; Y10S156/919; Y10S156/922; Y10S156/924; Y10S156/925; Y10T; Y10T156/00; Y10T156/11; Y10T156/1153; Y10T156/1163; Y10T156/19; Y10T156/1911
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
82 words
A process for making an electronic package comprising (a) hot pressing a greenware laminate comprising: (1) an AlN base; (2) at last one green sinterable sheet; and (3) a green sheet of nonsinterable material; said green sinterable sheet consisting essentially of a homogeneous mixture of finely divided AlN and borosilicate glass particles and a binder; said green sheet of nonsinterable material consisting essentially of a homogeneous mixture of finely divided nonsinterable BN particles and a binder; and (b) removing the nonsinterable material.
Claim 2
Dependent Claim
82 words
A process for making an electronic package comprising (a) hot pressing a greenware laminate comprising: (1) an AlN base; (2) at last one green sinterable sheet; and (3) a green sheet of nonsinterable material; said green sinterable sheet consisting essentially of a homogeneous mixture of finely divided AlN and borosilicate glass particles and a binder; said green sheet of nonsinterable material consisting essentially of a homogeneous mixture of finely divided nonsinterable BN particles and a binder; and (b) removing the nonsinterable material.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein the binder is an organic binder which leaves no undesirable residue upon pyrolysis in the absence of oxygen.
Claim 4
Dependent Claim
11 words
A process according to claim 2, wherein the binder is polyethylene.
Claim 5
Dependent Claim
20 words
A process according to claim 1, wherein at least one of the laminate layers is metallized prior to hot pressing.
Claim 6
Dependent Claim
17 words
A process according to claim 1, wherein the laminate layers comprises vias containing metal particulates and binder.
Claim 7
Dependent Claim
34 words
A process according to claim 1, wherein the pressing is carried out at a temperature of about 600-1400° C., at a pressure of about 500-1000 psi, and for a time of about 1-2 hours.
Claim 8
Dependent Claim
46 words
A process according to claim 1, wherein the greenware laminate comprises: (1) densified AlN base; (2) at least one green sheet of AlN-borosilicate glass outlining an exposed surface cavity; (3) said cavity enclosing a green sheet plug of BN; and (4) a green sheet of BN.
Claim 9
Dependent Claim
20 words
A process according to claim 7, wherein at least one of the laminate layers is metallized prior to hot pressing.
Claim 10
Dependent Claim
109 words
A process for making a dense article comprising hot pressing a greenware laminate comprising the following layers: (1) a first layer comprising a dense AlN base; (2) a second layer comprising a green ceramic sheet having distinct areas of sinterable and non-sinterable green sheets in a desired pattern wherein said sinterable green sheet consists essentially of AlN and borosilicate glass particles and said non-sinterable green sheet consists essentially of BN particles; and (3) a third layer comprising a green ceramic replicate which compliments the second layer such that the sinterable and non-sinterable sheet materials are interchanged; and removing layer (3) as well as the non-sinterable material from layer (2).
Claim 11
Dependent Claim
109 words
A process for making a dense article comprising hot pressing a greenware laminate comprising the following layers: (1) a first layer comprising a dense AlN base; (2) a second layer comprising a green ceramic sheet having distinct areas of sinterable and non-sinterable green sheets in a desired pattern wherein said sinterable green sheet consists essentially of AlN and borosilicate glass particles and said non-sinterable green sheet consists essentially of BN particles; and (3) a third layer comprising a green ceramic replicate which compliments the second layer such that the sinterable and non-sinterable sheet materials are interchanged; and removing layer (3) as well as the non-sinterable material from layer (2).
Claim 12
Dependent Claim
26 words
A process according to claim 9, wherein layer (2) comprises more than one green sheet and accordingly layer (3) comprises a similar number of complimentary sheets.
Claim 13
Dependent Claim
82 words
A process for forming a ceramic green sheet comprising the steps: (i) mixing a homogeneous mixture of finely divided AlN-borosilicate glass, an organic binder which leaves no undesirable residue upon pyrolysis in the absence of oxygen and mineral oil; and compounding the mixture at an elevated temperature to facilitate melting of the organic binder; (ii) molding the compounded mixture in step (i) to form sheets by extrusion through a die; and (iii) removing the mineral oil by extraction with an organic solvent.
Claim 14
Dependent Claim
82 words
A process for forming a ceramic green sheet comprising the steps: (i) mixing a homogeneous mixture of finely divided AlN-borosilicate glass, an organic binder which leaves no undesirable residue upon pyrolysis in the absence of oxygen and mineral oil; and compounding the mixture at an elevated temperature to facilitate melting of the organic binder; (ii) molding the compounded mixture in step (i) to form sheets by extrusion through a die; and (iii) removing the mineral oil by extraction with an organic solvent.
Claim 15
Dependent Claim
27 words
A process according to claim 11, where the ceramic green sheets are formed in step (ii) by pressing the compounded mixture in step (i) into flat sheets.
Claim 16
Dependent Claim
117 words
A process for producing a dense AlN-borosilicate article comprising the following steps: (a) preparing at least one ceramic green sheet comprising AlN powder, borosilicate glass powder and an organic binder which leaves no undesirable residue upon pyrolysis in the absence of oxygen; (b) placing boron nitride sheets comprising boron nitride (BN) powder and an organic binder which leaves no undesirable carbonaceous residue upon pyrolysis in the absence of oxygen, on each side of the ceramic green sheet prepared in step (a) to form a composite; (c) hot pressing the composite prepared in step (b) under sufficient temperature and pressure to densify the ceramic; and (d) removing the BN layers on each side of the dense ceramic sheet.
Claim 17
Dependent Claim
117 words
A process for producing a dense AlN-borosilicate article comprising the following steps: (a) preparing at least one ceramic green sheet comprising AlN powder, borosilicate glass powder and an organic binder which leaves no undesirable residue upon pyrolysis in the absence of oxygen; (b) placing boron nitride sheets comprising boron nitride (BN) powder and an organic binder which leaves no undesirable carbonaceous residue upon pyrolysis in the absence of oxygen, on each side of the ceramic green sheet prepared in step (a) to form a composite; (c) hot pressing the composite prepared in step (b) under sufficient temperature and pressure to densify the ceramic; and (d) removing the BN layers on each side of the dense ceramic sheet.
References Cited (Backward Citations)
US4229873A
Cited
US4504411A
Cited
US4659611A
Cited
US4863683A
Cited
US4715892A
Cited
US4882212A
Cited
US4775596A
Cited
US4920640A
Cited
US4906514A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-16 | 1995-06-17 | 1995-12-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-16 | 1999-06-17 | 1999-12-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-16 | 2003-06-17 | 2003-12-17 | $7700.00 | Window Closed / Lapsed |