Heat insulating glass with dielectric multilayer coating
Assignee: Central Glass Co Ltd
•
Filing: 1990-07-31
•
Granted: 1991-12-17
•
Expires: 2010-07-31
Abstract
Abstract The invention provides a heat insulating glass plate with a multilayer coating which is fairly low in transmittance for solar radiation and fairly high in transmittance for the visible light and also for radio waves. The multilayer coating is a lamination of transparent and dielectric layers and has three essential layers in which the middle layer is higher or lower in refractivity than the inner and outer layers. The coating may have five layers in which the second and fourth layers are higher or lower in refractivity than the remaining three layers. Each layer of the multilayer coating is a metal compound film deposited by sputtering or CVD. In a first embodiment of the three-layer coating each of the inner and outer layers is formed of SnO x , ZrO x , TaO x or AlN x having a refractive index of 1.8-2.1 and the middle layer is formed of TiO x having a refractive index of 2.2-2.5. In a second embodiment, each of the inner and outer layers is formed of SnO x , TiO x , ZrO x , TaO x , ZnO x , AlN x or SiN x having a refractive index of 1.8-2.5 and the middle layer is formed of SiO x , AlO x or Si.AlO x having a refractive index of 1.4-1.7. The heat insulating glass plates are useful as vehicle window glasses, and the second embodiment of the multilayer coating is very suitable for use in laminated glass.
Inventors
- 👤 Yasunobu Iida
- 👤 Nobuyuki Takeuchi
- 👤 Masato Nakamura
- 👤 Koichi Furuya
- 👤 Hiroshi Nakashima
- 👤 Toshiaki Itoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:26
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/36; C03C17/3602; C03C17/3618; B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10009; B32B17/10036; B32B17/10165; B32B17/10174; C03C17/3411; C03C17/3417; C03C17/3429; C03C17/3435; C03C17/3626; C03C17/3644; C03C17/3652; C03C2217/00; C03C2217/70; C03C2217/73; C03C2217/734; C03C2217/78; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
235 words
A heat insulating glass plate particularly suitable as a vehicle window glass, having a transparent glass plate and a multilayer coating formed on one side of the glass plate, the multilayer coating comprising: a first layer which is a transparent and dielectric film of a aluminum nitride having a refractive index in the range from 1.8 to 2.1 deposited on a surface of the glass plate; a second layer which is a transparent and dielectric film of a titanium oxide having a refractive index in the range from 2.2 to 2.5 deposited on said first layer; and a third layer which is a transparent and dielectric film of a aluminum nitride having a refractive index in the range from 1.8 to 2.1 deposited on said second layer; each of said first, second and third layers being formed by a sputtering process or a chemical vapor deposition process and having a thickness in the range from 100 to 2000 Å and a surface resistivity not lower than 10 kΩ/□, the multilayer coating being formed such that the heat insulating glass plate is not lower than 65% in transmittance for the visible light, not higher than 15% in reflectance for the visible light and not higher than 65% in transmittance for solar radiation and such that the heat insulating glass plate is lower than the glass plate itself in transmittance for solar radiation by at least 5%.
Claim 2
Dependent Claim
235 words
A heat insulating glass plate particularly suitable as a vehicle window glass, having a transparent glass plate and a multilayer coating formed on one side of the glass plate, the multilayer coating comprising: a first layer which is a transparent and dielectric film of a aluminum nitride having a refractive index in the range from 1.8 to 2.1 deposited on a surface of the glass plate; a second layer which is a transparent and dielectric film of a titanium oxide having a refractive index in the range from 2.2 to 2.5 deposited on said first layer; and a third layer which is a transparent and dielectric film of a aluminum nitride having a refractive index in the range from 1.8 to 2.1 deposited on said second layer; each of said first, second and third layers being formed by a sputtering process or a chemical vapor deposition process and having a thickness in the range from 100 to 2000 Å and a surface resistivity not lower than 10 kΩ/□, the multilayer coating being formed such that the heat insulating glass plate is not lower than 65% in transmittance for the visible light, not higher than 15% in reflectance for the visible light and not higher than 65% in transmittance for solar radiation and such that the heat insulating glass plate is lower than the glass plate itself in transmittance for solar radiation by at least 5%.
Claim 3
Dependent Claim
53 words
A heat insulating glass plate according to claim 1, further comprising a protective coating layer which is a film of an oxide of at least one metal selected from the group consisting of Si and Al deposited on said third layer and has a thickness in the range from 100 to 2000 Å.
Claim 4
Dependent Claim
25 words
A heat insulating glass plate according to claim 2, wherein said protective coating layer has a refractive index in the range from 1.4 to 1.7.
Claim 5
Dependent Claim
103 words
A heat insulating glass plate according to claim 1, further comprising a fourth layer which is a transparent and dielectric film of a metal compound having a refractive index in the range from 2.2 to 2.5 deposited on said third layer, and a fifth layer which is a transparent and dielectric film of a metal compound having a refractive index in the range from 1.8 to 2.1 deposited on said fourth layer, each of said fourth and fifth layers being formed by a sputtering process or a chemical vapor deposition process and having a thickness in the range from 100 to 2000 Å.
Claim 6
Dependent Claim
32 words
A heat insulating glass plate according to claim 4, wherein said metal compound of said fifth layer is aluminum nitride, and said metal compound of fourth layer is an oxide of Ti.
Claim 7
Dependent Claim
53 words
A heat insulating glass plate according to claim 4, further comprising a protective coating layer which is a film of an oxide of at least one metal selected from the group consisting of Si and Al deposited on said fifth layer and has a thickness in the range from 100 to 2000 Å.
Claim 8
Dependent Claim
25 words
A heat insulating glass plate according to claim 6, wherein said protective coating layer has a refractive index in the range from 1.4 to 1.7.
Claim 9
Dependent Claim
18 words
A heat insulating glass plate according to claim 1, wherein the glass plate is a color glass plate.
Claim 10
Dependent Claim
239 words
A heat insulating glass plate particularly suitable as a vehicle window glass, having a transparent glass plate and a multilayer coating formed on one side of the glass plate, the multilayer coating consisting essentially of: a first layer which is a transparent and dielectric film of a tin oxide having a refractive index in the range from 1.8 to 2.1 deposited on a surface of the glass plate; a second layer which is a transparent and dielectric film of a titanium oxide having a refractive index in the range from 2.2 to 2.5 deposited on said first layer; and a third layer which is a transparent and dielectric film of a tin oxide having a refractive index in the range from 1.8 to 2.1 deposited on said second layer; each of said first, second and third layers being formed by a sputtering process or a chemical vapor deposition process and having a thickness in the range from about 400 to about 600 Å and a surface resistivity not lower than 10 kΩ/□, the multilayer coating being formed such that the heat insulating glass plate is not lower than 65% in transmittance for the visible light, not higher than 15% in reflectance for the visible light and not higher than 65% in transmittance for solar radiation and such that the heat insulating glass plate is lower than the glass plate itself in transmittance for solar radiation by at least 5%.
Claim 11
Dependent Claim
239 words
A heat insulating glass plate particularly suitable as a vehicle window glass, having a transparent glass plate and a multilayer coating formed on one side of the glass plate, the multilayer coating consisting essentially of: a first layer which is a transparent and dielectric film of a tin oxide having a refractive index in the range from 1.8 to 2.1 deposited on a surface of the glass plate; a second layer which is a transparent and dielectric film of a titanium oxide having a refractive index in the range from 2.2 to 2.5 deposited on said first layer; and a third layer which is a transparent and dielectric film of a tin oxide having a refractive index in the range from 1.8 to 2.1 deposited on said second layer; each of said first, second and third layers being formed by a sputtering process or a chemical vapor deposition process and having a thickness in the range from about 400 to about 600 Å and a surface resistivity not lower than 10 kΩ/□, the multilayer coating being formed such that the heat insulating glass plate is not lower than 65% in transmittance for the visible light, not higher than 15% in reflectance for the visible light and not higher than 65% in transmittance for solar radiation and such that the heat insulating glass plate is lower than the glass plate itself in transmittance for solar radiation by at least 5%.
Claim 12
Dependent Claim
54 words
The heat insulating glass plate of claim 9, further consisting essentially of a protective coating layer which is a film of an oxide of at least one metal selected from the group consisting of Si and Al deposited on said third layer and has a thickness in the range from 100 to 2000 Å.
Claim 13
Dependent Claim
23 words
The heat insulating glass plate of claim 10, wherein said protective coating has a refractive index in the range from 1.4 to 1.7.
Claim 14
Dependent Claim
17 words
The heat insulating glass plate of claim 9, wherein the glass plate is a color glass plate.
References Cited (Backward Citations)
US3853386A
Cited
US3922068A
Cited
US4099840A
Cited
US4504109A
Cited
JPS6081047A
Cited
US4647812A
Cited
JPS63131101A
Cited
JPS63206333A
Cited
JPS63242948A
Cited
JPS645930A
Cited
US4940636A
Cited
DE3902456A1
Cited
US4834857A
Cited
US4965121A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-16 | 1995-06-17 | 1995-12-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-16 | 1999-06-17 | 1999-12-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-16 | 2003-06-17 | 2003-12-17 | $7700.00 | Window Closed / Lapsed |