Method of making a metallic pattern on a substrate
Assignee: Huntsman Advanced Materials Americas LLC
•
Filing: 1990-06-04
•
Granted: 1991-12-17
•
Expires: 2010-06-04
Abstract
Abstract Metallic patterns, such as printed circuits, are prepared by immersing metal substrates, bearing electrodeposited films and resist films in patterned areas, into an aqueous solution or dispersion of a hardening agent so that the hardening agent diffuses only into the electrodeposited film. This is followed by curing the hardening agent by heat or irradiation to render it resistant to the solvent used to remove the resist film and to the etchant solution for the metal exposed when the resist film is removed.
Inventors
- 👤 Christopher P. Banks
- 👤 Edward Irving
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:00
CPC Classifications
H; H05; H05K; H05K1/00; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K2203/00; H05K2203/05; H05K2203/0562; H05K2203/0582; H05K2203/13; H05K2203/1333; H05K2203/135; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
194 words
A method of making a metallic pattern on a substrate having a surface comprising bare metal in predetermined areas and metal coated by a resist in remaining areas which comprises (i) protecting the bare metal by electrodepositing thereon a film of an organic resin, (ii) immersing the substrate bearing the electrodeposited resin film in an aqueous solution or dispersion of a hardening agent for said film, said hardening agent being a material which is curable, either alone or through reaction with functional groups in the electrodeposited resin film, on heating or irradiation, whereby said aqueous solution or dispersion diffuses into the surface of the electrodeposited resin film, (iii) subjecting the substrate to curing conditions for the hardening agent, thereby hardening the surface of the electrodeposited resin film and rendering it resistant to a solvent used to remove the resist and resistant to an etchant used to remove metal from areas exposed by removal of the resist, (iv) removing the resist from said remaining areas using a solvent which does not remove the electrodeposited resin film, and (v) etching metal exposed in step (iv) using an etchant which does not remove the electrodeposited resin film.
Claim 2
Independent Claim
194 words
A method of making a metallic pattern on a substrate having a surface comprising bare metal in predetermined areas and metal coated by a resist in remaining areas which comprises (i) protecting the bare metal by electrodepositing thereon a film of an organic resin, (ii) immersing the substrate bearing the electrodeposited resin film in an aqueous solution or dispersion of a hardening agent for said film, said hardening agent being a material which is curable, either alone or through reaction with functional groups in the electrodeposited resin film, on heating or irradiation, whereby said aqueous solution or dispersion diffuses into the surface of the electrodeposited resin film, (iii) subjecting the substrate to curing conditions for the hardening agent, thereby hardening the surface of the electrodeposited resin film and rendering it resistant to a solvent used to remove the resist and resistant to an etchant used to remove metal from areas exposed by removal of the resist, (iv) removing the resist from said remaining areas using a solvent which does not remove the electrodeposited resin film, and (v) etching metal exposed in step (iv) using an etchant which does not remove the electrodeposited resin film.
Claim 3
Dependent Claim
27 words
A method according to claim 1, in which the electrodeposited resin film is of an acrylic polymer or an adduct of an epoxide resin with an amine.
Claim 4
Dependent Claim
36 words
A method according to claim 2, in which said polymer is a copolymer of at least one monoacrylic monomer containing a carboxyl group, at least one monoacrylic ester and, optionally, at least one other vinyl monomer.
Claim 5
Dependent Claim
43 words
A method according to claim 2, in which the acrylic polymer is a copolymer of at least one monoacrylic monomer containing a tertiary amine group, at least one monoacrylic ester having a reactive functional group and, optionally, at least one other vinyl monomer.
Claim 6
Dependent Claim
38 words
A method according to claim 2, in which said polymer is a copolymer of (a) acrylic acid, methacrylic acid or dimethylaminoethyl methacrylate with (b) a hydroxyalkyl acrylate or methacrylate and, optionally, (c) at least one further vinyl monomer.
Claim 7
Dependent Claim
27 words
A method according to claim 5, in which said further vinyl monomer is selected from alkyl acrylates, alkyl methacrylates, styrene or mixtures of two or more thereof.
Claim 8
Dependent Claim
24 words
A method according to claim 2, in which the electrodeposited resin film is of an adduct of a polyglycidyl ether with a secondary monoamine.
Claim 9
Dependent Claim
24 words
A method according to claim 7, in which the polyglycidyl ether is a polyglycidyl ether of a polyhydric phenol, which may have been advanced.
Claim 10
Dependent Claim
15 words
A method according to claim 7, in which the secondary monoamine is a secondary alkanolamine.
Claim 11
Dependent Claim
42 words
A method according to claim 1, in which the hardening agent is a photocurable material having, on average, more than one polymerisable acrylic group per molecule, together with a photoinitiator therefor, and the substrate is irradiated with actinic radiation in step (iii).
Claim 12
Dependent Claim
22 words
A method according to claim 10, in which the photocurable material is a monomer having at least two acrylate or methacrylate groups.
Claim 13
Dependent Claim
24 words
A method according to claim 1, in which the hardening agent is a heat-curable aminoplast resin and the substrate is heated in step (iii).
Claim 14
Dependent Claim
17 words
A method according to claim 12, in which the aminoplast resin is a melamine-formaldehyde or benzoguanamine-formaldehyde resin.
Claim 15
Dependent Claim
23 words
A method according to claim 12, in which the aminoplast is used together with a curing catalyst which releases an acid on heating.
Claim 16
Dependent Claim
39 words
A method according to claim 1, in which the electrodeposited resin film contains carboxyl, hydroxyl or primary or secondary amino groups, the hardening agent is a material having blocked isocyanate groups and the substrate is heated in step (iii).
Claim 17
Dependent Claim
32 words
A method according to claim 15, in which the hardening agent is a reaction product of an aromatic diisocyanate with either an oxime or a mixture of an oxime and an alcohol.
Claim 18
Dependent Claim
30 words
A method according to claim 1, in which the aqueous solvent in which the hardening agent is dissolved or dispersed is a mixture of water with a water-miscible organic solvent.
Claim 19
Dependent Claim
39 words
A method according to claim 1, in which the resist is removed in step (iv) using an aqueous solvent and, after the etching step (v), at least part of the electrodeposited resin film is removed using an organic solvent.
Claim 20
Dependent Claim
15 words
A method according to claim 1, in which the metallic pattern is a printed circuit.
References Cited (Backward Citations)
US3542739A
Cited
US4113958A
Cited
US4125661A
Cited
US4375498A
Cited
US4604344A
Cited
US4746399A
Cited
US4751172A
Cited
US4861438A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-16 | 1995-06-17 | 1995-12-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-16 | 1999-06-17 | 1999-12-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-16 | 2003-06-17 | 2003-12-17 | $7700.00 | Window Closed / Lapsed |