Process for heating materials by microwave energy
Assignee: Rio Tinto Alcan International Ltd
•
Filing: 1989-10-04
•
Granted: 1991-12-10
•
Expires: 2009-10-04
Abstract
Abstract A process for preparing a heat-treated body from a material (preferably a dielectric ceramic) that does not couple well with microwaves while nevertheless using microwave energy for the heating step. The process involves the use of a microwave susceptor (i.e. a material that couples well with microwaves) as a means for generating heat in the material. To avoid contamination of the final product, a susceptor is chosen which is converted, during the heating step, to a substance which is substantially the same as the material itself, both the susceptor and the material are converted to the same desired final product, or the material is converted to a substance substantially the same as the susceptor. The resulting substantially pure heat-treated (and preferably sintered) bodies can be used for a variety of purposes, e.g. as substrates for micro-electronic devices. The process can also be used for joining bodies of non-susceptor materials without contaminating the resulting joint.
Inventors
- 👤 Prasad S. Apte
- 👤 Robert M. Kimber
- 👤 Aniket Pant
- 👤 Raymond Roy
- 👤 David N. Mitchell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:46
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/622; C04B35/64; H; H05; H05B; H05B6/00; H05B6/64; H05B6/80; C04B2235/00; C04B2235/65; C04B2235/66; C04B2235/667; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/06; C04B2237/064; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/345; C04B2237/348; C04B2237/36; C04B2237/366; C04B2237/50; C04B2237/70; C04B2237/706; H05B2206/00; H05B2206/04; H05B2206/046
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
90 words
A process of producing a heat-treated body of a refractory material from a substance that does not couple well with microwaves, said process comprising: contacting said substance with a microwave susceptor; and carrying out a heating step by irradiating the susceptor with microwaves to heat the susceptor and consequently said substance; wherein said substance, if different from said refractory material, and said susceptor, if different from said refractory material, are compounds which are converted, during said heating step, to a product having the same chemical composition as said refractory material.
Claim 2
Dependent Claim
90 words
A process of producing a heat-treated body of a refractory material from a substance that does not couple well with microwaves, said process comprising: contacting said substance with a microwave susceptor; and carrying out a heating step by irradiating the susceptor with microwaves to heat the susceptor and consequently said substance; wherein said substance, if different from said refractory material, and said susceptor, if different from said refractory material, are compounds which are converted, during said heating step, to a product having the same chemical composition as said refractory material.
Claim 3
Dependent Claim
18 words
A process according to claim 1 wherein said susceptor is converted to said product during said heating step.
Claim 4
Dependent Claim
17 words
A process according to claim 2 wherein said product is physically the same as said refractory material.
Claim 5
Dependent Claim
19 words
A process according to claim 2 wherein said susceptor is converted thermally to said product during said heating step.
Claim 6
Dependent Claim
24 words
A process according to claim 2 wherein said susceptor is converted chemically to said product during said heating step by reaction with a reagent.
Claim 7
Dependent Claim
18 words
A process according to claim 2 wherein said substance is alpha alumina and said susceptor is sub-alpha alumina.
Claim 8
Dependent Claim
29 words
A process according to claim 2 wherein said substance is aluminum nitride and said susceptor is sub-alpha alumina and wherein a nitrogen source is present during said heating step.
Claim 9
Dependent Claim
18 words
A process according to claim 1 wherein said substance is converted to said product during said heating step.
Claim 10
Dependent Claim
17 words
A process according to claim 8 wherein said product is physically the same as said refractory material.
Claim 11
Dependent Claim
19 words
A process according to claim 8 wherein said substance is converted thermally to said product during said heating step.
Claim 12
Dependent Claim
24 words
A process according to claim 8 wherein said substance is converted chemically to said product during said heating step by reaction with a reagent.
Claim 13
Dependent Claim
25 words
A process according to claim 8 wherein said substance is zirconia and said susceptor is an alloy of zirconia with a minor proportion of yttria.
Claim 14
Dependent Claim
22 words
A process according to claim 1 wherein said substance and said susceptor are both converted to said product during said heating step.
Claim 15
Dependent Claim
27 words
A process according to claim 13 wherein said substance and said susceptor are chemically converted during said heating step to said product by reaction with a reagent.
Claim 16
Dependent Claim
24 words
A process according to claim 14 wherein said substance is alpha alumina, said susceptor is sub-alpha alumina and said reagent is a nitrogen source.
Claim 17
Dependent Claim
18 words
A process according to claim 1 wherein said susceptor is present in said body before said heating step.
Claim 18
Dependent Claim
17 words
A process according to claim 1 wherein said susceptor substantially surrounds said body before said heating step.
Claim 19
Dependent Claim
22 words
A process according to claim 1 wherein said heating step raises the temperature of said body sufficiently to sinter said refractory material.
Claim 20
Dependent Claim
17 words
A process according to claim 1 wherein said body is subjected to pressing during said heating step.
Claim 21
Dependent Claim
14 words
A process according to claim 19 wherein said body is subjected to isostatic pressing.
Claim 22
Dependent Claim
100 words
In a method of joining bodies made of a substance that does not couple well with microwaves by bringing the bodies together and heating the bodies to join the bodies together, the improvement which comprises heating said bodies by surrounding adjacent areas of said bodies with a microwave susceptor and irradiating the susceptor with microwaves, while employing as at least one component of said susceptor, a substance which is at least partially converted during said heating step to a product which is substantially chemically the same as said substance in order to reduce contamination of said bodies by said susceptor.
Claim 23
Dependent Claim
100 words
In a method of joining bodies made of a substance that does not couple well with microwaves by bringing the bodies together and heating the bodies to join the bodies together, the improvement which comprises heating said bodies by surrounding adjacent areas of said bodies with a microwave susceptor and irradiating the susceptor with microwaves, while employing as at least one component of said susceptor, a substance which is at least partially converted during said heating step to a product which is substantially chemically the same as said substance in order to reduce contamination of said bodies by said susceptor.
Claim 24
Dependent Claim
34 words
A method according to claim 21 wherein a sinterable intermediary that is made of a material substantially the same as said substance is interposed between said bodies prior to irradiating said susceptor with microwaves.
Claim 25
Dependent Claim
18 words
A method according to claim 21 wherein said substance is alpha alumina and said susceptor is sub-alpha alumina.
References Cited (Backward Citations)
US2622187A
Cited
US3335253A
Cited
US3398251A
Cited
US3469053A
Cited
US3585258A
Cited
FR2249855A1
Cited
US4147911A
Cited
US4100386A
Cited
US4148614A
Cited
US4219361A
Cited
US4307277A
Cited
US4608473A
Cited
US4529856A
Cited
JPS60221367A
Cited
US4606748A
Cited
EP0251256A1
Cited
US4772770A
Cited
US4757172A
Cited
US4938673A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-09 | 1995-06-10 | 1995-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-09 | 1999-06-10 | 1999-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-09 | 2003-06-10 | 2003-12-10 | $7700.00 | Window Closed / Lapsed |