Polyamide-polyimide and polybenzoxazole-polyimide polymer
Assignee: EMD Performance Materials Corp
•
Filing: 1990-07-26
•
Granted: 1991-12-10
•
Expires: 2010-07-26
Abstract
Abstract The present invention provides polyamide-polyimide and polybenzoxazole-polyimide polymers derived therefrom with improved processing and film characteristics having incorporated into the polymeric backbone the polymeric condensation residuum of novel aromatic diamino compounds having the formula: ##STR1## wherein A is selected from the group consisting of SO 2 , O, S, CO, C 1 to C 6 alkyl, perfluoroalkyl or perfluoroarylalkyl having from 1 to 10 carbon atoms and a carbon-carbon double bond directly linking the two aromatic groups, and R is hydrogen. The polyamide-polyimide polymers of this invention are prepared by reacting compounds of the above formula, alone or admixed with other aromatic diamines, with one or more aromatic tetracarboxylic acids or anhydrides thereof. Polybenzoxazole-polyimide derivatives of such polyamide-polyimide.
Inventors
- 👤 Dinesh N. Khanna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:22
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/22; C08G73/10; C08G73/1085; C08G73/14
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
131 words
A polyamide-polyimide polymer comprising at least one recurring group of the structure: ##STR13## wherein the moiety B is a substituted or unsubstituted tetravalent aromatic radical selected from the group consisting of a benzene nucleus, polyphenyl nuclei having up to four phenyl rings and naphthalene nuclei, n is an integer sufficient to give rise to a polymer having an inherent viscosity of at least 0.1 dl/g as measured from a solution of the polymer in dimethylacetamide at 25° C. at a polymer concentration of 0.5 weight percent, A is selected from the group consisting of SO 2 , O, S, CO, C 1 to C 6 alkyl, perfluoroalkyl or perfluoroarylalkyl having from 1 to 10 carbon atoms, and a carbon-carbon double bond directly linking the two aromatic groups, and R is hydrogen.
Claim 2
Dependent Claim
131 words
A polyamide-polyimide polymer comprising at least one recurring group of the structure: ##STR13## wherein the moiety B is a substituted or unsubstituted tetravalent aromatic radical selected from the group consisting of a benzene nucleus, polyphenyl nuclei having up to four phenyl rings and naphthalene nuclei, n is an integer sufficient to give rise to a polymer having an inherent viscosity of at least 0.1 dl/g as measured from a solution of the polymer in dimethylacetamide at 25° C. at a polymer concentration of 0.5 weight percent, A is selected from the group consisting of SO 2 , O, S, CO, C 1 to C 6 alkyl, perfluoroalkyl or perfluoroarylalkyl having from 1 to 10 carbon atoms, and a carbon-carbon double bond directly linking the two aromatic groups, and R is hydrogen.
Claim 3
Dependent Claim
11 words
The polymer of claim 1 wherein the radical A is ##STR14##
Claim 4
Dependent Claim
11 words
The polymer of claim 2 wherein the radical A is ##STR15##
Claim 5
Dependent Claim
17 words
The polymer of claim 3 wherein the amido linkages are meta with respect to the A group.
Claim 6
Dependent Claim
17 words
The polymer of claim 4 wherein the imido linkages are para with respect to each amido linkage.
Claim 7
Dependent Claim
11 words
The polymer of claim 1 wherein the radical B is ##STR16##
Claim 8
Dependent Claim
44 words
The polymer of claim 1 wherein B is the residuum nucleus of a dianhydride selected from the group consisting of 1,2,4,5-benzene tetracarboxylic acid dianhydride, bis(3,4-dicarboxy-phenyl) ether dianhydride, 3,3',4,4'-benzophenone tetracarboxylic acid dianhydride, 3,4',4,4'-diphenyl tetracarboxylic acid dianhydride, 2,2-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride and 4,4'-bis[2-(3,4-dicarboxyphenyl) hexafluoroisopropyl] diphenyl ether dianhydride.
Claim 9
Dependent Claim
21 words
The polymer of claim 7 wherein, A is ##STR17## and the amido linkages are meta with respect to the A group.
Claim 10
Dependent Claim
17 words
The polymer of claim 8 wherein the imido linkages are para with respect to each amido linkage.
Claim 11
Dependent Claim
9 words
A solvent solution of the polymer of claim 1.
Claim 12
Dependent Claim
9 words
A dried film comprising the polymer of claim 1.
References Cited (Backward Citations)
US4954613A
Cited
US4980447A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-09 | 1995-06-10 | 1995-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-09 | 1999-06-10 | 1999-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-09 | 2003-06-10 | 2003-12-10 | $7700.00 | Window Closed / Lapsed |