Method for producing large silica sol-gels doped with inorganic and organic compounds
Assignee: GRYPHON VENTURES II LP
•
Filing: 1990-11-06
•
Granted: 1991-12-10
•
Expires: 2010-11-06
Abstract
Abstract A method of producing doped, monolithic objects of silica in a wide variety of shapes which comprises impregnating a stabilized silica sol-gel monolith with a doping solution having therein a wide range of inorganic or organic dopants to achieve unique physical properties, such as specific optical absorption bands or scintillation properties.
Inventors
- 👤 Jean-Luc Nogues
- 👤 Larry L. Hench
- 👤 Shi-Ho Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:08
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; C; C03; C03B; C03B19/00; C03B19/12; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C; C03C14/00; C03C14/006; C03C14/008; C03C23/00; C03C23/0095; C03C2203/00; C03C2203/20; C03C2203/36; C03C2214/00; C03C2214/16; C03C2214/17; C03C2214/32; G02F; G02F1/00; G02F1/35; G02F1/355; G02F1/3555
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
91 words
A method of fabricating monolithic silica objects having dopants therein, comprising the steps of: (a) preparing at least one doping solution comprising a solvent having dissolved therein one or more inorganic or organic dopants; (b) preparing an ultraporous, dried silica-gel matrix; (c) stabilizing said dried silica-gel matrix by subjecting said dried silica-gel matrix to a heat treatment to produce an ultraporous, stabilized silica-gel monolith; (d) contacting said ultraporous, stabilized silica-gel monolith with at least one of said doping solutions to produce a doped silica-gel monolith; (e) drying said doped silica-gel monolith.
Claim 2
Independent Claim
91 words
A method of fabricating monolithic silica objects having dopants therein, comprising the steps of: (a) preparing at least one doping solution comprising a solvent having dissolved therein one or more inorganic or organic dopants; (b) preparing an ultraporous, dried silica-gel matrix; (c) stabilizing said dried silica-gel matrix by subjecting said dried silica-gel matrix to a heat treatment to produce an ultraporous, stabilized silica-gel monolith; (d) contacting said ultraporous, stabilized silica-gel monolith with at least one of said doping solutions to produce a doped silica-gel monolith; (e) drying said doped silica-gel monolith.
Claim 3
Dependent Claim
25 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, further comprising sealing the surface porosity of said doped silica-gel monolith.
Claim 4
Dependent Claim
33 words
A method of fabricating monolithic silica objects having dopants therein according to claim 2, wherein said sealing is carried out by subjecting the surface porosity of said doped silica-gel monolith to localized heating.
Claim 5
Dependent Claim
34 words
A method of fabricating monolithic silica objects having dopants therein according to claim 2, wherein said sealing is carried out by applying a polymer coating onto the surface porosity of said doped silica-gel monolith.
Claim 6
Dependent Claim
36 words
A method of fabricating monolithic silica objects having dopants therein according to claim 2, wherein said sealing is carried out by subjecting said monolith to low temperature densification with surface doping of low valence fluxing additives.
Claim 7
Dependent Claim
36 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, further comprising densifying said doped silica-gel monolith by heating said monolith up to a temperature of about 800° to about 1300° C.
Claim 8
Dependent Claim
27 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said ultraporous, stabilized silica-gel monolith possesses both open porosity and optical properties.
Claim 9
Dependent Claim
40 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said heat treatment is carried out at a temperature which produces a gel structure with open porosity but with enough strength to withstand subsequent doping.
Claim 10
Dependent Claim
25 words
A method of fabricating monolithic silica objects having dopants therein according to claim 8, wherein said temperature is from about 150° to about 1150° C.
Claim 11
Dependent Claim
23 words
A method of fabricating monolithic silica objects having dopants therein according to claim 9, wherein said temperature is 500° to about 1150° C.
Claim 12
Dependent Claim
43 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said dopant is a transition element selected from the group consisting of Ag, Al, Au, Ba, Co, Cr, Cu, Fe, Mn, Nb, Ni, Pb, Ti, V and Zr.
Claim 13
Dependent Claim
32 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said dopant is a rare earth element selected from the group consisting of Er, Ce and Nd.
Claim 14
Dependent Claim
22 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said dopant is a non-linear optic compound.
Claim 15
Dependent Claim
20 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said dopant is a dye.
Claim 16
Dependent Claim
21 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said dopant is a laser dye.
Claim 17
Dependent Claim
38 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said stabilized silica-gel monolith is contacted with at least one doping solution by immersing said monolith in said at least one doping solution.
Claim 18
Dependent Claim
34 words
A method of fabricating monolithic silica objects having dopants therein according to claim 16, wherein said stabilized silica-gel monolith is immersed in said at least one doping solution under pressure or in a vacuum.
Claim 19
Dependent Claim
38 words
A method of fabricating monolithic silica objects having dopants therein according to claim 16, wherein said stabilized silica-gel monolith is immersed in said at least one doping solution while subjecting said doping solution to mechanical or ultrasonic stirring.
Claim 20
Dependent Claim
34 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said stabilized silica-gel monolith is only partially contacted with a doping solution by spraying, local deposition or partial immersion.
Claim 21
Dependent Claim
43 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, further comprising masking a portion of the stabilized silica-gel monolith prior to contacting with said doping solution and then contacting the masked, stabilized silica-gel monolith with a doping solution.
Claim 22
Dependent Claim
27 words
A method of fabricating monolithic silica objects having dopants therein according to claim 1, wherein said stabilized silica-gel monolith is contacted with more than one doping solution.
References Cited (Backward Citations)
US4286024A
Cited
US4389233A
Cited
US4400306A
Cited
US4495297A
Cited
US4812155A
Cited
US4840653A
Cited
US4851023A
Cited
US4851373A
Cited
US4849378A
Cited
US4778826A
Cited
US4769477A
Cited
US4770671A
Cited
US4789533A
Cited
US4800180A
Cited
US4883779A
Cited
US4788164A
Cited
US4810674A
Cited
US4765818A
Cited
US4851270A
Cited
US4898755A
Cited
US4788373A
Cited
US4777311A
Cited
US4878224A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-09 | 1995-06-10 | 1995-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-09 | 1999-06-10 | 1999-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-09 | 2003-06-10 | 2003-12-10 | $7700.00 | Window Closed / Lapsed |