Glossy finish fiber reinforced molded product and processes of construction
Assignee: CH Masland and Sons
•
Filing: 1990-05-01
•
Granted: 1991-12-10
•
Expires: 2010-05-01
Abstract
Abstract Fiber reinforced thermoplastic molded products, sheets, and the like, having a glossy surface are produced by intimately blending discrete reinforcing fibers (e.g. fiberglass) and thermoplastic fibers (e.g. polypropylene or polycarbonate) into a web. The web is heated to the melting point of the thermoplastic fibers while applying pressure, to eliminate air and press the web into a consolidated structure. Breakage of the reinforcing fibers is minimized by limiting the thickness of the web and limiting the pressure so as to produce a consolidated structure with minimal fiber breakage and a Notched Izod of at least one. Layered consolidated structures, some without reinforcing fibers, may be heated and pressed together to form a final structure having a thickness greater than the individual structures. The great majority of the fibers are provided so that the fibers of each type are within the range of about 0.5-5 inches. A sheet capable of replacing an automotive metal panel (that is having sufficiently high gloss, rigidity and impact characteristics) is provided, the sheet having a Notched Izod of at least about two and preferably at least about five. Products with Notched Izods of up to eight or nine may be achieved.
Inventors
- 👤 Rayna W. Smith
- 👤 Gerald W. Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:05
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/54; B29C70/543; B29C70/40; B29C70/42; B29C70/46; B29C70/467; B29K; B29K2995/00; B29K2995/0018; B29K2995/0022; B29L; B29L2031/00; B29L2031/30; B29L2031/3005
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
189 words
A process of preparing a fiber reinforced thermoplastic product having a glossy surface, comprising the steps of: (a) providing a reinforcing fiber in the form of discrete, single, staple filaments; (b) providing a thermoplastic fiber in the form of discrete staple filaments; (c) practicing steps (a) and (b) so that the length of the great majority of fibers of each type is within the range of about 0.5-5 inches; (d) intimately blending the discrete reinforcing and thermoplastic fibers into a loose non-needled non-woven web devoid of liquid binder; and (e) heating the loose non-woven web to at least the melting point of the thermoplastic fibers and applying pressure to the web to cause the thermoplastic fibers to melt to eliminate air from the web and press the web into a consolidated product, thermoplastic material from melted thermoplastic fibers providing the matrix for reinforcing fibers in the molded product, the thickness of the web and the temperature and pressure conditions being controlled during forming so as to minimize breakage of the reinforcing fiber, and so as to provide a glossy product with a Notched Izod of at least about two.
Claim 2
Dependent Claim
189 words
A process of preparing a fiber reinforced thermoplastic product having a glossy surface, comprising the steps of: (a) providing a reinforcing fiber in the form of discrete, single, staple filaments; (b) providing a thermoplastic fiber in the form of discrete staple filaments; (c) practicing steps (a) and (b) so that the length of the great majority of fibers of each type is within the range of about 0.5-5 inches; (d) intimately blending the discrete reinforcing and thermoplastic fibers into a loose non-needled non-woven web devoid of liquid binder; and (e) heating the loose non-woven web to at least the melting point of the thermoplastic fibers and applying pressure to the web to cause the thermoplastic fibers to melt to eliminate air from the web and press the web into a consolidated product, thermoplastic material from melted thermoplastic fibers providing the matrix for reinforcing fibers in the molded product, the thickness of the web and the temperature and pressure conditions being controlled during forming so as to minimize breakage of the reinforcing fiber, and so as to provide a glossy product with a Notched Izod of at least about two.
Claim 3
Dependent Claim
25 words
A process as recited in claim 1 wherein step (c) is practiced so that the thermoplastic fibers have a diameter of 0.020 inches or less.
Claim 4
Independent Claim
153 words
A method of producing a fiber reinforced thermoplastic molded part or preform having a glossy surface, comprising the steps of: (a) blending discrete, single, reinforcing fibers, and thermoplastic fibers, intimately together into a loose non-needled non-woven batt devoid of liquid binder; (b) inserting the batt in a combination press/mold; and (c) applying heat and pressure to the batt with the press/mold having polished metal plates so a to melt the thermoplastic fibers while eliminating air from the web and so as to form the loose non-woven batt into a molded part or preform, thermoplastic material from melted thermoplastic fibers providing the matrix or reinforcing fibers in the molded product, the thickness of the batt and the temperature and pressure conditions being controlled during forming so as to minimize breakage of the reinforcing fiber, and so as to provide the glossy molded part or preform with a Notched Izod of at least about two.
Claim 5
Independent Claim
153 words
A method of producing a fiber reinforced thermoplastic molded part or preform having a glossy surface, comprising the steps of: (a) blending discrete, single, reinforcing fibers, and thermoplastic fibers, intimately together into a loose non-needled non-woven batt devoid of liquid binder; (b) inserting the batt in a combination press/mold; and (c) applying heat and pressure to the batt with the press/mold having polished metal plates so a to melt the thermoplastic fibers while eliminating air from the web and so as to form the loose non-woven batt into a molded part or preform, thermoplastic material from melted thermoplastic fibers providing the matrix or reinforcing fibers in the molded product, the thickness of the batt and the temperature and pressure conditions being controlled during forming so as to minimize breakage of the reinforcing fiber, and so as to provide the glossy molded part or preform with a Notched Izod of at least about two.
Claim 6
Dependent Claim
19 words
A method as recited in claim 3 wherein the thermoplastic fibers have a diameter of 0.020 inches or less.
Claim 7
Dependent Claim
20 words
A method as recited in claim 3 wherein step (c) is practiced by applying the pressure of about 10 psi.
Claim 8
Dependent Claim
20 words
A process as recited in claim 1 wherein step (e) is practiced by applying a pressure of about 10 psi.
References Cited (Backward Citations)
US3671615A
Cited
US4083913A
Cited
US4229397A
Cited
US4390489A
Cited
US4290988A
Cited
US4258094A
Cited
US4258093A
Cited
US4418031A
Cited
US4568581A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-09 | 1995-06-10 | 1995-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-09 | 1999-06-10 | 1999-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-09 | 2003-06-10 | 2003-12-10 | $7700.00 | Window Closed / Lapsed |