US4083913A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Stabilization of mixed-fiber webs
Assignee: Fiber Technology Corp
•
Filing: 1973-12-17
•
Granted: 1978-04-11
•
Expires: 1993-12-17
Abstract
Abstract Air-laid fibrous webs are formed from randomly-oriented mixed fibers containing a minor proportion of short, flock-length, thermoplastic and thermoretractile fibers. The air-laid web is then heated, without pressure, to cause melting of the thermoplastic fibers to the point of substantially complete loss of fiber identity. The relative orientation of the web thus formed is stabilized so that the fibers therein maintain their general positional relationships through subsequent stresses incurred during the operations of printing, saturating, drying, winding into roll form and the like.
Inventors
- 👤 Preston F. Marshall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:03
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/70; D04H1/72; D04H1/40; D04H1/54
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
182 words
The process of stabilizing the relative orientation and distribution of the fibers in an air-laid web, the fibers of said web possessing a substantially random orientation comprising: a. forming a substantially randomly oriented air-laid web comprising a major portion of non-thermally sensitive fibers, said non-thermally sensitive fibers having admixed therewith in random distribution and oriented throughout the length, breadth, and depth of said web, a minor proportion of fibers of a drawn, thermoplastic and thermoretractile nature which melt at a temperature below the melting point of said non-thermally sensitive fibers, said drawn thermoretractile fibers consisting essentially of fibers between 0.05 and 0.40 inches in length; b. heating the mixed fiber web, substantially without pressure, sufficiently to cause said drawn thermoretractile fibers to retract and melt to a series of fluid beads, with a substantial loss of fiber identity, said beads locating principally at the crossover points of said non-thermally sensitive fibers by said drawn fibers retracting thereon; and, c. cooling said web until said fluid beads solidify so as to stabilize the relative orientation and distribution of the fibers in said web.
Claim 2
Dependent Claim
182 words
The process of stabilizing the relative orientation and distribution of the fibers in an air-laid web, the fibers of said web possessing a substantially random orientation comprising: a. forming a substantially randomly oriented air-laid web comprising a major portion of non-thermally sensitive fibers, said non-thermally sensitive fibers having admixed therewith in random distribution and oriented throughout the length, breadth, and depth of said web, a minor proportion of fibers of a drawn, thermoplastic and thermoretractile nature which melt at a temperature below the melting point of said non-thermally sensitive fibers, said drawn thermoretractile fibers consisting essentially of fibers between 0.05 and 0.40 inches in length; b. heating the mixed fiber web, substantially without pressure, sufficiently to cause said drawn thermoretractile fibers to retract and melt to a series of fluid beads, with a substantial loss of fiber identity, said beads locating principally at the crossover points of said non-thermally sensitive fibers by said drawn fibers retracting thereon; and, c. cooling said web until said fluid beads solidify so as to stabilize the relative orientation and distribution of the fibers in said web.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein said drawn thermoretractile fibers are polyolefin fibers.
Claim 4
Dependent Claim
41 words
The process of claim 1 including simultaneously admixing a proportion of paper fluff fibers with said non-thermally sensitive fibers and said drawn thermoretractile fibers during the forming of said air-laid web so as to be in random distribution throughout said web.
Claim 5
Dependent Claim
18 words
The process of claim 2 wherein said polyolefin fibers are a copolymer of polyvinyl acetate and polyvinyl chloride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-10 | 1981-10-10 | 1982-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-10 | 1985-10-10 | 1986-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-10 | 1989-10-10 | 1990-04-11 | $7700.00 | Window Closed / Lapsed |