US5069945A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ultrapous thin-film membranes
Assignee: Pall Filtration and Separations Group Inc
•
Filing: 1989-11-21
•
Granted: 1991-12-03
•
Expires: 2009-11-21
Abstract
Abstract Mono-layer thin film membranes are provided which are ultraporous. Such mono-layers are formed having a thickness on the order of about 1.2 to 150 nanometers, by a variety of polymerization, cross-linking, and film treatment processes to achieve the development of controlled pore sizes in the ultraporous size range corresponding to molecular weight cutoff values of from 500 to about 1,000,000. Such thin film mono-layer membranes are ordinarily supported on a microporous support material, desirably a microporous polymer membrane having a smooth, microporous skin with pore sizes in the range of from about 0.1 microns to about 3 microns, preferably from about 0.1 microns to about 0.5 microns, in diameter. There may be an intermediate gel layer. These membranes are useful for ultraporous, dialysis, and molecular separations.
Inventors
- 👤 Wolfgang J. Wrasidlo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:36
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0093; B01D69/00; B01D69/02; B01D69/12; B01D69/122; B01D69/125; B01D69/1251; B01D2323/00; B01D2323/30
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
50 words
A method of making a cross linked polymeric ultraporous thin film comprising forming a cross linked polymeric thin film and controlling the cross link density of said thin film to provide a limiting pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 2
Independent Claim
50 words
A method of making a cross linked polymeric ultraporous thin film comprising forming a cross linked polymeric thin film and controlling the cross link density of said thin film to provide a limiting pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein said thin film is formed by interfacial condensation polymerization.
Claim 4
Dependent Claim
27 words
The method of claim 2 wherein said thin film is a highly branched polymer member selected from the group consisting of polysaccharides, polysilicones, polyamides, polyacrylics, and polyimines.
Claim 5
Dependent Claim
25 words
The method of claim 3 wherein the cross link density is controlled by regulating one or more of the cross linking determinants of the polymerization.
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein said thin film is formed by interfacial cross linking of an oligomer or polymer with a cross linking agent.
Claim 7
Dependent Claim
27 words
The method of claim 5 wherein the cross link density is controlled by regulating one or more of the cross linking determinants of the cross linking reaction.
Claim 8
Dependent Claim
24 words
The method of claim 1 wherein said thin film is formed as an active layer supported on and adhered to a microporous membrane support.
Claim 9
Dependent Claim
39 words
The method of claim 1 wherein said thin film is formed as an active layer supported on and adhered to a cross linked polymer gel, which gel is in turn supported on and adhered to a microporous membrane support.
Claim 10
Dependent Claim
11 words
The method of claim 8 wherein said gel is a hydrogel.
Claim 11
Dependent Claim
43 words
The method of claim 1 wherein said cross linked thin film is formed and the cross link density thereof is subsequently decreased by treating said thin film with an agent which controllably and selectively decreases the cross link density of said thin film.
Claim 12
Dependent Claim
20 words
The method of claim 10 wherein said agent is selected from the group consisting of oxidizing agents and hydrolyzing agents.
Claim 13
Dependent Claim
18 words
The method of claim 1 wherein said thin film is formed by cross linking of a preformed polymer.
Claim 14
Dependent Claim
52 words
The method of claim 12 wherein said preformed polymer is formed in a first solution and a cross linking agent for said polymer is in a second solution immiscible with said first solution, said first solution is formed in a layer and contacted with said second solution to form said thin film.
Claim 15
Dependent Claim
27 words
The method of claim 13 wherein the cross link density of said thin film is controlled by limiting the concentration of the polymer in said first solution
Claim 16
Dependent Claim
29 words
The method of claim 13 wherein the cross link density of said thin film is controlled by limiting the concentration of the cross linking agent in said second solution.
Claim 17
Dependent Claim
71 words
The method of claim 13 wherein the cross link density of said thin film is controlled by forming a thin layer of said first solution on a support, draining said layer until a stable film of said first solution is attained, contacting said layer with a solution of a cross linking agent in said second solution for a time and at a temperature sufficient to attain the required cross link density.
Claim 18
Dependent Claim
24 words
The method of claim 16 wherein said thin film is formed as an active layer supported on and adhered to a microporous membrane support.
Claim 19
Dependent Claim
39 words
The method of claim 17 wherein said thin film is formed as an active layer supported on and adhered to a cross linked polymer gel, which gel is in turn supported on and adhered to a microporous membrane support.
Claim 20
Independent Claim
52 words
The method of increasing the pore size of a cross linked polymer thin film comprising contacting said film with an agent which controllably decreases the cross link density of said thin film to produce a pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 21
Independent Claim
52 words
The method of increasing the pore size of a cross linked polymer thin film comprising contacting said film with an agent which controllably decreases the cross link density of said thin film to produce a pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 22
Dependent Claim
22 words
The method of claim 19 wherein said agent is a member selected from the group consisting of oxidizing agents and hydrolyzing agents.
Claim 23
Independent Claim
97 words
The method of increasing the pore size of a cross linked polymer thin film membrane, wherein said polymer is a polyurea or a polyamide, by the steps of forming an aqueous solution of polyamide, by the steps of forming an aqueous solution of hypochlorite, and contacting said thin film membrane with said aqueous solution for a time and at a temperature sufficient to decrease the cross link density of said thin film to an extent sufficient to attain a desired pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 24
Independent Claim
97 words
The method of increasing the pore size of a cross linked polymer thin film membrane, wherein said polymer is a polyurea or a polyamide, by the steps of forming an aqueous solution of polyamide, by the steps of forming an aqueous solution of hypochlorite, and contacting said thin film membrane with said aqueous solution for a time and at a temperature sufficient to decrease the cross link density of said thin film to an extent sufficient to attain a desired pore size corresponding to molecular weight cutoff values of from at least 500 to at least 1,000,000.
Claim 25
Dependent Claim
36 words
The method of claim 21 wherein said pore size is determined by the concentration of said solution of hypochlorite, and said contacting is for a time and at a temperature sufficient to attain steady state conditions.
References Cited (Backward Citations)
US3904519A
Cited
US4039440A
Cited
US4244817A
Cited
US4277344A
Cited
US4360434A
Cited
EP0072002A1
Cited
EP0098352A2
Cited
US4429122A
Cited
EP0111714A2
Cited
US4659474A
Cited
EP0189019A1
Cited
US4814082A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-02 | 1995-06-03 | 1995-12-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-02 | 1999-06-03 | 1999-12-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-02 | 2003-06-03 | 2003-12-03 | $7700.00 | Window Closed / Lapsed |