US5063121A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Circuit substrate comprising nitride type ceramics, method for preparing it, and metallizing composition for use in it
Assignee: Toshiba Corp
•
Filing: 1989-09-22
•
Granted: 1991-11-05
•
Expires: 2009-09-22
Abstract
Abstract Disclosed is: i) a nitride type ceramic substrate comprises; a nitride type ceramic sintered sheet; a conductive metallized layer formed on the nitride type ceramic sintered sheet; and a layer of a compound containing yttria and alumina, present in the vicinity of the interface between the nitride type ceramic sintered sheet and the metallized layer; ii) a circuit substrate comprises; a substrate comprising a nitride type ceramic sintered sheet; a metallized layer comprising molybdenum and tungsten as a main component and an activation metal added thereto formed on the substrate; and a layer of a compound containing yttria and alumina, present inside of the metallized layer and in the vicinty of the interface between the substrate and the metallized layer; iii) a surface conductive ceramic substrate which is characterized by comprising; a nitride type ceramic substrate; and a conductive metallized layer chiefly comprised of at least one of Mo and W, a group IVa active metal element and a fourth period transition metal (except for Ti), formed on the substrate; and iv) a surface conductive ceramic substrate which is characterized by comprising a nitride type ceramic substrate; an intermediate reactive layer chiefly comprised of a compound containing a grain boundary constitutent phase component of the ceramic substrate, and a compound of a group IVa active metal; and a conductive metallized layer chiefly comprised of at least one of molybdenum and tungsten, a nitride of a group IVa active metal and a composite compound comprising an oxide of a group IVa active metal and an oxide of a fourth period transition metal (except for titanium), formed on the substrate with the interpositon of the intermediate reactive layer. Disclosed is also a method for preparing these substrates and metallizing composition used therefor. According to this invention, a circuit substrate having a conductive metallized layer formed thereon with a high joint strength can be obtained.
Inventors
- 👤 Hideki Sato
- 👤 Nobuyuki Mizunoya
- 👤 Hironori Asai
- 👤 Kazuo Anzai
- 👤 Tsuyoshi Hatano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 07:17
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/515; C04B35/58; C04B35/581; C04B41/45; C04B41/50; C04B41/51; C04B41/5133; C04B41/52; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C04B41/89; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/098; H10W70/60; H10W70/62; H10W70/66; H10W70/67; H10W70/69; H10W70/692; C04B2111/00; C04B2111/00474; C04B2111/00844; H05K1/09; H05K1/092; H05K3/00; H05K3/38; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/24926
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
70 words
A ceramic substrate comprising: a substrate comprising a nitride ceramic sintered sheet; a metallized layer formed on said substrate and comprising molybdenum, tungsten or a mixture thereof as a main component and at least one group IVb activation metal element; and a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and said metallized layer and uniformly penetrating said metallized layer.
Claim 2
Dependent Claim
70 words
A ceramic substrate comprising: a substrate comprising a nitride ceramic sintered sheet; a metallized layer formed on said substrate and comprising molybdenum, tungsten or a mixture thereof as a main component and at least one group IVb activation metal element; and a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and said metallized layer and uniformly penetrating said metallized layer.
Claim 3
Dependent Claim
44 words
The ceramic substrate according to claim 1, wherein said metallized layer is formed by coating a metallizing paste comprising molybdenum, tungsten or a mixture thereof, and yttria and alumina solely or in the form of a compound of yttria and alumina and sintering it.
Claim 4
Dependent Claim
35 words
The ceramic substrate according to claim 1, wherein said metallized layer is formed by; coating a paste comprising a compound of yttria and alumina on said substrate; coating a metallizing paste thereon; and firing them.
Claim 5
Dependent Claim
51 words
A ceramic substrate comprising: a nitride ceramic substrate; and a conductive metallized layer mainly comprised of at least one of Mo and W, a group IVb active metal element and at least one metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V, formed on said substrate.
Claim 6
Dependent Claim
51 words
A ceramic substrate comprising: a nitride ceramic substrate; and a conductive metallized layer mainly comprised of at least one of Mo and W, a group IVb active metal element and at least one metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V, formed on said substrate.
Claim 7
Dependent Claim
96 words
A ceramic substrate comprising: a nitride ceramic substrate; an intermediate reactive layer mainly comprised of a compound containing a grain boundary constituent phase component of said ceramic substrate, and a compound of a group IVb active metal; and a conductive metallized layer mainly comprised of at least one of molybdenum and tungsten, a nitride of a group IVb active metal and a composite compound comprising an oxide of a group IVb active metal and an oxide of Co, Ni, Fe, Mn, Cr or V, formed on said substrate with the interposition of said intermediate reactive layer.
Claim 8
Dependent Claim
96 words
A ceramic substrate comprising: a nitride ceramic substrate; an intermediate reactive layer mainly comprised of a compound containing a grain boundary constituent phase component of said ceramic substrate, and a compound of a group IVb active metal; and a conductive metallized layer mainly comprised of at least one of molybdenum and tungsten, a nitride of a group IVb active metal and a composite compound comprising an oxide of a group IVb active metal and an oxide of Co, Ni, Fe, Mn, Cr or V, formed on said substrate with the interposition of said intermediate reactive layer.
Claim 9
Dependent Claim
31 words
The ceramic substrate according to claim 5, wherein said conductive metallized layer further comprises at least one compound selected from the group consisting of a nickel compound and a calcium compound.
Claim 10
Dependent Claim
15 words
The ceramic substrate according to claim 5, wherein the group IVb active metal comprises titanium.
Claim 11
Dependent Claim
25 words
The ceramic substrate according to claim 5, wherein said composite compound comprises an oxide of a group IVb active metal and an oxide of cobalt.
Claim 12
Dependent Claim
18 words
The ceramic substrate according to claim 5, wherein the nitride ceramic substrate comprises an aluminum nitride ceramic substrate.
Claim 13
Dependent Claim
25 words
The ceramic substrate according to claim 1, wherein said group IVb activation metal element is selected from the group consisting of titanium, zirconium and hafnium.
Claim 14
Dependent Claim
19 words
The ceramic substrate according to claim 1, wherein said nitride ceramic sintered sheet comprises an aluminum nitride sintered sheet.
Claim 15
Dependent Claim
25 words
The ceramic substrate according to claim 1, wherein said metallized layer comprises about 3 to 25% by weight of said compound comprising yttria and alumina.
Claim 16
Dependent Claim
26 words
The ceramic substrate according to claim 1, wherein said nitride ceramic sintered sheet includes at least about 5% by weight of Y 2 O 3 .
Claim 17
Dependent Claim
11 words
A circuit substrate comprising a ceramic substrate according to claim 1.
Claim 18
Dependent Claim
67 words
A metallizing composition for use in a nitride ceramic substrate comprising from about 26 to 90% by weight of molybdenum and tungsten, from about 5 to 70% by weight of an oxide of a group IVb active metal, and from about 2 to 20% by weight of at least one compound of a metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V.
Claim 19
Dependent Claim
67 words
A metallizing composition for use in a nitride ceramic substrate comprising from about 26 to 90% by weight of molybdenum and tungsten, from about 5 to 70% by weight of an oxide of a group IVb active metal, and from about 2 to 20% by weight of at least one compound of a metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V.
Claim 20
Dependent Claim
22 words
The metallizing composition for use in a nitride ceramic substrate according to claim 15, wherein said group IVb active metal comprises titanium.
Claim 21
Dependent Claim
22 words
The metallizing composition for use in a nitride ceramic substrate according to claim 15, wherein said compound comprises a compound of cobalt.
Claim 22
Dependent Claim
66 words
A metallizing composition for use in a nitride ceramic comprising from about 26 to 90% by weight of molybdenum and tungsten, from about 5 to 70% by weight of an oxide of a group IVb active metal, and from about 2 to 20% by weight of at least one compound of a metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V.
Claim 23
Dependent Claim
66 words
A metallizing composition for use in a nitride ceramic comprising from about 26 to 90% by weight of molybdenum and tungsten, from about 5 to 70% by weight of an oxide of a group IVb active metal, and from about 2 to 20% by weight of at least one compound of a metal selected from the group consisting of Co, Ni, Fe, Mn, Cr and V.
Claim 24
Dependent Claim
32 words
The metallizing composition for use in a nitride ceramic according to claim 18, wherein the metallizing composition further comprises from about 2 to 15% by weight of a nickel or calcium compound.
Claim 25
Dependent Claim
21 words
The metallizing composition for use in a nitride ceramic according to claim 18, wherein said group IVb active metal comprises titanium.
Claim 26
Dependent Claim
21 words
The metallizing composition for use in a nitride ceramic according to claim 18, wherein said compound comprises a compound of cobalt.
Claim 27
Independent Claim
121 words
A method for preparing a ceramic substrate comprising: providing a substrate comprising a nitride ceramic sintered sheet; coating on said ceramic substrates a metallizing paste comprising molybdenum, tungsten or a mixture thereof as a main component, at least one of titanium, zirconium and hafnium as an activation metal and at least one of yttria and alumina; and firing the coated substrate in an inert atmosphere at a temperature of from 1600° to 1900° C. to prepare a ceramic substrate comprising a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and a metallized layer formed from said metallizing paste, wherein said compound comprising yttria and alumina also uniformly penetrates said metallized layer.
Claim 28
Independent Claim
121 words
A method for preparing a ceramic substrate comprising: providing a substrate comprising a nitride ceramic sintered sheet; coating on said ceramic substrates a metallizing paste comprising molybdenum, tungsten or a mixture thereof as a main component, at least one of titanium, zirconium and hafnium as an activation metal and at least one of yttria and alumina; and firing the coated substrate in an inert atmosphere at a temperature of from 1600° to 1900° C. to prepare a ceramic substrate comprising a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and a metallized layer formed from said metallizing paste, wherein said compound comprising yttria and alumina also uniformly penetrates said metallized layer.
Claim 29
Independent Claim
126 words
A method for preparing a ceramic substrate comprising: coating a paste comprising a compound of yttria and alumina on a substrate comprising a nitride ceramic sintered sheet; coating on the yttria and alumina compound coating a metallizing paste comprising molybdenum, tungsten or a mixture thereof as a main component and at least one of titanium, zirconium and hafnium as an activation metal; and firing the coated substrate in an inert atmosphere at a temperature of from 1600° to 1900° C. to prepare a ceramic substrate comprising a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and a metallized layer formed from said metallized paste, wherein said yttria and alumina compound also uniformly penetrates said metallized layer.
Claim 30
Independent Claim
126 words
A method for preparing a ceramic substrate comprising: coating a paste comprising a compound of yttria and alumina on a substrate comprising a nitride ceramic sintered sheet; coating on the yttria and alumina compound coating a metallizing paste comprising molybdenum, tungsten or a mixture thereof as a main component and at least one of titanium, zirconium and hafnium as an activation metal; and firing the coated substrate in an inert atmosphere at a temperature of from 1600° to 1900° C. to prepare a ceramic substrate comprising a uniform layer of a compound comprising yttria and alumina at the interface between said nitride ceramic sintered sheet and a metallized layer formed from said metallized paste, wherein said yttria and alumina compound also uniformly penetrates said metallized layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-04 | 1995-05-06 | 1995-11-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-04 | 1999-05-06 | 1999-11-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-04 | 2003-05-06 | 2003-11-05 | $7700.00 | Window Closed / Lapsed |