Epoxy resin based powder coating composition with mixed filler including microfine silica
Assignee: Somar Corp
•
Filing: 1989-11-16
•
Granted: 1991-09-17
•
Expires: 2009-11-16
Abstract
Abstract An epoxy resin based powder coating composition which comprises: (A) 100 parts by weight of a mixed epoxy resin having a softening point of 60 DEG -80 DEG C. which consists of 50 to 70 wt. % of a bisphenol A expoxy resin having a number-average molecular weight of 800 to 1,800 and 30 to 50 wt. % of a cresol novolak epoxy resin; (B) 5 to 80 parts by weight of a novolak resin; (C) 0.5 to 5 parts by weight of triphenylphosphine; (D) 60 to 200 parts by weight of an inorganic powder having an average particle size of 0.5 to 75 um; and (E) 0.01 to 2 parts by weight of a microfine silica powder having an average particle size of 1 to 100 nm. The epoxy resin based powder coating composition can be coated on electrical and electronic components at 90 DEG -100 DEG C. with retaining the high moisture resistance, storage stability and free-flowing properties.
Inventors
- 👤 Yoshihisa Fujimoto
- 👤 Yoshihiro Motoki
- 👤 Kazufumi Ueji
- 👤 Kunio Imai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 01:07
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/03; H; H10; H10W; H10W74/00; H10W74/40; H10W74/47; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/32; C08G59/38; C09D163/00; Y; Y10; Y10S; Y10S525/00; Y10S525/934
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
132 words
An epoxy resin based powder coating composition which comprises: (A) 100 parts by weight of a mixed epoxy resin having a softening point of 60°-80° C. which consists of 50 to 70 wt % of a bisphenol A epoxy resin having a number-average molecular weight of 800 to 1,800 and 30 to 50 wt % of a cresol novolak epoxy resin; (B) 5 to 80 parts by weight of a novolak resin having a softening point of 70°-120° C.; (C) 0.5 to 5 parts by weight of triphenylphosphine; (D) 60 to 200 parts by weight of an inorganic powder having an average particle size of 0.5 to 75 μm; and (E) 0.01 to 2 parts by weight of a microfine silica powder having an average particle size of 1 to 100 nm.
Claim 2
Dependent Claim
132 words
An epoxy resin based powder coating composition which comprises: (A) 100 parts by weight of a mixed epoxy resin having a softening point of 60°-80° C. which consists of 50 to 70 wt % of a bisphenol A epoxy resin having a number-average molecular weight of 800 to 1,800 and 30 to 50 wt % of a cresol novolak epoxy resin; (B) 5 to 80 parts by weight of a novolak resin having a softening point of 70°-120° C.; (C) 0.5 to 5 parts by weight of triphenylphosphine; (D) 60 to 200 parts by weight of an inorganic powder having an average particle size of 0.5 to 75 μm; and (E) 0.01 to 2 parts by weight of a microfine silica powder having an average particle size of 1 to 100 nm.
Claim 3
Dependent Claim
40 words
An epoxy resin based powder coating composition as in claim 1, wherein said coating composition further comprises a silane coupling agent in an amount of 0.1 to 6 parts by weight per 100 parts by weight of said epoxy resin.
Claim 4
Dependent Claim
28 words
An epoxy resin based powder coating composition as in claim 1, wherein said novolak resin is produced by synthesizing at least one of phenol and alkylphenol and formaldehyde.
Claim 5
Dependent Claim
21 words
An epoxy resin based powder coating composition as in claim 3, wherein the alkylphenol is selected from cresol and tert-butyl phenol.
Claim 6
Dependent Claim
20 words
An epoxy resin based powder coating composition as in claim 1, wherein said novolak resin is a phenol novolak resin.
Claim 7
Dependent Claim
26 words
An epoxy resin based powder coating composition as in claim 1, wherein said bisphenol A epoxy resin has a number-average molecular weight of 950 to 1,100.
Claim 8
Dependent Claim
34 words
An epoxy resin based powder coating composition as in claim 1, wherein the content of said novolak resin is 10 to 50 parts by weight per 100 parts by weight of said epoxy resin.
Claim 9
Dependent Claim
33 words
An epoxy resin based powder coating composition as in claim 1, wherein the content of said triphenylphosphine is 1.0 to 3.0 parts by weight per 100 parts by weight of said epoxy resin.
Claim 10
Dependent Claim
36 words
An epoxy resin based powder coating composition as in claim 1, wherein said inorganic powder is selected from the group consisting of silica, calcium carbonate, dolomite, calcium silicate, alumina, clay, mica, talc and glass fiber powder.
Claim 11
Dependent Claim
18 words
An epoxy resin based powder coating composition as in claim 9, wherein said inorganic powder is silica powder.
Claim 12
Dependent Claim
21 words
An epoxy resin powder coating composition as in claim 1, wherein said novolak resin has a softening point of 70°-100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-16 | 1995-03-18 | 1995-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-16 | 1999-03-18 | 1999-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-16 | 2003-03-18 | 2003-09-17 | $7700.00 | Window Closed / Lapsed |