US5045512A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Mixed sintered metal materials based on borides, nitrides and iron binder metals
Assignee: Elektroschmelzwerk Kempten GmbH
•
Filing: 1990-11-02
•
Granted: 1991-09-03
•
Expires: 2010-11-02
Abstract
Abstract The invention relates to mixed sintered metal materials based on high-melting borides and nitrides and low-melting iron binder metals having the composition: (1) 40-97% by volume of borides, such as titanium diboride and zirconium diboride; (2) 1-48% by volume of nitrides, such as titanium nitride and zirconium nitride; (3) 0-10% by volume of oxides, such as titanium oxide and zirconium oxide, with the proviso that components (2) and (3) may also be present as oxynitrides such as titanium and zirconium oxynitride; and (4) 2-59% by volume of low-carbon binder metals, such as iron and iron alloys and to processes for preparing the same.
Inventors
- 👤 Dietrich Lange
- 👤 Lorenz Sigl
- 👤 Karl-Alexander Schwetz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:31
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0292; C22C29/00; C22C29/14
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
199 words
Mixed sintered metal materials comprising: (1) 40 to 97% by volume of borides selected from the group consisting of titanium diboride, zirconium diboride and solid solutions thereof; (2) 1 to 48% by volume of nitrides selected from the group consisting of titanium nitride and zirconium nitride; (3) 0 to 10% by volume of oxides selected from the group consisting of titanium oxide and zirconium oxide, wherein components (2) and (3) may be present, completely or partially, in the form of oxynitrides, selected from the group consisting of titanium oxynitrides and zirconium oxynitrides; and (4) 2 to 59% by volume of a binder metal selected from low-carbon iron, low-carbon iron alloys and mixtures thereof, said sintered metal material having the following properties; (a) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material, (b) a grain size of the sintered material phase of at most 5.5 μm, (c) a hardness (HV 30) of at least 1,200, (d) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa, and (e) a fracture resistance K IC of at least 8.0 MPa m 1/2 .
Claim 2
Dependent Claim
199 words
Mixed sintered metal materials comprising: (1) 40 to 97% by volume of borides selected from the group consisting of titanium diboride, zirconium diboride and solid solutions thereof; (2) 1 to 48% by volume of nitrides selected from the group consisting of titanium nitride and zirconium nitride; (3) 0 to 10% by volume of oxides selected from the group consisting of titanium oxide and zirconium oxide, wherein components (2) and (3) may be present, completely or partially, in the form of oxynitrides, selected from the group consisting of titanium oxynitrides and zirconium oxynitrides; and (4) 2 to 59% by volume of a binder metal selected from low-carbon iron, low-carbon iron alloys and mixtures thereof, said sintered metal material having the following properties; (a) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material, (b) a grain size of the sintered material phase of at most 5.5 μm, (c) a hardness (HV 30) of at least 1,200, (d) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa, and (e) a fracture resistance K IC of at least 8.0 MPa m 1/2 .
Claim 3
Dependent Claim
35 words
The sintered materials of claim 1, wherein the sintering material components (1) and (2) are titanium diboride and titanium nitride in a combined amount of 50 to 97% by volume of the total mixed material.
Claim 4
Dependent Claim
22 words
The sintered material of claim 2, wherein the combined amount of titanium diboride and titanium nitride is 50 to 90% by volume.
Claim 5
Dependent Claim
21 words
The sintered material of claim 3, wherein the combined amount of titanium diboride and titanium nitride is about 80% by volume.
Claim 6
Dependent Claim
20 words
The sintered material of claim 1, wherein titanium nitride is present in an amount of 2.5 to 40% by volume.
Claim 7
Dependent Claim
20 words
The sintered material of claim 5, wherein the oxides are present in an amount of 0.1 to 10% by volume.
Claim 8
Dependent Claim
18 words
The sintered material of claim 1, wherein the binder metal has less than 0.1% by weight of carbon.
Claim 9
Dependent Claim
24 words
The sintered material of claim 1, wherein the binder metal is a low-carbon iron alloy containing chromium or a mixture of nickel and chromium.
Claim 10
Dependent Claim
21 words
The sintered material of claim 8, wherein the low-carbon iron alloy contains chromium in an amount of about 12% by weight.
Claim 11
Dependent Claim
35 words
The sintered material of claim 8, wherein the low-carbon iron alloy contains a mixture of nickel and chromium in an amount of about 8% by weight of nickel and about 18% by weight of chromium.
Claim 12
Dependent Claim
169 words
Mixed sintered metal materials comprising: (a) 2.5 to 40% by volume of titanium nitride; (b) an amount of titanium diboride sufficient to provide a combined volume of titanium nitride and titanium diboride of from 50 to 90% of the total mixed sintered material; (c) 0 to 10% by volume of oxides selected from the group consisting of titanium oxide and zirconium oxide; and (d) 2 to 59% by volume of a binder metal selected from low-carbon iron, low-carbon iron alloys and mixtures thereof, said sintered metal material having the following properties; (1) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material, (2) a grain size of the sintered material phase of at most 5.5 μm, (3) a hardness (HV 30) of at least 1,200, (4) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa, and (5) a fracture resistance K IC of at least 8.0 MPa m 1/2 .
Claim 13
Dependent Claim
169 words
Mixed sintered metal materials comprising: (a) 2.5 to 40% by volume of titanium nitride; (b) an amount of titanium diboride sufficient to provide a combined volume of titanium nitride and titanium diboride of from 50 to 90% of the total mixed sintered material; (c) 0 to 10% by volume of oxides selected from the group consisting of titanium oxide and zirconium oxide; and (d) 2 to 59% by volume of a binder metal selected from low-carbon iron, low-carbon iron alloys and mixtures thereof, said sintered metal material having the following properties; (1) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material, (2) a grain size of the sintered material phase of at most 5.5 μm, (3) a hardness (HV 30) of at least 1,200, (4) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa, and (5) a fracture resistance K IC of at least 8.0 MPa m 1/2 .
Claim 14
Dependent Claim
19 words
The sintered material of claim 11, wherein the combined volume of titanium nitride and titanium diboride is about 80%.
Claim 15
Dependent Claim
141 words
A process for producing a mixed sintered material having the following composition: (a) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material; (b) a grain size of the sintered material phase of at least 5.5 μm; (c) a hardness (HV 30) of at least 1,200; (d) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa; and (e) a fracture resistance K IC of at least 8.0 MPa m 1/2 . said process comprising autogenously grinding said composition into a powdered mixture, cold-pressing and shaping the powdered mixture to obtain a green compact and sintering the green compact without pressure in a carbon-free atmosphere in the absence of oxygen at a temperature in the range of from 1350° C. to 1900° C.
Claim 16
Dependent Claim
141 words
A process for producing a mixed sintered material having the following composition: (a) a density of at least 97% of the theoretical density, relative to the theoretically possible density of the total mixed material; (b) a grain size of the sintered material phase of at least 5.5 μm; (c) a hardness (HV 30) of at least 1,200; (d) a bending fracture strength measured by the 4-point method at room temperature of at least 1,000 MPa; and (e) a fracture resistance K IC of at least 8.0 MPa m 1/2 . said process comprising autogenously grinding said composition into a powdered mixture, cold-pressing and shaping the powdered mixture to obtain a green compact and sintering the green compact without pressure in a carbon-free atmosphere in the absence of oxygen at a temperature in the range of from 1350° C. to 1900° C.
Claim 17
Dependent Claim
39 words
The process of claim 13 comprising hot-isostatically recompacting the sintered green compact by means of a gaseous pressure transmission medium at a temperature of from 1200° C. to 1400° C. under a pressure of from 150 to 250 MPa.
Claim 18
Dependent Claim
86 words
The process of claim 13 comprising autogenously grinding a mixture of borides and nitrides and optionally oxides of titanium and zirconium, to obtain a fine powdered mixture, cold-pressing and shaping the fine powdered mixture to obtain a green compact, heating the green compact under a powder fill of the binder metal component in a carbon-free atmosphere to a temperature above the melting point of the metallic binder phase until the resulting molten binder metal penetrates into the porous green compact and completely seals the pores thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-02 | 1995-03-04 | 1995-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-02 | 1999-03-04 | 1999-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-02 | 2003-03-04 | 2003-09-03 | $7700.00 | Window Closed / Lapsed |