Method of producing electrical heating elements and electrical heating elements so produced
Assignee: Deeman Product Development Ltd
•
Filing: 1990-01-10
•
Granted: 1991-08-13
•
Expires: 2010-01-10
Abstract
Abstract A method of forming an electrical heating element in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, in the range 20-150 microns, roughening the surface of a supporting body onto which a heating element is to be formed, pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C. and flame spraying the dry metal powder onto said heated surface of the supporting body in a plurality of passes over the supporting body. The effective resistivity of the flame sprayed deposit is predetermined by adjusting the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body. The amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, can be varied by selecting the size range of the particles used, within said range of 20-150 microns. Alternatively the amount of oxidation on the surfaces of the flame sprayed particles can be varied by blending selected alloys into the powder to be sprayed such as to adjust the quantity of conductive oxides present on the sprayed particles.
Inventors
- 👤 Jeffery Boardman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:04
CPC Classifications
H; H05; H05B; H05B3/00; H05B3/10; H05B3/12; C; C23; C23C; C23C4/00; C23C4/02; C23C4/12; C23C4/129; F; F23; F23Q; F23Q7/00; H05B3/20; H05B3/22; H05B3/26; H05B2203/00; H05B2203/013; H05B2203/017; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49083
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
165 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body.
Claim 2
Independent Claim
165 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body.
Claim 3
Dependent Claim
44 words
A method according to claim 1, wherein the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, is varied by selecting the size range of the particles used, within said range of 20-150 microns.
Claim 4
Independent Claim
212 words
A method of forming an electrical heating element of desired electrical resistance for use in a toaster element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 60-110 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 60-110 microns.
Claim 5
Independent Claim
212 words
A method of forming an electrical heating element of desired electrical resistance for use in a toaster element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 60-110 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 60-110 microns.
Claim 6
Independent Claim
214 words
A method of forming an electrical heating element of desired electrical resistance for use as a trouser press element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 45-90 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 45-90 microns.
Claim 7
Independent Claim
214 words
A method of forming an electrical heating element of desired electrical resistance for use as a trouser press element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 45-90 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 45-90 microns.
Claim 8
Independent Claim
213 words
A method of forming an electrical heating element of desired electrical resistance for use as a convector element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 45-90 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 45-90 microns.
Claim 9
Independent Claim
213 words
A method of forming an electrical heating element of desired electrical resistance for use as a convector element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 45-90 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 45-90 microns.
Claim 10
Independent Claim
213 words
A method of forming an electrical heating element of desired electrical resistance for use as a convector element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 40-100 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 40-100 microns.
Claim 11
Independent Claim
213 words
A method of forming an electrical heating element of desired electrical resistance for use as a convector element and the like in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 40-100 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by selecting the size range of the particles used, within said range of 40-100 microns.
Claim 12
Independent Claim
214 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by blending the selected alloys into the powder to be sprayed, such as to adjust the quantity of conductive oxides present on the sprayed particles.
Claim 13
Independent Claim
214 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, the effective resistance of the flame sprayed deposit being determined by controlling the amount of oxidation on the surfaces of the metallic particles sprayed onto the supporting body and the amount of oxidation on the surfaces of the flame sprayed particles, and hence the resistivity of the sprayed deposit, being varied by blending the selected alloys into the powder to be sprayed, such as to adjust the quantity of conductive oxides present on the sprayed particles.
Claim 14
Dependent Claim
30 words
A method according to claim 7, wherein the powder sprayed consists of a nickel chromium alloy to which one or more further alloys are added for purposes of oxides adjustment.
Claim 15
Dependent Claim
27 words
A method according to claim 8, wherein the powder sprayed consists of a nickel chromium alloy to which is added NiCoFe alloy for purposes of oxides adjustment.
Claim 16
Dependent Claim
32 words
A method according to claim 8, wherein the powder sprayed consists of a nickel chromium alloy to which NiCoFe, Al 2 O 3 and Ni are added for purposes of oxides adjustment.
Claim 17
Dependent Claim
18 words
A method according to claim 8, wherein the powder sprayed consists of a mixture of NiCoFe and FeCrAl.
Claim 18
Independent Claim
165 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, said flame spraying being carried out in an oxygen/acetylene flame spraying gun, the ratio of oxygen pressure to acetylene pressure being within the range 1.18:1 and 1.45:1.
Claim 19
Independent Claim
165 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the water atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; and (4) flame spraying the dry metal powder onto said heated surface of the supporting body in an oxidising atmosphere and in a plurality of passes over the supporting body, said flame spraying being carried out in an oxygen/acetylene flame spraying gun, the ratio of oxygen pressure to acetylene pressure being within the range 1.18:1 and 1.45:1.
Claim 20
Dependent Claim
32 words
A method according to claim 12, wherein the flame spraying gun is moved in a series of passes over the supporting body at a speed in the range 15 to 80 cms/sec.
Claim 21
Dependent Claim
29 words
A method according to claim 1, wherein successive layers of flame sprayed NiCr or FeCrAl powders are interspersed on the supporting body with flame sprayed layers of NiCoFe powder.
Claim 22
Dependent Claim
15 words
A heating element when formed by the method of any of claims 1 to 14.
Claim 23
Dependent Claim
151 words
A vehicle cigar/cigarette lighter comprising a heating element formed in accordance with the method of claim 1, the heating element being resiliently pivotable about its one end so that when it is angularly displaced by the engagement therewith of a cigar/cigarette to be lighted its other end engages a fixed contact to complete an electrical circuit supplying electric power to the heating element, and wherein an electrically insulating body carries a pair of metallic clips whose one ends are extended to form respective contact terminations by which the lighter can be plugged into a suitable electric socket, the heating element being in the form of a disc having a respective further metal clip fitted around diametrically opposite ends to provide electrical contacts to the resistive material, and a resilient flexible electrically conductive strip interconnecting one of the clips on the heating element with one of the clips on the insulating body.
Claim 24
Independent Claim
178 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, lying within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the resulting water-atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; (4) flame spraying the dry metal powder onto said heating surface of the supporting body in a plurality of passes over the supporting body, the flame spraying step being carried out in an oxidising atmosphere so that metal oxides are deposited on the supporting body, the effective resistance of the flame sprayed deposit being determined in dependence upon the level of oxidation of the metal particles of the powder.
Claim 25
Independent Claim
178 words
A method of forming an electrical heating element of desired electrical resistance in the form of an electrically non-conductive supporting body onto which an electrically resistive material is deposited, the method comprising the steps of: (1) preparing a dry metal powder of irregularly shaped metal particles of widely varying sizes, lying within the range 20-150 microns, by blasting a molten mixture of the metal into water and subsequently crushing and drying the resulting water-atomised powder; (2) roughening the surface of a supporting body onto which a heating element is to be formed; (3) pre-heating said surface of the supporting body to a temperature within the range of 150°-250° C.; (4) flame spraying the dry metal powder onto said heating surface of the supporting body in a plurality of passes over the supporting body, the flame spraying step being carried out in an oxidising atmosphere so that metal oxides are deposited on the supporting body, the effective resistance of the flame sprayed deposit being determined in dependence upon the level of oxidation of the metal particles of the powder.
References Cited (Backward Citations)
US1932193A
Cited
US3811934A
Cited
US3737624A
Cited
US3872419A
Cited
US4348434A
Cited
US4348433A
Cited
US4513020A
Cited
US4587402A
Cited
GB2134008A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-12 | 1995-02-11 | 1995-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-12 | 1999-02-11 | 1999-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-12 | 2003-02-11 | 2003-08-13 | $7700.00 | Window Closed / Lapsed |