Process for preparation of alkaline earth metal aluminosilicate sintered body
Assignee: Tokuyama Corp
•
Filing: 1989-12-29
•
Granted: 1991-07-30
•
Expires: 2009-12-29
Abstract
Abstract An alkaline earth metal aluminosilicate sintered body is obtained by molding a starting mixture of a zeolite having an alkaline earth metal form and an SiO2/Al2O3 molar ratio not higher than 3.0 and a boron compound such as boron oxide, and firing the molded body at a temperature lower than 1,000 DEG C. An amorphous calcination product formed by calcining the zeolite may also be used in the starting mixture with the boron compound. This process allows the range of firing temperatures suitable for formation of a sintered body to be varied over a range of from about 50 DEG to 150 DEG C. or more while also allowing lower firing temperatures than in the absence of the boron compound to be used while still obtaining the desired densified sintered body.
Inventors
- 👤 Genji Taga
- 👤 Masaki Noritake
- 👤 Masahiro Nakamura
- 👤 Hua-Min Zhang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:25
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/42; C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/195
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
90 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body, which comprises molding a starting mixture comprising (i) a zeolite of an alkaline earth metal form having an SiO 2 /Al 2 O 3 molar ratio not higher than 3.0 or an amorphous calcination product formed by calcining said zeolite and (ii) a boron compound selected from the group consisting of boron oxide and boron compounds capable of being converted to boron oxide by firing, and firing the molded body at a temperature lower than 1000° C.
Claim 2
Dependent Claim
90 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body, which comprises molding a starting mixture comprising (i) a zeolite of an alkaline earth metal form having an SiO 2 /Al 2 O 3 molar ratio not higher than 3.0 or an amorphous calcination product formed by calcining said zeolite and (ii) a boron compound selected from the group consisting of boron oxide and boron compounds capable of being converted to boron oxide by firing, and firing the molded body at a temperature lower than 1000° C.
Claim 3
Dependent Claim
94 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1, wherein the zeolite of an alkaline earth metal form is a zeolite represented by the following general formula [I]: (iM.sup.1 O.jM.sub.2.sup.2 O).lAl.sub.2 O.sub.3.mSiO.sub.2.nH.sub.2 O[I] wherein M 1 represents an alkaline earth metal ion, M 2 represents an alkali metal ion or an ammonium ion, i, j, l and m are numbers satisfying the requirements of i+j=1, j=0 to 0.15, l=0.9 to 1.1, m=1.5 to 3.0 and m/l=1.5 to 3, and n is 0 or a positive number.
Claim 4
Dependent Claim
87 words
A process for the preparation of an alkaline earth metal aluminosilicate according to claim 1, wherein the zeolite of an alkaline earth metal form is a zeolite represented by the following general formula [II]: (kCaO.pMgO.qM.sub.2.sup.2 O).lAl.sub.2 O.sub.3.mSiO.sub.2.nH.sub.2 O[II] wherein M 2 represents an alkali metal ion or an ammonium ion, k, p, q, l and m are numbers satisfying the requirements of k+p+q=1, p/k=0.05 to 1, q=0 to 0.15, l=0.9 to 1.1, m=1.5 to 3.0 and m/l=1.5 to 3.0, and n is 0 or a positive number.
Claim 5
Dependent Claim
61 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1, wherein the starting mixture is an amorphous calcination product having an SiO 2 /Al 2 O 3 molar ratio not higher than 3, which is obtained by mixing the boron compound to the zeolite of an alkaline earth metal form and calcining the mixture.
Claim 6
Dependent Claim
38 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1, wherein the boron compound is mixed in an amount of 0.1 to 20% by weight as B 2 O 3 .
Claim 7
Dependent Claim
31 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1, wherein the boron compound is boron oxide, boric acid, boron nitride or boron carbide.
Claim 8
Dependent Claim
52 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1, wherein the boron compound is dissolved in a solvent and is mixed in the liquid state with the zeolite of an alkaline earth metal form or the amorphous calcination product obtained by calcining said zeolite.
Claim 9
Dependent Claim
22 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 7, wherein the solvent is water.
Claim 10
Dependent Claim
34 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1 wherein the firing is carried out at a temperature of from about 850° to about 950° C.
Claim 11
Dependent Claim
19 words
The process according to claim 9 wherein the firing is conducted for from about 1 to about 10 hours.
Claim 12
Dependent Claim
45 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1 wherein the starting mixture comprises the boron compound and a zeolite of calcium form or an amorphous calcination product thereof and the resulting sintered body is an anorthite.
Claim 13
Dependent Claim
46 words
A process for the preparation of an alkaline earth metal aluminosilicate sintered body according to claim 1 wherein the starting mixture comprises the boron compound and a zeolite of magnesium form or an amorphous calcination product thereof, and wherein the resulting sintered body is a cordierite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-29 | 1995-01-28 | 1995-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-29 | 1999-01-28 | 1999-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-29 | 2003-01-28 | 2003-07-30 | $7700.00 | Window Closed / Lapsed |