Method for thermoforming and bonding a paint-coated polymeric film to a substrate
Assignee: Avery Dennison Corp
•
Filing: 1989-09-05
•
Granted: 1991-07-23
•
Expires: 2009-09-05
Abstract
Abstract Paint-coated polymeric films which are bonded to substrates such as automobile panels, as a substitute for spray painted finishes, often develop surface blemishes or defects from the coating or web handling operations. These can be reduced or eliminated by vacuum thermoforming the film to the desired substrate in a plural stage procedure. The periphery of the film is clamped in a frame. Then the film is preheated to a temperature above its glass transition temperature until the film becomes taut in the frame. It is allowed to cool and is then reheated to at least the glass transition temperature and is then vacuum thermoformed to the substrate. This procedure eliminates many if not all of the visible surface defects in the thermoformed film.
Inventors
- 👤 Jack Pata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:24
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/14; B29C51/26; B29C51/42; B29C51/421; B29L; B29L2031/00; B29L2031/722; Y; Y10; Y10S; Y10S264/00; Y10S264/65; Y10S264/71; Y10S264/909; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1028
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
152 words
A method for thermoforming and bonding a thermoformable paint-coated polymeric film, the coating being flawed, which has an adhesive side and a non-adhesive side to a substrate which comprises: clamping the periphery of the film having the flawed coating in a frame; preheating the clamped film to a temperature above its glass transitions temperature until it becomes taut within the frame and the coating flaw is reduced or eliminated; allowing the preheated clamped film to cool to a temperature below its glass transition temperature; reheating the cooled clamped film to at least its glass transition temperature; placing a substrate in an open thermoforming chamber in close proximity to the adhesive side of the reheated clamped film; hermetically sealing the opening of the chamber with the adhesive side of the reheated clamped film; lowering the pressure in the sealed chamber and thereby forcing the reheated clamped film into bonding contact with the substrate.
Claim 2
Independent Claim
152 words
A method for thermoforming and bonding a thermoformable paint-coated polymeric film, the coating being flawed, which has an adhesive side and a non-adhesive side to a substrate which comprises: clamping the periphery of the film having the flawed coating in a frame; preheating the clamped film to a temperature above its glass transitions temperature until it becomes taut within the frame and the coating flaw is reduced or eliminated; allowing the preheated clamped film to cool to a temperature below its glass transition temperature; reheating the cooled clamped film to at least its glass transition temperature; placing a substrate in an open thermoforming chamber in close proximity to the adhesive side of the reheated clamped film; hermetically sealing the opening of the chamber with the adhesive side of the reheated clamped film; lowering the pressure in the sealed chamber and thereby forcing the reheated clamped film into bonding contact with the substrate.
Claim 3
Dependent Claim
28 words
A method according to claim 1 wherein the paint-coated film comprises a thermoplastic carrier film having on its non-adhesive side a polyurethane paint layer and a polyurethane clearcoat.
Claim 4
Dependent Claim
14 words
A method according to claim 1 wherein the paint layer contains light reflective flakes.
Claim 5
Dependent Claim
21 words
A method according to claim 1 wherein the adhesive side of the film has coated thereon a layer of pressure-sensitive adhesive.
Claim 6
Dependent Claim
29 words
A method according to claim 1 wherein the paint-coated film comprises a carrier film formed from a blend of a copolyester and a thermoplastic rubber-modified vinyl aromatic polymer composition.
Claim 7
Dependent Claim
30 words
A method according to claim 1 wherein the preheating of the film to the point of tautness and coating flaw reduction or elimination occurs in intervals of successively higher temperatures.
References Cited (Backward Citations)
US3551232A
Cited
US3674626A
Cited
US4415523A
Cited
US4306856A
Cited
US4306856B1
Cited
US4364885A
Cited
JPS5770610A
Cited
DE3103584A1
Cited
US4471018A
Cited
US4818589A
Cited
US4828637A
Cited
US4838973A
Cited
US4769100A
Cited
EP0285071A2
Cited
US4824506A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-22 | 1995-01-21 | 1995-07-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-22 | 1999-01-21 | 1999-07-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-22 | 2003-01-21 | 2003-07-23 | $7700.00 | Window Closed / Lapsed |