Titanium diboride/boron carbide composites with high hardness and toughness
Assignee: Dow Chemical Co
•
Filing: 1990-01-22
•
Granted: 1991-07-16
•
Expires: 2010-01-22
Abstract
Abstract A powder composition consisting essentially of an intimate mixture of boron carbide and titanium diboride, the mixture having an average particle size of less than about 0.5 micron, the particles being uniformly dispersed such that elemental analytical techniques show all discrete concentrations of boron carbide and titanium diboride to be less than or equal to about 0.5 micron in diameter, is disclosed. The powder is useful for making a densified ceramic composition comprising titanium diboride grains, having an average grain size of less than or equal to about 3 microns in diameter, uniformly dispersed with boron carbide grains, having an average grain size of less than about 5 microns in diameter. The densified composition exhibits improved hardness and toughness when compared wiht titanium diboride or boron carbide compositions. The powder can be prepared by a process comprising subjecting a stream of reactant gases consisting essentially of a volatile boron source, a volatile titanium source, a volatile carbon source, and a hydrogen source to an amount of laser radiation and at a pressure effective to convert at least a portion of the volatile boron, carbon and titanium sources to an intimate mixture of boron carbide and titanium diboride.
Inventors
- 👤 Arne K. Knudsen
- 👤 William Rafaniello
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:32
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; B; B01; B01J; B01J19/00; B01J19/08; B01J19/12; B01J19/121; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/991; C01B35/00; C01B35/02; C01B35/04; C04B35/515; C04B35/56; C04B35/563; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; B01J2219/00; B01J2219/08; B01J2219/0894; C01P; C01P2002/00; C01P2002/70; C01P2002/72; C01P2004/00; C01P2004/01; C01P2004/02; C01P2004/03; C01P2004/04; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/10; C01P2006/90
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
109 words
A process which comprises subjecting reactant gases consisting essentially of a volatile boron source, a volatile titanium source, a volatile carbon source and a hydrogen source to an amount of laser radiation effective to convert at least a portion of the volatile boron, carbon and titanium sources to an intimate mixture of boron carbide and titanium diboride, said mixture being a uniformly dispersed ceramic powder such that electron probe analysis X-ray maps show substantially all discrete localized concentrations of boron carbide and titanium diboride to be less than or equal to about 3 microns in diameter, said powder being, as determined by bulk X-ray powder diffraction analysis, predominantly non-crystalline.
Claim 2
Dependent Claim
109 words
A process which comprises subjecting reactant gases consisting essentially of a volatile boron source, a volatile titanium source, a volatile carbon source and a hydrogen source to an amount of laser radiation effective to convert at least a portion of the volatile boron, carbon and titanium sources to an intimate mixture of boron carbide and titanium diboride, said mixture being a uniformly dispersed ceramic powder such that electron probe analysis X-ray maps show substantially all discrete localized concentrations of boron carbide and titanium diboride to be less than or equal to about 3 microns in diameter, said powder being, as determined by bulk X-ray powder diffraction analysis, predominantly non-crystalline.
Claim 3
Dependent Claim
31 words
The process according to claim 1 wherein the boron source comprises a member of the group consisting of an alkyl boron, an alkyl borate, a boron hydride and a boron halide.
Claim 4
Dependent Claim
23 words
The process according to claim 1 wherein the carbon source comprises a member of the group consisting of volatile hydrocarbons and volatile halocarbons.
Claim 5
Dependent Claim
23 words
The process according to claim 1 wherein the carbon source comprises a member of the group consisting of methane, ethylene and carbon tetrachloride.
Claim 6
Dependent Claim
12 words
The process according to claim 1 wherein the carbon source is methane.
Claim 7
Dependent Claim
33 words
The process according to claim 1 wherein the carbon source is present in an amount less than the stoichiometric amount calculated on the boron in the boron source destined for B 4 C.
Claim 8
Dependent Claim
46 words
The process according to claim 6 wherein the carbon source is present in the starting gas mixture in an amount ranging from about 20 percent to about 80 percent of the stoichiometric amount, calculated on the boron in the boron source destined for B 4 C.
Claim 9
Dependent Claim
46 words
The process according to claim 1 wherein the hydrogen source is present in an amount at least stoichiometric, calculated on the boron in the boron source destined for B 4 C and TiB 2 and the titanium in the titanium source destined for TiB 2 .
Claim 10
Dependent Claim
52 words
The process according to claim 8 wherein the hydrogen source is present in an amount ranging from about stoichiometric to about 10 times stoichiometric, calculated on the boron in the boron source destined for B 4 C and TiB 2 and the titanium in the titanium source destined for TiB 2 .
Claim 11
Dependent Claim
23 words
The process according to claim 1 wherein the titanium source comprises a member of the group consisting of titanium halides and titanium alkoxides.
Claim 12
Dependent Claim
13 words
The process according to claim 10 wherein the titanium halide is titanium tetrachloride.
Claim 13
Dependent Claim
26 words
The process according to claim 1 wherein the titanium source is present in an amount such that substantially all titanium is combined as TiB 2 .
Claim 14
Dependent Claim
38 words
The process according to claim 1 wherein the intimate mixture has a stoichiometry such that when the mixture is densified there is less than about 5 weight percent of phases other than TiB 2 and B 4 C.
Claim 15
Dependent Claim
20 words
The process of claim 1 wherein the reaction is conducted at an absolute pressure of at least about 300 Torr.
Claim 16
Dependent Claim
22 words
The process according to claim 1 wherein the reaction is conducted at an absolute pressure of about 300 to about 1,500 Torr.
Claim 17
Dependent Claim
22 words
The process according to claim 1 wherein the reaction is conducted at an absolute pressure of about 600 to about 760 Torr.
Claim 18
Dependent Claim
14 words
The process according to claim 1 wherein the reactant gases form a continuous stream.
Claim 19
Dependent Claim
20 words
The process according to claim 1 wherein the intimate mixture exhibits average particle diameters of less than about 3 microns.
Claim 20
Dependent Claim
17 words
The process according to claim 18 wherein the average particle diameter is less than about 0.5 micron.
Claim 21
Dependent Claim
19 words
The process according to claim 1 wherein the ceramic powder also includes a substantial amount of boron-rich boron carbide.
Claim 22
Dependent Claim
17 words
The process according to claim 1 wherein the laser radiation is supplied by a CO 2 laser.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-15 | 1995-01-14 | 1995-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-15 | 1999-01-14 | 1999-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-15 | 2003-01-14 | 2003-07-16 | $7700.00 | Window Closed / Lapsed |