Carpet tile and method of preparing same
Assignee: Heuga Holdings BV
•
Filing: 1989-09-28
•
Granted: 1991-07-09
•
Expires: 2009-09-28
Abstract
Abstract A carpet tile which comprises: a) a carpet material having an upper wear surface and a lower under surface; b) a primary backing which is bonded to the lower under surface (16) of the carpet material (12A) and which comprises at least one layer (18) of a solid, hot melt composition having an application temperature of over 140 DEG C; c) a secondary backing which is bonded to the underside of the primary backing (18, 26, 18) and which comprises: i) an intermediate layer (20) of a porous, non-woven, glass fiber tissue sheet material saturated with and bonded to hot melt composition from the lowermost layer thereof in the primary backing (18, 26, 18), and ii) a bottom layer (22) of non-woven, porous, temperature-sensitive, fibrous sheet material, which material tends to melt or distort at temperatures greater than 140 DEG C, the bottom layer being only partially saturated with hot melt composition and bonded thereby to said intermediate layer (20), and having a lower surface (24) which forms the exterior backing surface of the carpet tile (10) and is essentially free of hot melt composition. e
Inventors
- 👤 Johannes A. H. Claessen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:23
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B32B38/00; B32B38/08; B32B5/02; B32B5/022; D; D06; D06N; D06N7/00; D06N7/0063; D06N7/0071; D06N7/0078; D06N7/0081; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2262/10; B32B2262/101; B32B2471/00; B32B2471/02; D06N2201/00; D06N2201/02; D06N2201/0254; D06N2201/08; D06N2201/082; D06N2203/00; D06N2203/04; D06N2203/042; D06N2203/08; D06N2209/00; D06N2209/16; D06N2209/1628; D06N2213/00; D06N2213/06; D06N2213/063; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T428/00; Y10T428/23907; Y10T428/23979; Y10T428/23986; Y10T428/23993; Y10T428/31504; Y10T428/31815
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
233 words
A carpet tile which comprises: (a) a carpet material having an upper wear surface and a lower under surface; (b) a backing layer bonded to the lower under surface of the carpet material and which backing layer comprises a solid, hot melt composition having an application temperature of over about 140° C.; (c) a secondary backing layer bonded to the hot melt composition backing layer which comprises: (i) a layer of non-woven, porous, temperature-sensitive, fibrous sheet material which material tends to melt or distort at temperatures greater than about 140° C., the fibrous sheet material forming the exterior secondary backing surface of the carpet tile; (ii) an adjacent layer of a porous, non-woven, non-stretchable, heat resistant, glass fiber tissue sheet material, the tissue sheet material having sufficient fibrous body to protect the underlying temperature-sensitive sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and a porosity of 2.0 to 8.0 to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature, the glass fiber tissue sheet material saturated with and bonded to the hot melt composition backing layer, and the adjacent layer of the fibrous sheet material partially saturated with the hot melt composition and bonded thereto with the exterior backing surface of the fibrous sheet material essentially free of hot melt composition.
Claim 2
Dependent Claim
233 words
A carpet tile which comprises: (a) a carpet material having an upper wear surface and a lower under surface; (b) a backing layer bonded to the lower under surface of the carpet material and which backing layer comprises a solid, hot melt composition having an application temperature of over about 140° C.; (c) a secondary backing layer bonded to the hot melt composition backing layer which comprises: (i) a layer of non-woven, porous, temperature-sensitive, fibrous sheet material which material tends to melt or distort at temperatures greater than about 140° C., the fibrous sheet material forming the exterior secondary backing surface of the carpet tile; (ii) an adjacent layer of a porous, non-woven, non-stretchable, heat resistant, glass fiber tissue sheet material, the tissue sheet material having sufficient fibrous body to protect the underlying temperature-sensitive sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and a porosity of 2.0 to 8.0 to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature, the glass fiber tissue sheet material saturated with and bonded to the hot melt composition backing layer, and the adjacent layer of the fibrous sheet material partially saturated with the hot melt composition and bonded thereto with the exterior backing surface of the fibrous sheet material essentially free of hot melt composition.
Claim 3
Dependent Claim
22 words
The carpet tile of claim 1 wherein the fibrous sheet material has a weight of about 20 to 100 g/m 2 .
Claim 4
Dependent Claim
16 words
The carpet tile of claim 1 wherein the hot melt composition comprises bitumen or atactic polypropylene.
Claim 5
Dependent Claim
22 words
The carpet tile of claim 1 wherein the hot melt composition has an application temperature of about 145° C. to 180° C.
Claim 6
Dependent Claim
34 words
The carpet tile of claim 1 wherein the hot melt composition comprises a modified bitumen composition which comprises bitumen, limestone particulate filler material and a modifying amount of a thermoplastic block copolymer of styrene-butadiene-styrene.
Claim 7
Dependent Claim
31 words
The carpet tile of claim 1 wherein the glass fiber tissue sheet material comprises a non-woven, resin-bonded, glass fiber, porous tissue sheet material having a porosity of about 2.0 to 8.0.
Claim 8
Dependent Claim
33 words
The carpet tile of claim 1 wherein the non-woven, glass fiber tissue sheet material has a thickness of about 20 to 80 mils and a weight of 25 to 80 g/m 2 .
Claim 9
Dependent Claim
27 words
The carpet tile of claim 1 which includes generally intermediate and within the hot melt composition backing layer a stabilizing layer of a glass fiber sheet material.
Claim 10
Dependent Claim
18 words
The carpet tile of claim 1 wherein the fibrous sheet material comprises a spun-bonded polypropylene fibrous sheet material.
Claim 11
Dependent Claim
22 words
The carpet tile of claim 9 wherein the polypropylene, non-woven, fibrous sheet material has a thickness of about 15 to 65 mils.
Claim 12
Dependent Claim
30 words
The carpet tile of claim 1 wherein the hot melt composition partially saturates the fibrous sheet material in an amount of about 20% to 50% of the fibrous sheet material.
Claim 13
Dependent Claim
28 words
The carpet tile of claim 2 wherein the fibrous sheet material comprises a non-woven polyester sheet material having a weight of about 40 to 60 g/m 2 .
Claim 14
Dependent Claim
246 words
A carpet tile of improved dimensional stability, which carpet tile comprises: (a) a carpet material having an upper fibrous wear surface and a lower under surface; (b) a backing layer secured to the under surface of the carpet and comprising a solid, hot melt composition of bitumen, the composition having an application temperature of greater than about 140° C.; and (c) a secondary backing layer bonded to the back surface of the hot melt composition backing layer which comprises: (i) a layer of non-woven, porous, temperature-sensitive, fibrous sheet material as the exterior backing surface of the secondary backing layer, the fibrous sheet material having a melt temperature of about 140° C. to 150° C.; (ii) a layer of a porous, non-woven, non-stretchable glass fiber tissue sheet material having a porosity of about 3.5 to 4.5 and a weight of about 25 to 80 g/m 2 adjacent the layer of the non-woven, fibrous sheet material with a fibrous body sufficient to protect the temperature-sensitive, fibrous sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and sufficient porosity to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature; (iii) the hot composition saturating the glass fiber tissue sheet material and partially saturating the non-woven fibrous sheet material to a controlled thickness, the exterior backing surface of the fibrous sheet material essentially free of the hot melt composition.
Claim 15
Dependent Claim
246 words
A carpet tile of improved dimensional stability, which carpet tile comprises: (a) a carpet material having an upper fibrous wear surface and a lower under surface; (b) a backing layer secured to the under surface of the carpet and comprising a solid, hot melt composition of bitumen, the composition having an application temperature of greater than about 140° C.; and (c) a secondary backing layer bonded to the back surface of the hot melt composition backing layer which comprises: (i) a layer of non-woven, porous, temperature-sensitive, fibrous sheet material as the exterior backing surface of the secondary backing layer, the fibrous sheet material having a melt temperature of about 140° C. to 150° C.; (ii) a layer of a porous, non-woven, non-stretchable glass fiber tissue sheet material having a porosity of about 3.5 to 4.5 and a weight of about 25 to 80 g/m 2 adjacent the layer of the non-woven, fibrous sheet material with a fibrous body sufficient to protect the temperature-sensitive, fibrous sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and sufficient porosity to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature; (iii) the hot composition saturating the glass fiber tissue sheet material and partially saturating the non-woven fibrous sheet material to a controlled thickness, the exterior backing surface of the fibrous sheet material essentially free of the hot melt composition.
Claim 16
Independent Claim
287 words
A method of preparing a carpet tile from a carpet material having an upper wear surface and a lower under surface, which method comprises: (a) placing a layer of porous, non-stretchable, heat resistant, glass fiber tissue sheet material directly adjacent and on a layer of flexible, porous, non-woven, temperature-sensitive, fibrous sheet material to form a carrier sheet for the tissue sheet material, which fibrous sheet material tends to melt or distort at temperatures greater than about 140° C., the tissue sheet material having sufficient fibrous body to protect the underlying, temperature-sensitive sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and a porosity of 2.0 to 8.0 to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature; (b) applying to the surface of the glass fiber tissue sheet material a first backing layer of a viscous liquid, hot melt composition, the hot melt composition having an application temperature of over about 140° C.; (c) forcing the viscous liquid, hot melt composition of the backing layer by a driven roll-over-roll applicator to penetrate the porous glass fiber tissue sheet material and partially to penetrate the fibrous sheet material, but not through to the exterior backing surface of the fibrous sheet material; (d) contacting the hot melt composition of the first backing layer with the under surface of the carpet material; (e) cooling the hot melt composition in contact with the under surface of the carpet material to form a solid hot melt composition backing layer bonded to the under surface of the carpet material; and (f) optionally cutting the cooled backing layer carpet material into carpet tiles.
Claim 17
Independent Claim
287 words
A method of preparing a carpet tile from a carpet material having an upper wear surface and a lower under surface, which method comprises: (a) placing a layer of porous, non-stretchable, heat resistant, glass fiber tissue sheet material directly adjacent and on a layer of flexible, porous, non-woven, temperature-sensitive, fibrous sheet material to form a carrier sheet for the tissue sheet material, which fibrous sheet material tends to melt or distort at temperatures greater than about 140° C., the tissue sheet material having sufficient fibrous body to protect the underlying, temperature-sensitive sheet material from the hot melt composition on application and to prevent shrinkage of the fibrous sheet material and a porosity of 2.0 to 8.0 to permit the hot melt composition on application to be forced through the tissue sheet material at the hot melt application temperature; (b) applying to the surface of the glass fiber tissue sheet material a first backing layer of a viscous liquid, hot melt composition, the hot melt composition having an application temperature of over about 140° C.; (c) forcing the viscous liquid, hot melt composition of the backing layer by a driven roll-over-roll applicator to penetrate the porous glass fiber tissue sheet material and partially to penetrate the fibrous sheet material, but not through to the exterior backing surface of the fibrous sheet material; (d) contacting the hot melt composition of the first backing layer with the under surface of the carpet material; (e) cooling the hot melt composition in contact with the under surface of the carpet material to form a solid hot melt composition backing layer bonded to the under surface of the carpet material; and (f) optionally cutting the cooled backing layer carpet material into carpet tiles.
Claim 18
Dependent Claim
22 words
The method of claim 14 wherein the viscous, hot melt composition has an application temperature of about 140° C. to 180° C.
Claim 19
Dependent Claim
44 words
The method of claim 14 which includes applying a second backing layer of hot melt composition over the first backing layer and applying a glass fiber sheet material to the surface of the first backing layer and prior to applying the second backing layer.
Claim 20
Dependent Claim
32 words
The method of claim 14 which includes precoating the under surface of the carpet material prior to contacting the under surface of the carpet material with the first or second backing layers.
Claim 21
Dependent Claim
27 words
The method of claim 14 wherein the hot melt composition comprises bitumen, limestone particulate filler material and a modifying amount of a thermoplastic block copolymer of styrene-butadiene-styrene.
Claim 22
Dependent Claim
29 words
The method of claim 14 wherein the glass fiber tissue sheet material comprises a resin-bonded tissue sheet material having a weight of about 25 to 80 g/m 2 .
Claim 23
Dependent Claim
30 words
The method of claim 14 wherein the fibrous sheet material comprises a lightweight polyester or polypropylene sheet material having a weight of from about 30 to 60 g/m 2 .
Claim 24
Dependent Claim
26 words
The method of claim 14 wherein the fibrous sheet material comprises a spun-bonded polypropylene sheet material having weight of about 20 to 100 g/m 2 .
Claim 25
Dependent Claim
45 words
The method of claim 21 wherein the fibrous sheet material comprises a polypropylene sheet material and has a melt temperature of about 140° C. to 150° C. and which includes applying the hot melt composition at a temperature of about 145° C. to 160° C.
Claim 26
Dependent Claim
28 words
The method of claim 14 wherein the glass fiber tissue sheet material has a porosity of 2.0 to 8.0, and a thickness of about 20 to 80 mils.
Claim 27
Dependent Claim
19 words
The method of claim 14 wherein the fibrous sheet material has a thickness of about 15 to 65 mils.
Claim 28
Dependent Claim
36 words
The method of claim 14 wherein the viscous liquid hot melt composition has a viscosity of about 60,000 to 100,000 cps, and the glass fiber tissue sheet material has a porosity of about 2.0 to 8.0.
Claim 29
Dependent Claim
36 words
The method of claim 14 which includes a driven roll-over-roll applicator wherein the upper roll has a smaller diameter than the lower roll, and which lower roll is in contact with the temperature-sensitive fibrous sheet material.
Claim 30
Dependent Claim
43 words
The method of claim 14 which includes retaining the fibers of the temperature-sensitive fibrous sheet material in a substantially non-shrink position when the fibers become soft on the application of the hot melt composition by the contacting adjacent glass fiber tissue sheet material.
Claim 31
Dependent Claim
10 words
The carpet tile produced by the method of claim 21.
Claim 32
Dependent Claim
10 words
The carpet tile produced by the method of claim 14.
References Cited (Backward Citations)
US3847647A
Cited
US4582554A
Cited
US4737221A
Cited
US4576665A
Cited
US4678694A
Cited
US4702950A
Cited
US4824709A
Cited
US4913952A
Cited
US4915999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-08 | 1995-01-07 | 1995-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-08 | 1999-01-07 | 1999-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-08 | 2003-01-07 | 2003-07-09 | $7700.00 | Window Closed / Lapsed |