Dielectric ceramic with high K, low DF and flat TC
Assignee: Tam Ceramics LLC
•
Filing: 1989-07-20
•
Granted: 1991-07-02
•
Expires: 2009-07-20
Abstract
Abstract The present invention provides ceramic compositions for preparing multi-layer capacitors, having high dielectric constants between about 4900 and 5400, dissipation factors below about 2.0%, high insulation resistance capacitance products and stable temperature coefficient characteristics, by a process of mixing a major ceramic component with one or more precipitated dopant components. By controlling the conditions of the system, precipitated dopant particles are charged oppositely to major ceramic component particles and are thus associated with the major ceramic component particles.
Inventors
- 👤 Terence C. Dean
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 16:16
CPC Classifications
B; B32; B32B; B32B18/00; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; C04B2235/00; C04B2235/70; C04B2235/74; C04B2235/76; C04B2235/768; C04B2235/78; C04B2235/785; C04B2237/00; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/345; C04B2237/346; C04B2237/348
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
91 words
A method for making a dielectric cermaic having dopant particles uniformly dispersed therein comprising: dispersing major component particles in a liquid medium wherein the major component particles comprise about 98.5 to about 98.8 per cent by weight; precipitating dopant particles from a liquid medium containing a precursor of the dopant wherein the dopant particles comprise about 1.2 to about 1.5 per cent by weight; dispersing the dopant articles throughout the major component particles so that the dopant particles are associated with the major component particles; removing the liquid medium; and sintering.
Claim 2
Independent Claim
91 words
A method for making a dielectric cermaic having dopant particles uniformly dispersed therein comprising: dispersing major component particles in a liquid medium wherein the major component particles comprise about 98.5 to about 98.8 per cent by weight; precipitating dopant particles from a liquid medium containing a precursor of the dopant wherein the dopant particles comprise about 1.2 to about 1.5 per cent by weight; dispersing the dopant articles throughout the major component particles so that the dopant particles are associated with the major component particles; removing the liquid medium; and sintering.
Claim 3
Dependent Claim
45 words
The method of claim 1 wherein the dopant particles comprise a first dopant, cobalt oxide, and a second dopant which is dispersed by precipitating it in the presence of the major component particles such that the dopant particles become associated with the major component particles.
Claim 4
Dependent Claim
27 words
The method of claim 2 wherein the dopant which is precipitated is precipitated such that the dopant particles are of a particle size of about 0.1 microns.
Claim 5
Dependent Claim
40 words
The method of claim 2 wherein the liquid medium containing the precursor of the dopant is added to the liquid medium containing the major component particles; and wherein the dopant is precipitated in the presence of the major component particles.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the major component is barium titanate and the dopant particles comprise niobium pentoxide and cobalt oxide.
Claim 7
Dependent Claim
30 words
The method of claim 1 wherein the major component particles are dispersed in water and the precursor of the dopant is dispersed in a solution of niobium pentoxide and ethanol.
Claim 8
Dependent Claim
40 words
A dielectric cermaic comprising: a sintered mass of precipitated dopant particles dispersed throughout major component particles such that the dopant particles are associated with the major component particles wherein said precipitated dopant particles are smaller than said major component particles.
Claim 9
Dependent Claim
40 words
A dielectric cermaic comprising: a sintered mass of precipitated dopant particles dispersed throughout major component particles such that the dopant particles are associated with the major component particles wherein said precipitated dopant particles are smaller than said major component particles.
Claim 10
Dependent Claim
36 words
The dielectric ceramic composition of claim 7 wherein the major component is chosen from the group consisting of perovskite forming metal oxides, and the dopant particles comprise a first dopant, cobalt oxide, and a second dopant.
Claim 11
Dependent Claim
19 words
The dielectric composition of claim 8 wherein the major component comprises barium titanate and the dopant comprises niobium pentoxide.
Claim 12
Dependent Claim
12 words
The dielectric composition of claim 8 wherein the dopant comprises niobium pentoxide.
Claim 13
Dependent Claim
131 words
A multilayer cermaic capacitor comprising; a plurality of dielectric ceramic layers wherein the dielectric ceramic comprises precipitated niobium pentroxide particles and cobalt oxide particles associated with barium titanate particles such that the dopant particles are in fixed proportion to the major component particles and such that the dielectric ceramic when fired has a dielectric constant between about 4900 and 5400, a dissipation factor of below about 2.0%, an insulation resistance capacitance product about 7000 ohm-farads at 25° C. and above about 3000 phm-farads at 125° C. and a temperature stable temperature coefficient in which the dielectric constant does not vary more than plus or minus 15% from its value at 25° C. over the temperature range from -55° C. to 125° C.; and a plurality of electrodes between the dielectric layers.
Claim 14
Dependent Claim
131 words
A multilayer cermaic capacitor comprising; a plurality of dielectric ceramic layers wherein the dielectric ceramic comprises precipitated niobium pentroxide particles and cobalt oxide particles associated with barium titanate particles such that the dopant particles are in fixed proportion to the major component particles and such that the dielectric ceramic when fired has a dielectric constant between about 4900 and 5400, a dissipation factor of below about 2.0%, an insulation resistance capacitance product about 7000 ohm-farads at 25° C. and above about 3000 phm-farads at 125° C. and a temperature stable temperature coefficient in which the dielectric constant does not vary more than plus or minus 15% from its value at 25° C. over the temperature range from -55° C. to 125° C.; and a plurality of electrodes between the dielectric layers.
Claim 15
Dependent Claim
16 words
The multilayer ceramic capacitor of claim 11 wherein the major component comprises barium titanate and the
Claim 16
Independent Claim
106 words
A method for making a sintereable ceramic mixture having dopant particles uniformly dispersed therein comprising: dispersing major component particles in a liquid medium therein the major component particles comprise about 98.5 to about 98.8 per cent by weight; precipitating dopant particles from a liquid medium containing a precursor of the dopant wherein the dopant particles comprise about 1.2 to about 1.5 per cent by weight under conditions such that the major component particles are charged oppositely to the dopant particles; dispersing the dopant particles throughout the major component particles, so that the dopant particles are associated with the major component particles; and removing the liquid medium.
Claim 17
Independent Claim
106 words
A method for making a sintereable ceramic mixture having dopant particles uniformly dispersed therein comprising: dispersing major component particles in a liquid medium therein the major component particles comprise about 98.5 to about 98.8 per cent by weight; precipitating dopant particles from a liquid medium containing a precursor of the dopant wherein the dopant particles comprise about 1.2 to about 1.5 per cent by weight under conditions such that the major component particles are charged oppositely to the dopant particles; dispersing the dopant particles throughout the major component particles, so that the dopant particles are associated with the major component particles; and removing the liquid medium.
Claim 18
Dependent Claim
24 words
The method of claim 13 wherein the conditions are controlled by maintaining the pH of the liquid media within a selected range of values.
Claim 19
Dependent Claim
31 words
The method of claim 13 wherein the dopant comprises cobalt oxide, and a compound which is dispersed by precipitation from the liquid medium in the presence of the major component particles.
Claim 20
Dependent Claim
18 words
The method of claim 15 wherein the precipitated dopant particles have a particle size of about 0.1 microns.
Claim 21
Dependent Claim
40 words
The method of claim 15 wherein the liquid medium containing the precursor of the dopant is added to the liquid medium containing the major component particles; and wherein the dopant is precipitated in the presence of the major component particles.
Claim 22
Dependent Claim
19 words
The method of claim 15 wherein the major component is barium titanate and the precipitated dopant is niobium pentoxide.
Claim 23
Dependent Claim
30 words
The method of claim 13 wherein the major component particles are dispersed in water and the precursor of the dopant is dispersed in a solution of niobium pentoxide and ethanol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-01 | 1994-12-31 | 1995-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-01 | 1998-12-31 | 1999-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-01 | 2002-12-31 | 2003-07-02 | $7700.00 | Window Closed / Lapsed |