Hydrophilic material and method of manufacturing
Assignee: Terumo Corp
•
Filing: 1989-07-21
•
Granted: 1991-07-02
•
Expires: 2009-07-21
Abstract
Abstract A hydrophilic material having excellent hydrophilicity and fitness to living bodies and used for porous membranes or the like and also a method of manufacturing the same. The hydrophilic material is formed by subjecting at least part of the surfaces of a substrate of a polymer material to a plasma treatment to thereby produce a polymer radical and graft polymerizing therewith a block copolymer containing a hydrophilic monomer supplied in the gasious phase and a subsequently supplied hydrophobic monomer.
Inventors
- 👤 Makoto Ohnishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:45
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0093; B01D67/00931; A; A61; A61L; A61L33/00; A61L33/0076; A61L33/0088; C; C08; C08J; C08J7/00; C08J7/12; C08J7/16; C08J7/18; B01D2323/00; B01D2323/38; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249978
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
46 words
A hydrophilic material comprising a block copolymer containing a material (X) having a hydrophilic polymer chain and a material (Y) having a hydrophobic polymer chain, the copolymer being coupled as a substantially non-crosslinked graft chain to the surface of a substrate (Z) of a polymer material.
Claim 2
Dependent Claim
46 words
A hydrophilic material comprising a block copolymer containing a material (X) having a hydrophilic polymer chain and a material (Y) having a hydrophobic polymer chain, the copolymer being coupled as a substantially non-crosslinked graft chain to the surface of a substrate (Z) of a polymer material.
Claim 3
Dependent Claim
15 words
A material compatible with a living body comprising the hydrophilic material according to claim 1.
Claim 4
Dependent Claim
86 words
A hydrophilic porous membrane, comprising: (a) a porous membrane substrate (Z); (b) a hydrophilic polymer chain (X) grafted to at least a portion of the substrate (Z); and (c) hydrophobic polymer chain (Y) grafted to the polymer chain (X); wherein the polymer (X) and polymer (Y) together comprise a substantially non-crosslinked block copolymer, and wherein said copolymer is grafted to at least a portion of the surface of the substrate (Z) and to at least a portion of the inner pore surfaces of the substrate (Z).
Claim 5
Dependent Claim
86 words
A hydrophilic porous membrane, comprising: (a) a porous membrane substrate (Z); (b) a hydrophilic polymer chain (X) grafted to at least a portion of the substrate (Z); and (c) hydrophobic polymer chain (Y) grafted to the polymer chain (X); wherein the polymer (X) and polymer (Y) together comprise a substantially non-crosslinked block copolymer, and wherein said copolymer is grafted to at least a portion of the surface of the substrate (Z) and to at least a portion of the inner pore surfaces of the substrate (Z).
Claim 6
Dependent Claim
81 words
The hydrophilic porous membrane according to claim 3, wherein said substrate (Z) comprises a hydrophobic polymer material having at least one of a threshold surface tension of 50 dyne/cm or below or a water absorption factor of 1.0% or below, and wherein said porous membrane has a bubble point of from about 0.2 to about 20.0 kgf/cm 2 , a membrane thickness of from about 20 to about 300 μm and a porosity of from about 20 to about 80 percent.
Claim 7
Dependent Claim
21 words
The hydrophilic porous membrane according to claim 3 or 4, wherein said substrate (Z) comprises a hydrophobic polymer material including polypropylene.
Claim 8
Dependent Claim
33 words
The hydrophilic porous membrane according to claim 3, wherein polymer (X) comprises repeating units of an acryl or methacryl derivative, a vinyl monomer containing a polyether group, or an acrylamide or methacrylamide derivative.
Claim 9
Dependent Claim
32 words
The hydrophilic porous membrane according to claim 6, wherein polymer (X) comprises repeating units selected from the group consisting of polyhydroxyethylacrylate, polydimethylamino-methylmethacrylate, polyethylene glycol, polypropylene glycol, polyacrylamide, polydiacetoneamide, poly-N-methylacrylamide, and combinations thereof.
Claim 10
Dependent Claim
29 words
The hydrophilic porous membrane according to claim 3, wherein polymer (Y) comprises a polymer having a threshold surface tension or water absorption factor less than that of polymer (X).
Claim 11
Dependent Claim
30 words
The hydrophilic porous membrane according to claim 3, wherein polymer (Y) comprises repeating units selected from the group consisting of polystyrene, polyethylmethacrylate, polybutylacrylate, polymethylmethacrylate, polyvinylidene chloride, polytetrafluoroethylene and combinations thereof.
Claim 12
Dependent Claim
29 words
The hydrophilic porous membrane according to claim 3, wherein water permeability through said porous membrane is substantially maintained when said porous membrane is in contact with an aqueous medium.
Claim 13
Independent Claim
111 words
A method for producing a hydrophilic material, comprising the steps of: (a) plasma treating at least part of the surface of a polymer substrate (Z), thereby producing polymer radicals on the surface of substrate (Z); (b) graft polymerizing a gaseous hydrophilic monomer (X) onto the polymer substrate surface via said polymer radicals, thereby forming a polymer (X) attached at one end to said surface; and (c) graft polymerizing a gaseous hydrophobic monomer (Y) onto said hydrophilic polymer (X) at a point of growth of the hydrophilic polymer (X), thereby forming a polymer (Y) attached at one end to said polymer (X), the polymers (X) and (Y) forming a substantially non-crosslinked copolymer.
Claim 14
Independent Claim
111 words
A method for producing a hydrophilic material, comprising the steps of: (a) plasma treating at least part of the surface of a polymer substrate (Z), thereby producing polymer radicals on the surface of substrate (Z); (b) graft polymerizing a gaseous hydrophilic monomer (X) onto the polymer substrate surface via said polymer radicals, thereby forming a polymer (X) attached at one end to said surface; and (c) graft polymerizing a gaseous hydrophobic monomer (Y) onto said hydrophilic polymer (X) at a point of growth of the hydrophilic polymer (X), thereby forming a polymer (Y) attached at one end to said polymer (X), the polymers (X) and (Y) forming a substantially non-crosslinked copolymer.
Claim 15
Dependent Claim
34 words
The method according to claim 11, including after step (c), the step of (d) graft polymerizing monomer (X) onto polymer (Y) at the point of growth of polymer (Y), thereby forming a copolymer (X)--(Y)--(X).
Claim 16
Dependent Claim
36 words
The method according to claim 12, including after step (d), repeating at least once steps (c) and (d), thereby producing a graft copolymer on substrate (Z) which includes alternating blocks of polymer (X) and polymer (Y).
Claim 17
Dependent Claim
36 words
The method according to claim 11, 12 or 13, wherein the substrate (Z) is porous, and wherein the graft polymerization of monomer (X) and monomer (Y) takes place at the inner pore surfaces of polymer (Z).
References Cited (Backward Citations)
US3666693A
Cited
US4032440A
Cited
US4100113A
Cited
US4280970A
Cited
US4346142A
Cited
US4432875A
Cited
US4413074A
Cited
US4594079A
Cited
US4618533A
Cited
EP0249513A2
Cited
US4845132A
Cited
US4784769A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-01 | 1994-12-31 | 1995-07-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-01 | 1998-12-31 | 1999-07-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-01 | 2002-12-31 | 2003-07-02 | $7700.00 | Window Closed / Lapsed |