High temperature combuster
Assignee: CORNELISON RICHARD C dba CAMET Co 12000 WINROCK ROAD HIRAM OHIO 44234
•
Filing: 1988-07-15
•
Granted: 1991-06-25
•
Expires: 2008-07-15
Abstract
Abstract There has thus been provided a highly efficient metal-ceramic catalytic combustor for a gas turbine/catalytic combustor assembly. The catalyst zone is formed of a high temperature resistant metal wire mesh, e.g., palladium coated tungsten or ferritic stainless steel screen, e.g., 40 mesh, which is aluminized with metallic aluminum, and heated to convert the outermost layer of aluminum to aluminum oxide and encourage the diffusion of the inner layer of aluminum into the body of the metal wire, desirably forming a thin metal/aluminum alloy layer. The outer surface because of the Kerkendall Effect is porous and readily accepts and strongly bonds to a metal oxide coat, e.g., a magnesia/alumina, or magnesia/alumina/yttria, or barium oxide/alumina, or barium oxide/alumina/yttria wash coat. There may also be included a catalyst deposited on the ceramic outer coat, e.g., a noble metal catalyst, for enhancement of the combustion of an air/fuel mixture. Because the metals from which the wire mesh is formed all have melting points above the maximum temperature of operation, i.e., 2700° F., the screen itself has significant tensile strength at temperature.
Inventors
- 👤 Richard C. Cornelison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:57
CPC Classifications
F; F23; F23C; F23C13/00; B; B01; B01J; B01J35/00; B01J35/50; B01J35/58; C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C04B2111/00; C04B2111/00474; C04B2111/0081; C04B2111/80; Y; Y10; Y10S; Y10S502/00; Y10S502/525
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
154 words
A catalytic combustor device for gas turbine power plants comprising a housing, a primary fuel mixing zone, and a catalytic combustor in axially spaced relation to said fuel mixing zone within said housing, said catalytic combustor being characterized by a coated catalyst support member disposed in air/fuel intercepting relation in said fuel mixing zone within said housing, said catalyst combustor comprising nonnesting layers of said coated catalyst support member which is nonlinearly corrugated and which is made of a first layer composed of a high temperature resistant refractory metal or a ferritic stainless steel, a second layer composed of a noble metal adhered to said first layer, a third layer composed of a refractory metal oxide on said second layer, and fourth layer composed of a catalytically active noble metal catalyst supported on said third layer, said coated catalyst support member being in the form of a metal-ceramic honeycomb which is opaque to infrared.
Claim 2
Dependent Claim
154 words
A catalytic combustor device for gas turbine power plants comprising a housing, a primary fuel mixing zone, and a catalytic combustor in axially spaced relation to said fuel mixing zone within said housing, said catalytic combustor being characterized by a coated catalyst support member disposed in air/fuel intercepting relation in said fuel mixing zone within said housing, said catalyst combustor comprising nonnesting layers of said coated catalyst support member which is nonlinearly corrugated and which is made of a first layer composed of a high temperature resistant refractory metal or a ferritic stainless steel, a second layer composed of a noble metal adhered to said first layer, a third layer composed of a refractory metal oxide on said second layer, and fourth layer composed of a catalytically active noble metal catalyst supported on said third layer, said coated catalyst support member being in the form of a metal-ceramic honeycomb which is opaque to infrared.
Claim 3
Dependent Claim
220 words
A catalytic combustor having a housing, a fuel-air mixing zone, and a catalytic combustor zone in spaced relation within said housing, means for feeding fuel to said fuel-air mixing zone, means for feeding a fuel oxidant to said fuel-air mixing zone, said catalytic combustor zone characterized by a metallic honeycomb of a high temperature and oxidation resistant metal wire screen having coated thereon a noble metal layer, and an additional coating of a metal oxide which is impregnated thereon with a catalyst, said wire having a melting point of from about 2600° F. to about 6150° F., said screen having a wire diameter of from about 0.001" to about 0.01" and a mesh size of from about 15 to about 200 uniformly spaced wires per inch, said screen being corrugated to a pitch of from about 0.02" to about 0.2" and an amplitude of from about 0.05" to about 0.25", said metal oxide having a thickness of from about 0.0005" to about 0.003" and being strongly adhered to said wire, said honeycomb comprising a number of layers of such metal oxide coated corrugated wire screen dimensioned to fill the cross-section of said catalytic combustor zone and axially dimensioned sufficient to render said honeycomb opaque to infrared radiation and to provide a gas permeable open area of at least about 70%.
Claim 4
Dependent Claim
220 words
A catalytic combustor having a housing, a fuel-air mixing zone, and a catalytic combustor zone in spaced relation within said housing, means for feeding fuel to said fuel-air mixing zone, means for feeding a fuel oxidant to said fuel-air mixing zone, said catalytic combustor zone characterized by a metallic honeycomb of a high temperature and oxidation resistant metal wire screen having coated thereon a noble metal layer, and an additional coating of a metal oxide which is impregnated thereon with a catalyst, said wire having a melting point of from about 2600° F. to about 6150° F., said screen having a wire diameter of from about 0.001" to about 0.01" and a mesh size of from about 15 to about 200 uniformly spaced wires per inch, said screen being corrugated to a pitch of from about 0.02" to about 0.2" and an amplitude of from about 0.05" to about 0.25", said metal oxide having a thickness of from about 0.0005" to about 0.003" and being strongly adhered to said wire, said honeycomb comprising a number of layers of such metal oxide coated corrugated wire screen dimensioned to fill the cross-section of said catalytic combustor zone and axially dimensioned sufficient to render said honeycomb opaque to infrared radiation and to provide a gas permeable open area of at least about 70%.
Claim 5
Dependent Claim
17 words
A catalytic combustor in accordance with claim 2 wherein the metal oxide is a refractory metal oxide.
Claim 6
Dependent Claim
15 words
A catalytic combustor in accordance with claim 3 wherein the refractory metal oxide comprises alumina.
Claim 7
Dependent Claim
15 words
A catalytic combustor in accordance with claim 3 wherein the refractory metal oxide comprises perovskite.
Claim 8
Dependent Claim
34 words
A catalytic combustor in accordance with claim 3 wherein the refractory metal oxide coated wire screen substrate is folded in a zig-zag manner back and forth upon itself to form a three dimensional core.
Claim 9
Dependent Claim
16 words
A catalytic combustor in accordance with claim 3 wherein the catalyst is a noble metal catalyst.
Claim 10
Dependent Claim
15 words
A catalytic combustor in accordance with claim 7 wherein the noble metal catalyst is palladium.
Claim 11
Dependent Claim
15 words
A catalytic combustor in accordance with claim 7 wherein the noble metal catalyst is platinum.
Claim 12
Dependent Claim
15 words
A catalytic combustor in accordance with claim 7 wherein the noble metal catalyst is rhodium.
References Cited (Backward Citations)
US2811490A
Cited
US2887456A
Cited
US3867313A
Cited
US3928961A
Cited
US3940923A
Cited
US4019316A
Cited
US3846979A
Cited
US3975900A
Cited
US3992330A
Cited
US4094142A
Cited
US4119701A
Cited
US4098722A
Cited
US4072007A
Cited
US4154568A
Cited
US4252690A
Cited
US4196099A
Cited
US4233183A
Cited
US4276203A
Cited
US4287090A
Cited
GB2072036A
Cited
US4295818A
Cited
US4337028A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-24 | 1994-12-24 | 1995-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-24 | 1998-12-24 | 1999-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-24 | 2002-12-24 | 2003-06-25 | $7700.00 | Window Closed / Lapsed |