Catalytic system and process for producing it
Assignee: Acurex Corp
•
Filing: 1979-04-26
•
Granted: 1981-06-30
•
Expires: 1999-04-26
Abstract
Abstract A system and process for forming a catalytic bed in which the active catalytic material is formed with an enhanced surface area and secure adhesion onto a support structure. The system is formed by a process in which a liquid solution of a salt which is decomposable into a refractory oxide is applied to a support structure. The solution is dried to remove the solvent and, following decomposition of said salt, an active catalytic material is impregnated by applying onto the surface a soluble compound comprised of a noble metal or a catalytic oxide-forming metal. The structure is calcined to activate the catalytic material.
Inventors
- 👤 William C. Pfefferle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:14
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/024; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
98 words
In a process for forming a catalytic bed with a porous support structure of a low surface area ceramic, the steps of applying onto the surface of the support structure a mixture consisting essentially of a solution of a solvent and a salt which decomposes to form a refractory oxide, drying the solution to remove the solvent therefrom, decomposing the salt into the oxide leaving a refractory oxide adhering within the surface pores of the support structure, impregnating the surface with a solution of an active catalytic material, and drying the last-mentioned solution to remove the solvent therefrom.
Claim 2
Dependent Claim
98 words
In a process for forming a catalytic bed with a porous support structure of a low surface area ceramic, the steps of applying onto the surface of the support structure a mixture consisting essentially of a solution of a solvent and a salt which decomposes to form a refractory oxide, drying the solution to remove the solvent therefrom, decomposing the salt into the oxide leaving a refractory oxide adhering within the surface pores of the support structure, impregnating the surface with a solution of an active catalytic material, and drying the last-mentioned solution to remove the solvent therefrom.
Claim 3
Dependent Claim
28 words
A process as in claim 1 in which the salt is comprised of an element selected from the group consisting of zirconium, thorium, cerium, magnesium, lanthanum and aluminum.
Claim 4
Dependent Claim
13 words
A process as in claim 1 in which the salt is a nitrate.
Claim 5
Dependent Claim
13 words
A process as in claim 1 in which the salt is a sulfate.
Claim 6
Dependent Claim
13 words
A process as in claim 1 in which the salt is an acetate.
Claim 7
Dependent Claim
31 words
A process as in claim 1 in which the step of decomposing the salt is carried out by heating the applied salt above its decomposition temperature to form the refractory oxide.
Claim 8
Dependent Claim
84 words
A process as in claim 1 in which the step of impregnating the surface with the catalytic material is carried out by applying a solution of a halide of a noble metal to the surface of the support structure onto which the solution of a salt is applied, and drying to remove the solvent from the metal halide solution, and the step of decomposing the salt is carried out by heating the applied salt to a temperature which decomposes the salt into said oxide.
Claim 9
Dependent Claim
97 words
A process as in claim 1 in which the salt is selected from the group consisting of zirconyl nitrate, thorium nitrate and aluminum nitrate, said salt is applied onto the surface in a solution with a liquid solvent, the step of impregnating the surface with the catalytic material is carried out by applying to the surface a metal halide in which the metal is selected from the group consisting of platinum, palladium and iridium, and the applied salt is heated to above the decomposition temperature of the salt to thermally decompose the same to form said oxide.
Claim 10
Dependent Claim
85 words
A catalytic system comprising a porous support structure of a low surface area ceramic, a refractory oxide formed in the surface pores of the support structure by the method of applying onto the surface of the support a mixture consisting essentially of a solution of a solvent and a salt which is decomposable into the oxide, drying the solution to remove the solvent therefrom, and decomposing the salt within the surface pores to form the oxide, and an active catalytic material adhering to the oxide.
Claim 11
Dependent Claim
85 words
A catalytic system comprising a porous support structure of a low surface area ceramic, a refractory oxide formed in the surface pores of the support structure by the method of applying onto the surface of the support a mixture consisting essentially of a solution of a solvent and a salt which is decomposable into the oxide, drying the solution to remove the solvent therefrom, and decomposing the salt within the surface pores to form the oxide, and an active catalytic material adhering to the oxide.
Claim 12
Dependent Claim
22 words
A catalytic system as in claim 9 in which the salt is decomposed by heating the same to above its decomposition temperature.
Claim 13
Dependent Claim
29 words
A catalytic system as in claim 9 in which the salt is comprised of an element selected from the group consisting of zirconium, thorium, aluminum, lanthanum, cerium, and magnesium.
Claim 14
Dependent Claim
25 words
A catalytic system as in claim 9 in which the salt is selected from the group consisting of zirconyl nitrate, thorium nitrate and aluminum sulfate.
Claim 15
Dependent Claim
53 words
A catalytic system as in claim 9 in which the catalytic material is formed on the oxide by applying to the surface a metal halide in which the metal is a noble metal, and heating the metal halide to a temperature which decomposes the halide into the noble metal adhering to the oxide.
Claim 16
Dependent Claim
23 words
A catalytic system as in claim 13 in which the metal is selected from the group consisting of platinum, iridium, rhodium, and palladium.
Claim 17
Dependent Claim
36 words
A catalytic system as in claim 9 in which the catalytic material is formed on the oxide by applying to the surface a soluble compound of a metal and converting said compound to the metal oxide.
Claim 18
Dependent Claim
28 words
A catalytic system as in claim 15 in which the metal oxide is selected from the group consisting of cobalt oxide, nickel oxide, chromium oxide and manganese oxide.
References Cited (Backward Citations)
US3565830A
Cited
US3362783A
Cited
US3615166A
Cited
US3903020A
Cited
US3931050A
Cited
US3960510A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-29 | 1984-12-29 | 1985-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-29 | 1988-12-29 | 1989-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-29 | 1992-12-29 | 1993-06-30 | $7700.00 | Window Closed / Lapsed |