Method for decontaminating a pressurized water nuclear reactor system
Assignee: Westinghouse Electric Corp
•
Filing: 1989-08-09
•
Granted: 1991-06-18
•
Expires: 2009-08-09
Abstract
Abstract Metal surfaces having an oxide coating containing radioactive substances, such as the primary system of a pressurized water reactor, are decontaminated by passage thereover of a decontamination solution containing a weak chelating agent, such as nitrilotriacetic acid, and a ferrous salt, such as ferrous glutonate. The weak chelating agent is present in an aqueous solution in an amount of 0.1 to 2.0 percent by weight and the ferrous salt in an amount to provide 50 to 500 parts per million iron based on the weight of the solution. The solution, after contact with the metal surfaces is regenerated by an ion exchange resin or, preferably, by electrolysis.
Inventors
- 👤 Alexander P. Murray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:49
CPC Classifications
G; G21; G21F; G21F9/00; G21F9/001; G21F9/002; G21F9/004
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
89 words
The method of decontaminating metal surfaces having an oxide coating containing radioactive substances comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent capable of forming multiligand complexes with metals, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; and passing said decontamination solution over the metal surfaces.
Claim 2
Independent Claim
89 words
The method of decontaminating metal surfaces having an oxide coating containing radioactive substances comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent capable of forming multiligand complexes with metals, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; and passing said decontamination solution over the metal surfaces.
Claim 3
Dependent Claim
29 words
The method as defined in claim 1 wherein said weak chelating agent is selected from the group consisting of nitrilotriacetic acid, hydroxyethylenediamine tetraacetic acid, citric acid, and iminodiacetic acid.
Claim 4
Dependent Claim
25 words
The method as defined in claim 1 wherein said ferrous salt is selected from the group consisting of ferrous acetate, ferrous oxalate and ferrous glutonate.
Claim 5
Dependent Claim
44 words
The method as defined in claim 1 wherein said weak chelating agent is nitrilotriacetic acid and is present in an amount of about 0.2 percent, and said ferrous salt is ferrous glutonate and is present in an amount to provide about 100 ppm iron.
Claim 6
Dependent Claim
28 words
The method as defined in claim 1 wherein said decontamination solution, after contact with said metal surfaces is regenerated and returned for further passing over the metal surfaces.
Claim 7
Dependent Claim
21 words
The method as defined in claim 5 wherein said decontamination solution is regenerated by passage thereof over a cation exchange resin.
Claim 8
Dependent Claim
20 words
The method as defined in claim 5 wherein said decontamination solution is regenerated by passage thereof through a permeable electrode.
Claim 9
Independent Claim
140 words
The method of decontaminating metal surfaces having an oxide coating containing radioactive substances comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent selected from the group consisting of nitrilotriacetic acid, hydroxyethylenediamine tetraacetic acid, citric acid, and iminodiacetic acid, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt, selected from the group consisting of ferrous acetate, ferrous oxalate and ferrous glutonate, in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; and passing said decontamination solution over the metal surfaces; and after contact with said metal surfaces, regenerating said solution by passage thereof through a permeable electrode, and returning the regenerated solution for further passing over the metal surfaces.
Claim 10
Independent Claim
140 words
The method of decontaminating metal surfaces having an oxide coating containing radioactive substances comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent selected from the group consisting of nitrilotriacetic acid, hydroxyethylenediamine tetraacetic acid, citric acid, and iminodiacetic acid, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt, selected from the group consisting of ferrous acetate, ferrous oxalate and ferrous glutonate, in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; and passing said decontamination solution over the metal surfaces; and after contact with said metal surfaces, regenerating said solution by passage thereof through a permeable electrode, and returning the regenerated solution for further passing over the metal surfaces.
Claim 11
Independent Claim
97 words
A method of dissolving radioactive corrosion products from the internal metallic surfaces of a pressurized water nuclear reactor comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent capable of forming multiligand complexes with metals of said metallic surfaces, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; passing said decontamination solution over said metallic surfaces.
Claim 12
Independent Claim
97 words
A method of dissolving radioactive corrosion products from the internal metallic surfaces of a pressurized water nuclear reactor comprising: providing an aqueous decontamination solution which comprises an aqueous solution of a weak chelating agent capable of forming multiligand complexes with metals of said metallic surfaces, said chelating agent present in an amount of between about 0.1 to 2.0 percent based on the weight of the solution, and a ferrous salt in an amount to provide 50 to 500 parts per million iron based on the weight of the solution; passing said decontamination solution over said metallic surfaces.
Claim 13
Dependent Claim
47 words
The method as defined in claim 9 wherein said weak chelating agent is selected from the group consisting of nitrilotriacetic acid, hydroxyethylenediamine tetraacetic acid, citric acid, and iminodiacetic acid, and said ferrous salt is selected from the group consisting of ferrous acetate, ferrous oxalate and ferrous glutonate.
Claim 14
Dependent Claim
28 words
The method as defined in claim 10 wherein said decontamination solution, after contact with said metal surfaces is regenerated and returned for further passing over the metal surfaces.
Claim 15
Dependent Claim
21 words
The method as defined in claim 11 wherein said decontamination solution is regenerated by passage thereof over a cation exchange resin.
Claim 16
Dependent Claim
20 words
The method as defined in claim 11 wherein said decontamination solution is regenerated by passage thereof through a permeable electrode.
References Cited (Backward Citations)
US3873362A
Cited
US4325744A
Cited
US4587043A
Cited
US4537666A
Cited
US4828790A
Cited
US4670066A
Cited
US4792385A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |