Abstract Processes for producing titanium alloy SPF/DB components, particularly structural panels, are provided. In one embodiment, the process comprises providing rapidly solidified titanium alloy sheetstock, providing a plurality of rapidly solidified titanium alloy ribbons or strips, forming the ribbons into waveform structures, assembling a plurality of these waveform structures to produce a honeycomb core, positioning this core between face sheets, and bonding the core to the face sheets. In another embodiment the process comprises providing rapidly solidified titanium alloy sheetstock, superplastically forming at least one piece of sheetstock into a shaped piece having spaced apart, parallel bonding regions, positioning this shaped piece between two face sheets, and bonding the shaped piece to each face sheet. In yet another embodiment of the invention, the process comprises providing rapidly solidified titanium alloy sheetstock, applying a diffusion bond-inhibiting material in a desired pattern to at least one piece of sheetstock, assembling the sheetstock having the bond-inhibiting pattern thereon with at least one further piece of sheetstock, diffusion bonding this assembly, and superplastically forming the bonded assembly by introducing an inert gas into the region defined by the bond-inhibiting material.
A method for producing a titanium alloy honeycomb-core structural panel which comprises the steps of: (a) forming a plurality of rapidly solidified titanium alloy strips into waveform structures; (b) assembling a plurality of said waveform structures to produce a honeycomb core; (c) positioning said core between two cover pieces of rapidly solidified titanium alloy sheetstock; and (d) diffusion bonding said core to each of said cover pieces.
Claim 2
Independent Claim
67 words
A method for producing a titanium alloy honeycomb-core structural panel which comprises the steps of: (a) forming a plurality of rapidly solidified titanium alloy strips into waveform structures; (b) assembling a plurality of said waveform structures to produce a honeycomb core; (c) positioning said core between two cover pieces of rapidly solidified titanium alloy sheetstock; and (d) diffusion bonding said core to each of said cover pieces.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said titanium alloy is selected from the group consisting of alpha+beta titanium alloys and beta titanium alloys.
Claim 4
Dependent Claim
41 words
The method of claim 1 wherein said sheetstock is fabricated from rapidly solidified foil by diffusion bonding a plurality of layers of foil under bonding conditions which permit retention of the uniform and fine grain microstructure of said rapidly solidified foil.
Claim 5
Dependent Claim
10 words
The method of claim 3 wherein said strips are sheetstock.
Claim 6
Dependent Claim
53 words
The method of claim 1 wherein said strips are relatively thick foils fabricated from relatively thin, rapidly solidified foil by diffusion bonding a plurality of layers of said relatively thin rapidly solidified foil under bonding conditions which permit retention of the uniform and fine grain microstructure of said relatively thin rapidly solidified foil.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said waveform structures are joined together during assembly to produce said honeycomb core.
Claim 8
Dependent Claim
15 words
The method of claim 6 wherein said waveform structures are joined together by diffusion bonding.
Claim 9
Dependent Claim
34 words
The method of claim 6 wherein said waveform structures are joined together by a fugitive thermoplastic binder material and wherein said fugitive binder is removed prior to bonding said core to said cover pieces.
Claim 10
Dependent Claim
47 words
The method of claim 1 wherein diffusion bonding is carried out at a temperature about 100° to 300° C. below the beta-transus temperature of said titanium alloy at a pressure of about 10 to about 100 MPa for about 15 minutes to about 24 hours or more.