Polyvinylidene fluoride porous membrane and a method for producing the same
Assignee: Asahi Kasei Corp
•
Filing: 1990-01-10
•
Granted: 1991-06-11
•
Expires: 2010-01-10
Abstract
Abstract A porous membrane comprising a polyvinylidene fluoride resin and having a uniform, three-dimensional, network pore structure. The membrane has excellent chemical resistance, excellent filtering characteristics and excellent mechanical properties. The porous membrane can be produced by blending a polyvinylidene fluoride resin, an organic liquid and a powdery hydrophobic silica, subjecting the resultant blend to melt-molding to form a membrane, and extracting the organic liquid and the hydrophobic silica from the melt-molded membrane.
Inventors
- 👤 Yoshinao Doi
- 👤 Haruo Matsumura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:41
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/26; B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/003; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/34; B01D2323/00; B01D2323/02; B01D2325/00; B01D2325/24; C08J2201/00; C08J2201/04; C08J2201/054; C08J2201/0542; C08J2201/0543; C08J2201/0545; C08J2201/0546; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/16
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
216 words
A porous membrane comprising a polyvinylidene fluoride, resin and having pores running throughout an interior of said porous membrane and opening at both surfaces of said porous membrane, said interior of said porous membrane containing substantially no macrovoids having a diameter of 10 μm or more, the average diameter of said pores in each surface of said porous membrane being within the range of from 0.05 μm to less than 5 μm, the ratio of the average pore diameter of said pores at each surface of said porous membrane to the average pore diameter of said pores in the interior of said porous membrane in terms of the average pore diameter of pores in a cross-section of said porous membrane taken along a line perpendicular to each surface of said porous membrane, being from 0.5 to 2.0, the ratio of the maximum pore diameter of said pores as measured by the bubble point method to a true average pore diameter of said pores as measured by the half-dry method being from 1.2 to 2.5, and said membrane having a uniform, three-dimensional, network pore structure, and a tensile strength at break of from 70 to 200 kg/cm 2 , a tensile elongation at break of from 100 to 500% and a porosity of from 40 to 90%.
Claim 2
Dependent Claim
216 words
A porous membrane comprising a polyvinylidene fluoride, resin and having pores running throughout an interior of said porous membrane and opening at both surfaces of said porous membrane, said interior of said porous membrane containing substantially no macrovoids having a diameter of 10 μm or more, the average diameter of said pores in each surface of said porous membrane being within the range of from 0.05 μm to less than 5 μm, the ratio of the average pore diameter of said pores at each surface of said porous membrane to the average pore diameter of said pores in the interior of said porous membrane in terms of the average pore diameter of pores in a cross-section of said porous membrane taken along a line perpendicular to each surface of said porous membrane, being from 0.5 to 2.0, the ratio of the maximum pore diameter of said pores as measured by the bubble point method to a true average pore diameter of said pores as measured by the half-dry method being from 1.2 to 2.5, and said membrane having a uniform, three-dimensional, network pore structure, and a tensile strength at break of from 70 to 200 kg/cm 2 , a tensile elongation at break of from 100 to 500% and a porosity of from 40 to 90%.
Claim 3
Dependent Claim
41 words
The porous membrane according to claim 1, wherein said polyvinylidene fluoride resin is a vinylidene fluoride homopolymer or a copolymer of vinylidene fluoride and at least one comonomer selected from the group consisting of ethylene tetrafluoride, propylene hexafluoride, trifluorochloroethylene and ethylene.
Claim 4
Dependent Claim
22 words
The porous membrane according to claim 1, wherein said interior contains substantially no macrovoids having a diameter of 5 μm or more.
Claim 5
Dependent Claim
51 words
A method for producing a porous membrane of claim 1, comprising: (a) blending a polyvinylidene fluoride resin with an organic liquid and a powdery hydrophobic silica; (b) subjecting the resultant blend to melt-molding to form a membrane; and (c) extracting said organic liquid and said powdery hydrophobic silica from said membrane.
Claim 6
Dependent Claim
24 words
The method according to claim 4, wherein in step (c), said organic liquid is first extracted and, subsequently, said powdery hydrophobic silica is extracted.
Claim 7
Dependent Claim
24 words
The method according to claim 4, wherein in step (c), said organic liquid and said powdery hydrophobic silica are simultaneously extracted from said membrane.
Claim 8
Independent Claim
69 words
The method according to any one of claims 4 to 6, wherein said powdery hydrophobic silica has an average primary particle diameter of from 0.005 to 0.5 μm, a specific surface area of from 30 to 500 m 2 /g and a methanol wettability of at least 30% by volume in terms of the methanol concentration of an aqueous methanol solution capable of completely wetting said powdery hydrophobic silica.
Claim 9
Independent Claim
69 words
The method according to any one of claims 4 to 6, wherein said powdery hydrophobic silica has an average primary particle diameter of from 0.005 to 0.5 μm, a specific surface area of from 50 to 300 m 2 /g and a methanol wettability of at least 30% by volume in terms of the methanol concentration of an aqueous methanol solution capable of completely wetting said powdery hydrophobic silica.
Claim 10
Independent Claim
24 words
The method according to any one of claims 4 to 6, wherein said organic liquid has a solubility parameter of from 8.4 to 10.5.
Claim 11
Independent Claim
37 words
The method according to any one of claims 4 to 6, wherein said organic liquid is a mixture of at least two different types of organic liquids each having a solubility parameter of from 8.4 to 10.5.
Claim 12
Dependent Claim
26 words
The method according to claim 10, wherein said mixture contains at least 50% by weight of dioctyl phthalate, based on the total weight of said mixture.
Claim 13
Independent Claim
45 words
The method according to any one of claims 4 to 6, wherein said polyvinylidene fluoride resin is a vinylidene fluoride homopolymer or a copolymer of vinylidene fluoride and at least one comonomer selected from the group consisting of ethylene tetrafluoride, propylene hexafluoride, trifluorochloroethylene and ethylene.
References Cited (Backward Citations)
US3642668A
Cited
US3855133A
Cited
US3929950A
Cited
US3862030A
Cited
US4203848A
Cited
US4203847A
Cited
US4177228A
Cited
US4234528A
Cited
US4237083A
Cited
JPS5637836A
Cited
US4499211A
Cited
JPS5891732A
Cited
JPS5893734A
Cited
JPS6097001A
Cited
GB2168981A
Cited
US4921653A
Cited
GB2190039A
Cited
US4810384A
Cited
US4833172A
Cited
US4806291A
Cited
EP0330072A2
Cited
US4842741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-10 | 1994-12-10 | 1995-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-10 | 1998-12-10 | 1999-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-10 | 2002-12-10 | 2003-06-11 | $7700.00 | Window Closed / Lapsed |