Process of manufacturing a microporous sheet material
Assignee: Evanite Fiber Corp
•
Filing: 1979-02-13
•
Granted: 1980-12-02
•
Expires: 1999-02-13
Abstract
Abstract A process of manufacturing a microporous sheet by forming a blend of a polyolefin, silica and a water insoluble plasticizer, forming a sheet from the blend, and contacting the sheet with water for a time sufficient to render the sheet microporous. The plasticizer, being essentially insoluble in water, is easily separated therefrom and recycled. The preferred plasticizers are dialkyl phthalates and dialkyl adipates having between about two and about eleven carbon atoms in the oxo-alcohol moiety.
Inventors
- 👤 James Young
- 👤 Charles H. Geissel
- 👤 Piotr Zenczak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 08:27
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/003; B01D39/00; B01D39/08; B01D39/083; B01D39/14; B01D39/16; B01D39/1607; B01D39/1623; B01D69/00; B01D69/14; B01D69/141; B01D69/148; B01D71/00; B01D71/06; B01D71/26; B01D71/261; B01D71/262; B29; B29C; B29C67/00; B29C67/20; B29C67/202; C; C08; C08J; C08J9/00; C08J9/28; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; B01D2239/00; B01D2239/04; B01D2239/0407; B01D2239/0414; B01D2239/0421; B01D2239/12; B01D2239/1241; B01D2323/00; B01D2323/15; B01D2323/20; C08J2201/00; C08J2201/04; C08J2201/054; C08J2201/0542; C08J2201/0544; C08J2323/00; C08J2323/02; H01M50/489; H01M50/494; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10S; Y10S264/00; Y10S264/17
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
97 words
A process of manufacturing a microporous sheet comprising: plasticating a blend comprising a polyolefin selected from the group consisting of homopolymers and copolymers of ethylene, propylene and buylene, and mixtures thereof; finely divided silica; and a substantially water-insoluble plasticizer selected from the group consisting of dialkyl phthalates and dialkyl adipates having between about two to eleven carbon atoms in the oxo-alcohol moiety; forming a sheet from the plasticated blend; and contacting the sheet with water for a period of time sufficient to remove an amount of the plasticizer from the sheet sufficient to render the sheet microporous.
Claim 2
Dependent Claim
97 words
A process of manufacturing a microporous sheet comprising: plasticating a blend comprising a polyolefin selected from the group consisting of homopolymers and copolymers of ethylene, propylene and buylene, and mixtures thereof; finely divided silica; and a substantially water-insoluble plasticizer selected from the group consisting of dialkyl phthalates and dialkyl adipates having between about two to eleven carbon atoms in the oxo-alcohol moiety; forming a sheet from the plasticated blend; and contacting the sheet with water for a period of time sufficient to remove an amount of the plasticizer from the sheet sufficient to render the sheet microporous.
Claim 3
Dependent Claim
21 words
The process of claim 1 wherein the polyolefin is selected from the group consisting of high-density polyethylene and substantially isotactic polypropylene.
Claim 4
Dependent Claim
20 words
The process of claim 2 wherein the polyolefin is high-density polyethylene having a standard load melt index of substantially 0.
Claim 5
Dependent Claim
49 words
The process of claim 1 where the polyolefin comprises between about 4% and about 20% by weight of the blend, the silica comprises between about 15% and about 50% by weight of the blend, and the plasticizer comprises between about 30% and about 80% by weight of the blend.
Claim 6
Dependent Claim
42 words
The process of claim 1 wherein the polyolefin component is a mixture of high-density polyethylene having a standard load melt index of substantially 0 and a high-density polyethylene having a standard load melt index greater than about 10 g. per 10 min.
Claim 7
Dependent Claim
27 words
The process of claim 5 wherein the polyethylene having a substantially 0 melt index comprises between about 30% and about 60% by weight of the polyolefin component.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein the plasticizer has a solubility in water of less than about 0.1% by weight at 30° C.
Claim 9
Dependent Claim
40 words
The process of claim 1 wherein the finely divided silica is hydrophilic, has a specific surface area greater than about 100 m 2 /g, as measured by nitrogen absorption, and a particle size between about 0.001 and about 0.1 micron.
Claim 10
Dependent Claim
21 words
The process of claim 1 wherein the plasticizer has between about 7 and about 11 carbon atoms in the oxo-alcohol moiety.
Claim 11
Dependent Claim
27 words
The process of claim 1 wherein the sheet, after contact with the water, is subjected to a surface treatment to remove any film of plasticizer adhering thereto.
Claim 12
Dependent Claim
20 words
The process of claim 1 wherein the temperature of the water is between about 20° C. and about 100° C.
Claim 13
Dependent Claim
22 words
The process of claim 1 wherein the plasticizer has a density sufficiently different from water to permit separation from water by decantation.
Claim 14
Dependent Claim
15 words
The process of claim 12 wherein the plasticizer is removed from the water by decantation.
Claim 15
Dependent Claim
116 words
The process of forming a microporous battery separator comprising: plasticating a blend comprising a polyolefin selected from the group consisting of homopolymers and copolymers of ethylene, propylene and buylene, and mixtures thereof; finely divided silica; and a substantially water-insoluble plasticizer selected from the group consisting of dialkyl phthalates and dialkyl adipates having between about 2 and about 11 carbon atoms in the oxo-alcohol moiety; forming a sheet from the plasticated blend; contacting the sheet with water for a period of time sufficient to remove an amount of the plasticizer from the sheet sufficient to render the sheet microporous; drying the sheet; and cutting the sheet into a size suitable for separating the plates in a battery.
Claim 16
Dependent Claim
116 words
The process of forming a microporous battery separator comprising: plasticating a blend comprising a polyolefin selected from the group consisting of homopolymers and copolymers of ethylene, propylene and buylene, and mixtures thereof; finely divided silica; and a substantially water-insoluble plasticizer selected from the group consisting of dialkyl phthalates and dialkyl adipates having between about 2 and about 11 carbon atoms in the oxo-alcohol moiety; forming a sheet from the plasticated blend; contacting the sheet with water for a period of time sufficient to remove an amount of the plasticizer from the sheet sufficient to render the sheet microporous; drying the sheet; and cutting the sheet into a size suitable for separating the plates in a battery.
References Cited (Backward Citations)
US3228896A
Cited
GB1044028A
Cited
GB1044502A
Cited
US3351495A
Cited
US3536796A
Cited
US3931067A
Cited
US4024323A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-02 | 1984-06-02 | 1984-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-02 | 1988-06-02 | 1988-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-02 | 1992-06-02 | 1992-12-02 | $7700.00 | Window Closed / Lapsed |