US5013784A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Internal resin-tackified acrylic polymers containing crosslinkable comonomers
Assignee: ExxonMobil Chemical Patents Inc
•
Filing: 1989-12-01
•
Granted: 1991-05-07
•
Expires: 2009-12-01
Abstract
Abstract Acrylic copolymer compositions which contain a tackifying hydrocarbon resin and a polyfunctional crosslinking monomer and the use of such composition in pressure-sensitive adhesives are described. The tackifying hydrocarbon resin is dissolved, as is the polyfunctional monomer, in a solution of alkyl(meth)acrylate and (meth) acrylic acid monomers and is present during the polymerization of the monomers to form a tackified acrylic copolymer.
Inventors
- 👤 Henry W. Yang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:19
CPC Classifications
C; C09; C09J; C09J151/00; C09J151/003; C08; C08F; C08F289/00; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/385
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
90 words
A tackified acrylic copolymer composition comprising: a hydrogenated hydrocarbon resin, having a molecular weight of from about 500 to about 5000 and an aromatic content of at least 10% by weight; and an acrylic copolymer formed by free radical initiated polymerization of a polymerizable monomer mixture emulsified in an aqueous medium, said monomer mixture comprising alkyl(meth)acrylate and (meth)acrylic acid monomers having dissolved therein from about 10 to about 100 parts of the resin per 100 parts polymerizable monomer, said polymerizable monomer mixture including an effective amount of a crosslinking monomer.
Claim 2
Dependent Claim
90 words
A tackified acrylic copolymer composition comprising: a hydrogenated hydrocarbon resin, having a molecular weight of from about 500 to about 5000 and an aromatic content of at least 10% by weight; and an acrylic copolymer formed by free radical initiated polymerization of a polymerizable monomer mixture emulsified in an aqueous medium, said monomer mixture comprising alkyl(meth)acrylate and (meth)acrylic acid monomers having dissolved therein from about 10 to about 100 parts of the resin per 100 parts polymerizable monomer, said polymerizable monomer mixture including an effective amount of a crosslinking monomer.
Claim 3
Dependent Claim
32 words
The tackified copolymer composition of claim 1 wherein the crosslinking monomer is present in an amount of from about 0.1 wt. % to about 2 wt. % of the total monomer mixture.
Claim 4
Dependent Claim
22 words
The tackified copolymer composition of claim 1 wherein the crosslinking comonomer is a (meth)acrylic diester of a poly(oxyethylene) glycol or poly(oxypropylene) gylcol.
Claim 5
Dependent Claim
17 words
The tackified copolymer composition of claim 1 wherein the crosslinking monomer is a (meth)acrylic ester of trimethylolpropane.
Claim 6
Dependent Claim
31 words
The tackified copolymer composition of claim 1 wherein the resin is a hydrogenated petroleum hydrocarbon resin having an aromatic content of from about 20 wt. % to about 65 wt. %.
Claim 7
Dependent Claim
55 words
The tackified copolymer composition of claim 1 wherein the polymerizable monomer mixture comprises form about 1 to about 15 wt. % of a (meth)acrylic acid, from 0 to about 50 wt. % of a lower alkyl (meth)acrylate ester and from about 25 wt. % to about 99 wt. % of an upper alkyl (meth)acrylate ester.
Claim 8
Dependent Claim
111 words
The tackified copolymer composition of claim 1 wherein the resin is a hydrogenated petroleum hydrocarbon resin having an average molecular weight of from about 100 to about 2500 and an aromatic content of from about 20 wt. % to about 65 wt. % and the polymerizable monomer mixture comprises from about 2 wt. % to about 6 wt. % acrylic acid, from about 10 wt. % to about 35 wt. % ethyl acrylate and from about 60 wt. % to about 88 wt. % 2-ethylhexyl acrylate, and the resin is present in the monomer mixture in amounts of from about 20 to about 55 parts resin per 100 parts monomers polymerized.
Claim 9
Dependent Claim
40 words
The tackified acrylic copolymer of claim 1 wherein the polymerizable monomer mixture includes one or more of acrylonitrile, vinyl acetate, vinylidene chloride, styrene and methyl styrene in a range of from 2-30 wt. % of the total polymerizable monomer mixture.
References Cited (Backward Citations)
US2809948A
Cited
US3377298A
Cited
JPS51125472A
Cited
JPS5226916A
Cited
JPS5374041A
Cited
US4113792A
Cited
JPS59213783A
Cited
JPS59227967A
Cited
US4645711A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-06 | 1994-11-05 | 1995-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-06 | 1998-11-05 | 1999-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-06 | 2002-11-05 | 2003-05-07 | $7700.00 | Window Closed / Lapsed |