Abstract
Abstract A polymer laminate produced by crosshead extrusion suitable for wear resistant applications such as a vehile glass run channel comprises a layer of a weather resistant rubber such as an ethylene-propylenediene (EPDM) rubber and a layer of a wear resistant thermoplastic such as polypropylene. The laminate is passed through an oven at an elevated temperature sufficient to cure the EPDM rubber, for example, at about 375° F., with ambient temperature cooling fluid being blown over the exposed surface of the polypropylene thermoplastic. The interior polypropylene surface or interface is heated by the EPDM rubber which is at a high temperature as a result of the heat of extrusion and heat generated by cure thereof. As a result, the polypropylene interior surface or interface melts and causes it to flow and form a mechanical bond with the EPDM rubber while the exposed surface as well as a substantial portion of the polypropylene is kept from melting by the cooling fluid. The EPDM rubber can be extruded in the form of a channel having a longitudinal web which supports and is bonded to the laminated polypropylene wear strip to form a glass run channel.
Inventors
- 👤 Mark L. Brooks
- 👤 Keith E. Wilson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:52
CPC Classifications
B; B32; B32B; B32B25/00; B32B25/04; B32B25/08; B60; B60J; B60J10/00; B60J10/15; B60J10/17; B60J10/70; B60J10/74; B60J10/79; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/2419; Y10T428/24198; Y10T428/31504; Y10T428/31826; Y10T428/31833; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/31917; Y10T428/31931
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process to form a laminate of a layer of a cured weather resistant rubber and a layer of thermoplastic comprising the steps of: extruding a layer of a curable weather resistant rubber having a first surface and a layer of the thermoplastic having a melting point of 350° F. or less and having a top surface and a bottom surface, said extruding step causing said bottom thermoplastic surface to form an interface with said curable weather resistant rubber first surface; bonding said curable weather resistant rubber and said thermoplastic layers by heating said weather resistant rubber layer to a curing temperature which is above the melting point of said thermoplastic layer, and cooling said top surface of said thermoplastic layer whereby only a portion of said thermoplastic layer at said interface is melted.
Claim 2
Dependent Claim
134 words
A process to form a laminate of a layer of a cured weather resistant rubber and a layer of thermoplastic comprising the steps of: extruding a layer of a curable weather resistant rubber having a first surface and a layer of the thermoplastic having a melting point of 350° F. or less and having a top surface and a bottom surface, said extruding step causing said bottom thermoplastic surface to form an interface with said curable weather resistant rubber first surface; bonding said curable weather resistant rubber and said thermoplastic layers by heating said weather resistant rubber layer to a curing temperature which is above the melting point of said thermoplastic layer, and cooling said top surface of said thermoplastic layer whereby only a portion of said thermoplastic layer at said interface is melted.
Claim 3
Dependent Claim
81 words
A process according to claim 1, wherein said cured weather resistant rubber layer is made from a styrene-butadiene rubber, a polychloroprene rubber, a nitrile-polyvinyl chloride rubber blend, and EPDM rubber, or combinations thereof, wherein said thermoplastic compound is polyethylene or polypropylene, wherein said rubber layer includes an enclosed channel, said channel including the rubber interface surface, and whereby said thermoplastic top surface is cooled by passing a fluid at a temperature below the melting point of said thermoplastic through said channel.
Claim 4
Dependent Claim
28 words
A process according to claim 2, including extruding said thermoplastic layer under pressure against said curable weather resistant rubber layer, and cooling the laminate subsequent to said bonding.
Claim 5
Dependent Claim
108 words
A process according to claim 3, wherein said weather resistant rubber is said EPDM rubber, wherein said EPDM rubber contains from about 45 percent by weight to about 75 percent by weight of ethylene units therein based upon the total weight of said ethylene and propylene units, wherein said EPDM rubber contains from about 4 percent to about 15 percent by weight of non-conjugated diene units based upon the total weight of said EPDM rubber, wherein said non-conjugated diene unit contains from about 5 to about 10 carbon atoms, and wherein said thermoplastic is polypropylene having a density of from about 0.9 to about 1.2 grams per cc.
Claim 6
Dependent Claim
20 words
A process according to claim 3, including melting less than 10 percent of the total amount of said thermoplastic layer.
Claim 7
Dependent Claim
36 words
A process according to claim 33, wherein said thermoplastic layer is heated by said heated and curing extruded weather resistant rubber layer, and wherein said thermoplastic layer is mechanically bonded to said weather resistant rubber layer.
Claim 8
Dependent Claim
20 words
A process according to claim 6, including melting less than 10 percent of the total amount of said thermoplastic layer.
Claim 9
Dependent Claim
111 words
A process according to claim 7, wherein said weather resistant rubber is said EPDM rubber, wherein said EPDM rubber layer contains from about 50 to about 60 percent by weight of ethylene units therein based upon the total weight of said ethylene and propylene units, wherein the said EPDM rubber contains from about 6 to about 12 percent by weight of non-conjugated diene units based upon the total weight of said EPDM rubber, wherein said non-conjugated diene of said EPDM rubber has from 6 to 9 carbon atoms, wherein said thermoplastic is said polypropylene, and wherein said polypropylene has the density of from about 0.9 to about 1.1 grams per cc.
Claim 10
Dependent Claim
65 words
A process according to claim 3, wherein said cured weather resistant rubber is said EPDM rubber, wherein said thermoplastic is said polypropylene, wherein said EPDM rubber has a ratio from about 50 to about 60 percent of ethylene units by weight of the ethylene and propylene units therein, and wherein said polypropylene has a density of from about 0.9 to about 1.2 grams per cc.
Claim 11
Dependent Claim
36 words
A process according to claim 9, wherein said thermoplastic layer is heated by said heated and curing extruded weather resistant rubber layer, and wherein said thermoplastic layer is mechanically bonded to said weather resistant rubber layer.
Claim 12
Dependent Claim
20 words
A process according to claim 10, including melting less than 10 percent of the total amount of said thermoplastic layer.
Claim 13
Dependent Claim
108 words
A process according to claim 10, wherein said weather resistant rubber is said EPDM rubber, wherein said EPDM rubber contains from about 45 percent by weight to about 75 percent by weight of ethylene units therein based upon the total weight of said ethylene and propylene units, wherein said EPDM rubber contains from about 4 percent to about 15 percent by weight of non-conjugated diene units based upon the total weight of said EPDM rubber, wherein said non-conjugated diene unit contains from about 5 to about 10 carbon atoms, and wherein said thermoplastic is polypropylene having a density of from about 0.9 to about 1.2 grams per cc.
References Cited (Backward Citations)
US3193428A
Cited
US3659983A
Cited
US3706173A
Cited
US3624964A
Cited
US4296062A
Cited
US3918206A
Cited
US4104098A
Cited
US4596734A
Cited
US4538380A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-06 | 1994-11-05 | 1995-05-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-06 | 1998-11-05 | 1999-05-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-06 | 2002-11-05 | 2003-05-07 | $7700.00 | Window Closed / Lapsed |