Thermoplastic interpolymers and their use in mixtures of polyamide and styrene copolymers and/or graft polymers
Assignee: Bayer AG
•
Filing: 1989-08-07
•
Granted: 1991-04-23
•
Expires: 2009-08-07
Abstract
Abstract The invention relates to thermoplastic interpolymers having a certain chemical composition and to their use in thermoplastic molding compounds of polyamides and styrene copolymers and/or graft polymers for the production of improved blends of polyamides and styrene copolymers and/or graft polymers, particularly ABS polymers, having homogeneous surfaces and improved mechanical properties. The interpolymers themselves are produced by compounding of polyamides and copolymers based on styrenes and/or acrylonitrile and/or (meth)acrylates with primary or secondary alcohols and at least one ester of (meth)acrylic acid with a tertiary C4-10 alcohol in the melt. The interpolymers act as compatibility promoters in the blends and lead to a surprising improvement in a number of properties of thermoplastic molding compounds.
Inventors
- 👤 Uwe Westeppe
- 👤 Karl-Erwin Piejko
- 👤 Christian Lindner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:08
CPC Classifications
C; C08; C08L; C08L77/00; C08G; C08G81/00; C08G81/02; C08G81/024; C08G81/028
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
166 words
Interpolymers of (A) from 40 to 80% by weight polyamides with or without partial crystallinity and (B) from 20 to 60% by weight thermoplastic copolymers or mixtures of several thermoplastic copolymers of (B1) monomers comprising (B1.1) at least 15% by weight based on (B) of at least one monomer selected from the group consisting of styrenes and α-methylstyrenes which are unsubstituted or substituted by at least one haloalkyl or halogen, and (B1.2) from 0 to 50% by weight based on (B), of other monomers selected from the group consisting of vinyl acetate, acrylonitrile, methacrylonitrile, and acrylate or methacrylate esters of primary or secondary C 1-10 alcohols, and (B2) from 0.5 to 35% by weight based on (B) of at least one ester of acrylic or methacrylic acid with tertiary C 4 -C 10 alcohols prepared by homogenization of components (A) and (B) in the melt in standard mixing and kneading units at temperatures above the melting point of the higher-melting component until the interpolymers are formed.
Claim 2
Dependent Claim
166 words
Interpolymers of (A) from 40 to 80% by weight polyamides with or without partial crystallinity and (B) from 20 to 60% by weight thermoplastic copolymers or mixtures of several thermoplastic copolymers of (B1) monomers comprising (B1.1) at least 15% by weight based on (B) of at least one monomer selected from the group consisting of styrenes and α-methylstyrenes which are unsubstituted or substituted by at least one haloalkyl or halogen, and (B1.2) from 0 to 50% by weight based on (B), of other monomers selected from the group consisting of vinyl acetate, acrylonitrile, methacrylonitrile, and acrylate or methacrylate esters of primary or secondary C 1-10 alcohols, and (B2) from 0.5 to 35% by weight based on (B) of at least one ester of acrylic or methacrylic acid with tertiary C 4 -C 10 alcohols prepared by homogenization of components (A) and (B) in the melt in standard mixing and kneading units at temperatures above the melting point of the higher-melting component until the interpolymers are formed.
Claim 3
Dependent Claim
100 words
Interpolymers as claimed in claim 1, characterized in that thermoplastic copolymers (B) of (B1.1) at least 30% by weight styrene or α-methylstyrene or both and (B1.2) from 0 to 50% by weight acrylonitrile, methyl methacrylate, n-butyl methacrylate, cyclohexyl methacrylate or vinylacetate and (B2) from 1 to 20% by weight tertiary (meth)acrylates corresponding to the following formula ##STR2## in which R=H, CH 3 and R 1 , R 2 , R 3 =alkyl so that the sum of the carbon atoms in R 1 , R 2 and R 3 is from 3 to 9, are used to form the interpolymers.
Claim 4
Dependent Claim
31 words
Interpolymers as claimed in claim 1, characterized in that thermoplastic copolymers (B) of (1.1) α-methylstyrene or styrene and (B1.2) acrylonitrile or methylacrylate and (B2) tert.-butyl(meth)acrylate are used to form the interpolymers.
Claim 5
Dependent Claim
65 words
Interpolymers as claimed in claim 1, characterized in that thermoplastic copolymers (B) of terpolymers containing (B1.1) at least 30% by weight styrenes and (B1.2) 10 to 50% by weight acrylonitrile, (B2) and 1 to 20% by weight tert.-butyl (meth)acrylate, the percentages by weight totalling 100, based on the sum total of the % by weight components of component (B), are used to form the interpolymers.
Claim 6
Dependent Claim
34 words
Interpolymers as claimed in claim 1, characterized in that copolymers (B) having intrinsic viscosities of from 0.2 to 2 (as measured in dl/g at room temperature in DMF) are used to form the interpolymers.
Claim 7
Dependent Claim
16 words
Interpolymers as claimed in claim 4 wherein component (B1.1) is at least 45% by weight styrene.
Claim 8
Dependent Claim
16 words
Interpolymers as claimed in claim 4 wherein component (B1.2) is 20 to 45% by weight acrylonitrile.
Claim 9
Dependent Claim
15 words
Interpolymers as claimed in claim 4 wherein component (B2) is 1.5 to 15% by weight.
Claim 10
Dependent Claim
27 words
Interpolymers as claimed in claim 5 wherein the intrinsic viscosity of copolymers (B) is from 0.3 to 1.5, as measured in dl/g at room temperature in DMF.
Claim 11
Dependent Claim
110 words
Interpolymers of (A) from 40 to 80% by weight polyamides with or without partial crystallinity and (B) from 20 to 60% by weight based on (B) thermoplastic copolymers or mixtures of several thermoplastic copolymers of (B1) monomers comprising (B1.1) at least 45% by weight based on (B) styrenes or α-methylstyrene, and (B1.2) from 20 to 45% by weight based on (B), of acrylonitrile, and (B2) from 1.5 to 15% by weight based on (B) of tert. butyl acrylate, prepared by homogenization of components (A) and (B) in the melt in standard mixing and kneading units at temperatures above the melting point of the higher-melting component until the interpolymers are formed.
Claim 12
Dependent Claim
110 words
Interpolymers of (A) from 40 to 80% by weight polyamides with or without partial crystallinity and (B) from 20 to 60% by weight based on (B) thermoplastic copolymers or mixtures of several thermoplastic copolymers of (B1) monomers comprising (B1.1) at least 45% by weight based on (B) styrenes or α-methylstyrene, and (B1.2) from 20 to 45% by weight based on (B), of acrylonitrile, and (B2) from 1.5 to 15% by weight based on (B) of tert. butyl acrylate, prepared by homogenization of components (A) and (B) in the melt in standard mixing and kneading units at temperatures above the melting point of the higher-melting component until the interpolymers are formed.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-22 | 1994-10-22 | 1995-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-22 | 1998-10-22 | 1999-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-22 | 2002-10-22 | 2003-04-23 | $7700.00 | Window Closed / Lapsed |