CMOS and bipolar fabrication process using selective epitaxial growth scalable to below 0.5 micron
Assignee: National Semiconductor Corp
•
Filing: 1989-03-07
•
Granted: 1991-04-23
•
Expires: 2009-03-07
Abstract
Abstract A CMOS and bipolar fabrication process wherein a silicon dioxide layer initially formed over a silicon substrate is etched for forming separate collector and base/emitter regions for a bipolar device, and PMOS and NMOS regions for corresponding PMOS and NMOS devices. Buried layer implants are performed using a minimum number of masks, and then an epitaxial layer is grown over the exposed portions of the silicon substrate. The silicon dioxide walls between the devices provide full dielectric isolation between the devices, as well as between the collector and base/emitter regions of the bipolar device. Nonetheless, the oxide wall between the collector and base/emitter of the bipolar device is sufficiently small to allow the buried layer implants to joint under the wall for forming a conventional buried layer for the bipolar device. Because of the oxide walls, the minimum distance between devices may be 0.5 microns or less.
Inventors
- 👤 Juliana Manoliu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:40
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/10; H10D62/113; H10D62/115; H10D62/13; H10D62/137; H10D84/00; H10D84/01; H10D84/0107; H10D84/0109; H10D84/02; H10D84/03; H10D84/038; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/27; H10P14/271; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/018; H10W10/10; H10W15/00; H10W15/01; Y; Y10; Y10S; Y10S148/00; Y10S148/011; Y10S148/026; Y10S148/031
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
135 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; etching a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate: implanting a first conductivity type impurity into the first and second regions of the substrate: growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions; and heating the substrate for causing the first conductivity type impurity in the first and second regions of the substrate to join beneath the first wall.
Claim 2
Independent Claim
135 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; etching a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate: implanting a first conductivity type impurity into the first and second regions of the substrate: growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions; and heating the substrate for causing the first conductivity type impurity in the first and second regions of the substrate to join beneath the first wall.
Claim 3
Dependent Claim
25 words
The method according to claim 1 further comprising the steps of: implanting first conductivity type impurity into the epitaxial layer prior to heating the substrate.
Claim 4
Dependent Claim
52 words
The method according to claim 2 wherein the heating step further comprises the step of heating the substrate for causing the first conductivity type impurity in the first and second regions of the epitaxial layer to contact the first conductivity type impurity in the corresponding first and second region of the substrate.
Claim 5
Dependent Claim
31 words
The method according to claim 3 wherein the epitaxial layer growing step further comprises the step of simultaneously growing the epitaxial layer over the first and second regions of the substrate.
Claim 6
Dependent Claim
37 words
The method according to claim 4 further comprising the steps of forming a collector of a bipolar transistor in the first epitaxial region; and forming a base and emitter of a bipolar transistor in the second region.
Claim 7
Dependent Claim
48 words
The method according to claim 4 further comprising the step of etching a third opening in the silicon dioxide layer for exposing a third annular region encircling the first and second regions of the substrate; and implanting second conductivity type impurity into the third region of the substrate.
Claim 8
Dependent Claim
57 words
The method according to claim 6 further comprising the steps of: growing an epitaxial layer over the third region of the substrate simultaneously with the growing of the epitaxial layer over the first and second regions of the substrate for forming a third, annular epitaxial region: and implanting second conductivity type impurity into the third epitaxial region.
Claim 9
Dependent Claim
40 words
The method according to claim 7 further comprising the step of heating the substrate for causing the second conductivity type impurity in the third region of the substrate to contact the second conductivity type impurity in the third epitaxial region.
Claim 10
Dependent Claim
44 words
The method according to claim 7 further comprising the steps of: etching a fourth opening in to the silicon dioxide layer, the fourth opening exposing a fourth region of the substrate: and implanting first conductivitY type impurity into the fourth region of the substrate.
Claim 11
Dependent Claim
85 words
The method according to claim 8 further comprising the steps of: growing an epitaxial layer over the fourth region of the substrate simultaneously with the growing of the epitaxial layer over the first and second regions of the substrate for forming a fourth epitaxial region; implanting first conductivity type impurity into the fourth epitaxial region; and heating the substrate for causing the first conductivity type impurity in the fourth region of the substrate to contact the first conductivity type impurity in the fourth epitaxial region.
Claim 12
Dependent Claim
23 words
The method according to claim 9 further comprising the step of forming a first channel type MOS device in the fourth epitaxial region.
Claim 13
Dependent Claim
85 words
The method according to claim 8 further comprising the steps of: growing an epitaxial layer over the fourth region of the substrate simultaneously with the growing of the epitaxial layer over the first and second region of the substrate for forming a fourth epitaxial region; implanting second conductivity type impurity into the fourth epitaxial region; and heating the substrate for causing the second conductivity type impurity in the fourth region of the substrate to contact the second conductivity type impurity in the fourth epitaxial layer.
Claim 14
Dependent Claim
23 words
The method according to claim 12 further comprising the step of forming a first channel type MOS device in the fourth epitaxial region.
Claim 15
Dependent Claim
40 words
The method according to claim 13 further comprising the steps of: etching a fifth opening into the silicon dioxide layer, the fifth opening exposing a fifth region of the substrate; and implanting first conductivity type impurity into the fifth region.
Claim 16
Dependent Claim
85 words
The method according to claim 14 further comprising the steps of: growing an epitaxial layer over the fifth region of the substrate simultaneously with the growing of the epitaxial layer over the first and second regions of the substrate for forming a fifth epitaxial region; implanting first conductivity type impurity into the fifth epitaxial region; and heating the substrate for causing the first conductivity type impurity in the fifth region of the substrate to contact the first conductivity type impurity in the fifth epitaxial region.
Claim 17
Dependent Claim
23 words
The method according to claim 15 further comprising the step of forming a second channel type MOS device in the fifth epitaxial region.
Claim 18
Independent Claim
152 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching, with a first mask, a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; thereafter, implanting a first conductivity type impurity into the first region of the substrate; thereafter, etching, with a second mask, a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate, wherein the width of the first wall between the first and second regions is less than one micron; thereafter, implanting a second conductivity type impurity into the second regions of the substrate; and heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second regions of the substrate.
Claim 19
Independent Claim
152 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching, with a first mask, a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; thereafter, implanting a first conductivity type impurity into the first region of the substrate; thereafter, etching, with a second mask, a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate, wherein the width of the first wall between the first and second regions is less than one micron; thereafter, implanting a second conductivity type impurity into the second regions of the substrate; and heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second regions of the substrate.
Claim 20
Dependent Claim
37 words
The method according to claim 17 further comprising the step of, prior to the heating step, growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions.
Claim 21
Dependent Claim
35 words
The method according to claim 17 wherein the heating step further comprises the step of heating the substrate for causing the first conductivity type impurity to diffuse into the substrate for forming a buried layer.
Claim 22
Dependent Claim
47 words
The method according to claim 17 wherein the heating step further comprises the step of heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second epitaxial regions of the substrate for forming corresponding first and second active regions.
Claim 23
Dependent Claim
37 words
The method according to claim 20 further comprising the steps of, prior to the heating step: implanting first conductivity type impurity into the first epitaxial region: and implanting second conductivity type impurity into the second epitaxial region.
Claim 24
Dependent Claim
61 words
The method according to claim 21 wherein the heating step comprises the step of heating the substrate for causing the first and second conductivity type impurities in the first and second epitaxial regions and the first and second impurities in the first and second regions of the substrate to diffuse toward each other for forming corresponding first and second active regions.
Claim 25
Dependent Claim
45 words
The method according to claim 22 wherein the epitaxial layer growing step comprises the step of growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions that are coplanar with the silicon dioxide layer.
Claim 26
Independent Claim
153 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching, with a first mask, a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; thereafter, implanting a first conductivity type impurity into the first region of the substrate; thereafter, etching, with a second mask, a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate, wherein the width of the first wall between the first and second regions is not greater than 0.5 microns; thereafter, implanting a second conductivity type impurity into the second regions of the substrate; and heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second regions of the substrate.
Claim 27
Independent Claim
153 words
A method of constructing a semiconductor structure comprising the steps of: growing a layer of silicon dioxide on a silicon substrate; etching, with a first mask, a first opening in the silicon dioxide layer, the first opening exposing a first region of the substrate; thereafter, implanting a first conductivity type impurity into the first region of the substrate; thereafter, etching, with a second mask, a second opening in the silicon dioxide layer in close proximity to the first opening and separated therefrom by a first wall, the second opening exposing a second region of the substrate, wherein the width of the first wall between the first and second regions is not greater than 0.5 microns; thereafter, implanting a second conductivity type impurity into the second regions of the substrate; and heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second regions of the substrate.
Claim 28
Dependent Claim
37 words
The method according to claim 24 further comprising the step of, prior to the heating step, growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions.
Claim 29
Dependent Claim
35 words
The method according to claim 25 wherein the heating step further comprises the step of heating the substrate for causing the first conductivity type impurity to diffuse into the substrate for forming a buried layer.
Claim 30
Dependent Claim
47 words
The method according to claim 25 wherein the heating step further comprises the step of heating the substrate for causing the first and second conductivity type impurities to diffuse into the first and second epitaxial regions of the substrate for forming corresponding first and second active regions.
Claim 31
Dependent Claim
37 words
The method according to claim 27 further comprising the steps of, prior to the heating step: implanting first conductivity type impurity into the first epitaxial region; and implanting second conductivity type impurity into the second epitaxial region.
Claim 32
Dependent Claim
61 words
The method according to claim 28 wherein the heating step comprises the step of heating the substrate for causing the first and second conductivity type impurities in the first and second epitaxial regions and the first and second impurities in the first and second regions of the substrate to diffuse toward each other for forming corresponding first and second active regions.
Claim 33
Dependent Claim
45 words
The method according to claim 20 wherein the epitaxial layer growing step comprises the step of growing an epitaxial layer over the first and second regions of the substrate for forming corresponding first and second epitaxial regions that are coplanar with the silicon dioxide layer.
References Cited (Backward Citations)
US3305913A
Cited
US3635772A
Cited
US3698077A
Cited
US3788904A
Cited
US4101350A
Cited
US4099998A
Cited
US4004954A
Cited
US4177095A
Cited
JPS5848968A
Cited
JPS58131748A
Cited
US4551909A
Cited
JPS62204576A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-22 | 1994-10-22 | 1995-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-22 | 1998-10-22 | 1999-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-22 | 2002-10-22 | 2003-04-23 | $7700.00 | Window Closed / Lapsed |