Assignee: NXP BV
•
Filing: 1988-07-11
•
Granted: 1991-04-16
•
Expires: 2008-07-11
Abstract
Abstract A plasma etching process using HBr is set forth in which etching of silicon and polysilicon in IC manufacture is significantly improved by the high etching selectivity for either silicon and polysilicon to both oxides and photoresist materials.
Inventors
- 👤 Len-Yan Tsou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:23
CPC Classifications
H; H10; H10P; H10P95/00; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
102 words
In a method of manufacturing semiconductor IC devices by etching comprising the steps of (a) forming a composite structure by (i) providing a silicon substrate, (ii) forming a thin layer of silicon oxide on said silicon substrate, (iii) forming a polysilicon layer on said oxide, (iv) forming a mask of a photoresist on at least parts of said polysilicon layer, (b) removing any surface oxides from said polysilicon layer with an oxide etching plasma, and (c) then exposing the composite structure to a plasma containing only hydrogen bromide to selectively etch said polysilicon layer relative to said photoresist and said silicon oxide.
Claim 2
Dependent Claim
102 words
In a method of manufacturing semiconductor IC devices by etching comprising the steps of (a) forming a composite structure by (i) providing a silicon substrate, (ii) forming a thin layer of silicon oxide on said silicon substrate, (iii) forming a polysilicon layer on said oxide, (iv) forming a mask of a photoresist on at least parts of said polysilicon layer, (b) removing any surface oxides from said polysilicon layer with an oxide etching plasma, and (c) then exposing the composite structure to a plasma containing only hydrogen bromide to selectively etch said polysilicon layer relative to said photoresist and said silicon oxide.
Claim 3
Dependent Claim
89 words
A method according to claim 1, further comprising after said steps (b) and (c) the steps of removing said photoresist from said composite structure, forming at least a second polysilicon layer on said composite structure, forming at least a second photoresist on at least parts of said second polysilicon layer, removing any surface oxides from said second polysilicon layer with said oxide etching plasma, and then exposing said second polysilicon layer to said hydrogen bromide plasma, wherein said second polysilicon layer is selectively etched relative to said second photoresist.
Claim 4
Dependent Claim
24 words
A method according to claim 2, wherein said oxide etching plasma is selected from the group consisting of freon, silicon tetrachloride and boron trichloride.
Claim 5
Dependent Claim
14 words
A method according to claim 2, wherein said polysilicon layer is doped or undoped.
Claim 6
Dependent Claim
28 words
A method according to claim 1, wherein said hydrogen bromide selectively etches said polysilicon layer relative to said mask at an etch rate ratio of at least 60:1.
Claim 7
Dependent Claim
23 words
A method according to claim 5, wherein said polysilicon layer is selectively etched relative to said silicon oxide at a rate of 100:1.
Claim 8
Dependent Claim
24 words
A method according to claim 1, wherein said oxide etching plasma is selected from the group consisting of freon, silicon tetrachloride and boron trichloride.
Claim 9
Dependent Claim
14 words
A method according to claim 1, wherein said polysilicon layer is doped or undoped.
Claim 10
Dependent Claim
23 words
A method according to claim 1, wherein said polysilicon layer is selectively etched relative to said silicon oxide at a ratio of 100:1.
Claim 11
Independent Claim
78 words
A method of manufacturing semiconductors by selectively etching a layer of a silicon-bearing material relative to a mask, comprising the steps of: providing a patterned mask of a photoresist over a layer of silicon-bearing material to expose only areas to be etched, removing any surface oxides from said silicon-bearing layer with an oxide etching plasma, and then exposing said silicon-bearing layer to a plasma containing only hydrogen bromide to selectively etch said silicon-bearing layer relative to said mask.
Claim 12
Independent Claim
78 words
A method of manufacturing semiconductors by selectively etching a layer of a silicon-bearing material relative to a mask, comprising the steps of: providing a patterned mask of a photoresist over a layer of silicon-bearing material to expose only areas to be etched, removing any surface oxides from said silicon-bearing layer with an oxide etching plasma, and then exposing said silicon-bearing layer to a plasma containing only hydrogen bromide to selectively etch said silicon-bearing layer relative to said mask.
Claim 13
Dependent Claim
27 words
A method according to claim 10, wherein said silicon-bearing material is selected from the group consisting of silicon, doped or undoped polysilicon, tantalum silicide, and titanium silicide.
Claim 14
Dependent Claim
24 words
A method according to claim 10, wherein said oxide etching plasma is selected from the group consisting of freon, silicon tetrachloride, and boron trichloride.
Claim 15
Dependent Claim
28 words
A method according to claim 10, wherein said hydrogen bromide selectively etches said silicon-bearing layer relative to said mask at an etch rate ratio of at least 60:1.
References Cited (Backward Citations)
US4432132A
Cited
US4490209A
Cited
US4490209B1
Cited
US4490209B2
Cited
US4784720A
Cited
US4778563A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-15 | 1994-10-15 | 1995-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-15 | 1998-10-15 | 1999-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-15 | 2002-10-15 | 2003-04-16 | $7700.00 | Window Closed / Lapsed |