Transistor manufacturing process using three-step base doping
Assignee: NXP BV
•
Filing: 1989-11-20
•
Granted: 1991-04-09
•
Expires: 2009-11-20
Abstract
Abstract In a transistor fabrication process, the use of a three-step base doping technique enables the characteristics of a vertical bipolar transistor to be controllably reproduced at highly optimal values from run to run. Insulating spacers (52A) are employed in forming a self-aligned base contact zone (58B). A shallow emitter (46) is created by outdiffusion from a patterned non-monocrystalline semiconductor layer (38A) that serves as the emitter contact. The fabrication process is compatible with the largely simultaneous manufacture of an insulated-gate field-effect transistor of the lightly doped drain type.
Inventors
- 👤 Jan L. De Jong
- 👤 Jacob G. DeGroot
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:48
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/01; H10D10/051; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D62/00; H10D62/10; H10D62/17; H10D62/177; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0113; H10D84/00; H10D84/01; H10D84/0107; H10D84/0109; H10D84/02; H10D84/03; H10D84/038; Y; Y10; Y10S; Y10S148/00; Y10S148/009; Y10S148/124
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
316 words
A method of fabricating a bipolar transistor from a monocrystalline semiconductor body that comprises a major region of a first conductivity type located along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the major region to convert a surface-adjoining portion into a primary zone of the second conductivity type; creating a patterned electrically conductive layer above the primary zone so as to contact part of its upper surface; introducing a main impurity of the first conductivity type into the primary zone through part of its upper surface to convert a surface-adjoining portion into an emitter of the first conductivity type; introducing an intermediate dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion as an intermediate zone of the second conductivity type using the patterned layer and any electrically insulating material along its sides as a shield for blocking the intermediate dopant from passing through the directly underlying section of the upper surface of the major region; forming electrically insulating spacers along the sides of the patterned layer to a mean lateral width greater than that of any electrically insulating material located along the sides of the patterned layer during the previous step; and introducing a further dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion as a base contact zone of the second conductivity type laterally separated from the emitter using the patterned layer and spacers as a shield for blocking the further dopant from passing through the directly underlying section of the upper surface of the major region, the intermediate zone being continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 2
Independent Claim
316 words
A method of fabricating a bipolar transistor from a monocrystalline semiconductor body that comprises a major region of a first conductivity type located along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the major region to convert a surface-adjoining portion into a primary zone of the second conductivity type; creating a patterned electrically conductive layer above the primary zone so as to contact part of its upper surface; introducing a main impurity of the first conductivity type into the primary zone through part of its upper surface to convert a surface-adjoining portion into an emitter of the first conductivity type; introducing an intermediate dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion as an intermediate zone of the second conductivity type using the patterned layer and any electrically insulating material along its sides as a shield for blocking the intermediate dopant from passing through the directly underlying section of the upper surface of the major region; forming electrically insulating spacers along the sides of the patterned layer to a mean lateral width greater than that of any electrically insulating material located along the sides of the patterned layer during the previous step; and introducing a further dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion as a base contact zone of the second conductivity type laterally separated from the emitter using the patterned layer and spacers as a shield for blocking the further dopant from passing through the directly underlying section of the upper surface of the major region, the intermediate zone being continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 3
Dependent Claim
56 words
A method as in claim 1 wherein the base comprises the base contact zone, an intrinsic base portion consisting largely of that part of the primary zone directly below the emitter, and a base connection zone consisting largely of that part of the intermediate and primary zones extending between the intrinsic portion and the contact zone.
Claim 4
Dependent Claim
30 words
A method as in claim 2 wherein the step of introducing the main impurity of the first conductivity type is performed by outdiffusing the main impurity from the patterned layer.
Claim 5
Dependent Claim
18 words
A method as in claim 3 wherein the first and second conductivity types respectively are N-type and P-type.
Claim 6
Dependent Claim
53 words
A method as in claim 3 including, prior to the step of creating the patterned layer, the step of introducing a preliminary impurity of the first conductivity type into the major region through its upper surface to an average depth therebelow greater than that of the initial dopant of the second conductivity type.
Claim 7
Dependent Claim
32 words
A method as in claim 5 including, subsequent to the step of forming the spacers, the step of heating the body and adjoining material for 1-20 seconds at 1,000° C. or more.
Claim 8
Independent Claim
319 words
A method of fabricating a bipolar transistor from a monocrystalline semiconductor body that comprises a major region of a first conductivity type located along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the major region through its upper surface to convert a surface-adjoining portion of it into a primary zone of the second conductivity type; creating a patterned electrically conductive non-monocrystalline semiconductor layer above the primary zone so as to contact part of its upper surface, the patterned layer containing a main impurity of the first conductivity type; diffusing part of the main impurity of the first conductivity type from the patterned layer into the primary zone to convert a portion of the primary zone into an emitter of the first conductivity type; ion implanting an intermediate dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion of it as an intermediate zone of the second conductivity type using the patterned layer and any electrically insulating material along its sides as an implantation shield; forming electrically insulating spacers along the sides of the patterned layer such that the mean lateral width of the spacers is greater than the mean lateral width of any electrically insulating material located along the sides of the patterned layer during the ion implantation of the intermediate dopant; and ion implanting a further dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion of it as a base contact zone of the second conductivity type laterally separated from the emitter using the patterned layer and spacers as an implantation shield, the intermediate zone being continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 9
Independent Claim
319 words
A method of fabricating a bipolar transistor from a monocrystalline semiconductor body that comprises a major region of a first conductivity type located along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the major region through its upper surface to convert a surface-adjoining portion of it into a primary zone of the second conductivity type; creating a patterned electrically conductive non-monocrystalline semiconductor layer above the primary zone so as to contact part of its upper surface, the patterned layer containing a main impurity of the first conductivity type; diffusing part of the main impurity of the first conductivity type from the patterned layer into the primary zone to convert a portion of the primary zone into an emitter of the first conductivity type; ion implanting an intermediate dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion of it as an intermediate zone of the second conductivity type using the patterned layer and any electrically insulating material along its sides as an implantation shield; forming electrically insulating spacers along the sides of the patterned layer such that the mean lateral width of the spacers is greater than the mean lateral width of any electrically insulating material located along the sides of the patterned layer during the ion implantation of the intermediate dopant; and ion implanting a further dopant of the second conductivity type into the major region through part of its upper surface to establish a surface-adjoining portion of it as a base contact zone of the second conductivity type laterally separated from the emitter using the patterned layer and spacers as an implantation shield, the intermediate zone being continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 10
Dependent Claim
56 words
A method as in claim 7 wherein the base comprises the base contact zone, an intrinsic base portion consisting substantially of that part of the primary zone located directly below the emitter, and a base connection zone consisting substantially of that part of intermediate and primary zones extending between the intrinsic portion and the contact zone.
Claim 11
Dependent Claim
98 words
A method as in claim 7 wherein the step of creating the patterned layer involves: providing the upper surface of the body and any overlying material with a blanket non-monocrystalline semiconductor layer doped with the main impurity of the first conductivity type; removing substantially the entire thickness of portions of the blanket layer situated to the sides of the intended location for the emitter; and continuing the removal step by etching into the major region along its upper surface to remove at least 500 angstroms of material situated to the sides of the intended location for the emitter.
Claim 12
Dependent Claim
41 words
A method as in claim 7 wherein the semiconductor body has a substantially flat lower surface, the ion implantation of each of the intermediate and further dopants being performed in a direction substantially perpendicular to the lower surface of the body.
Claim 13
Dependent Claim
54 words
A method as in claim 7 including, prior to the step of creating the patterned layer, the step of ion implanting a preliminary impurity of the first conductivity type into the major region through its upper surface to an average depth therebelow greater than that of the initial dopant of the second conductivity type.
Claim 14
Dependent Claim
80 words
A method as in claim 7 wherein: the step of introducing the initial dopant of the second conductivity type is done by ion implantation; and, prior to creating the patterned layer, a preliminary impurity of the first conductivity type is ion implanted into the major region through its upper surface at an energy sufficient to enable the preliminary impurity to reach a peak concentration at an average depth greater than that at which the initial dopant reaches its peak concentration.
Claim 15
Dependent Claim
32 words
A method as in claim 7 including, subsequent to the step of forming the spacers, the step of heating the body and adjoining material for 1-20 seconds at 1,000° C. or more.
Claim 16
Dependent Claim
18 words
A method as in claim 7 wherein the first and second conductivity types respectively are N-type and P-type.
Claim 17
Independent Claim
417 words
A method of fabricating a bipolar transistor and a field-effect transistor from a monocrystalline semiconductor body that comprises first and second major regions of a first conductivity type spaced laterally apart from each other along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the first region through its upper surface to convert a surface-adjoining portion of the first region into a primary zone of the second conductivity type; providing an electrically insulating layer along the upper surface of the second region; creating a first patterned electrically conductive non-monocrystalline semiconductor layer above the primary zone so as to contact part of its upper surface, the first patterned layer doped with a main impurity of the first conductivity type; creating a second patterned non-monocrystalline semiconductor layer on the upper surface of part of the insulating layer; ion implanting an intermediate dopant of the second conductivity type into the major regions through parts of their then-existing upper surfaces to establish a surface-adjoining portion of the first region as an intermediate zone of the second conductivity type and to establish a pair of laterally separated surface-adjoining portions of the second region as auxiliary source/drain zones of the second conductivity type using the patterned layers and any electrically insulating material along their sides as an implantation shield; forming electrically insulating spacers along the sides of the patterned layers to a greater mean lateral width than that of any electrically insulating material lying along the sides of the patterned layers during the ion implantation of the intermediate dopant; diffusing part of the main impurity of the first conductivity type from the first patterned layer into the primary zone to convert a portion of it into an emitter of the first conductivity type; and ion implanting a further dopant of the second conductivity type into the major regions through parts of their then-existing upper surfaces to establish a surface-adjoining portion of the first region as a base contact zone of the second conductivity type laterally separated from the emitter and to establish a pair of laterally separated surface-adjoining portions of the second region as main source/drain zones of the second conductivity type respectively continuous with the auxiliary source/drain zones using the spacers and the patterned layers as an implantation shield, whereby the intermediate zone is continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 18
Independent Claim
417 words
A method of fabricating a bipolar transistor and a field-effect transistor from a monocrystalline semiconductor body that comprises first and second major regions of a first conductivity type spaced laterally apart from each other along an upper surface of the body, the method comprising the steps of: introducing an initial dopant of a second conductivity type opposite to the first conductivity type into the first region through its upper surface to convert a surface-adjoining portion of the first region into a primary zone of the second conductivity type; providing an electrically insulating layer along the upper surface of the second region; creating a first patterned electrically conductive non-monocrystalline semiconductor layer above the primary zone so as to contact part of its upper surface, the first patterned layer doped with a main impurity of the first conductivity type; creating a second patterned non-monocrystalline semiconductor layer on the upper surface of part of the insulating layer; ion implanting an intermediate dopant of the second conductivity type into the major regions through parts of their then-existing upper surfaces to establish a surface-adjoining portion of the first region as an intermediate zone of the second conductivity type and to establish a pair of laterally separated surface-adjoining portions of the second region as auxiliary source/drain zones of the second conductivity type using the patterned layers and any electrically insulating material along their sides as an implantation shield; forming electrically insulating spacers along the sides of the patterned layers to a greater mean lateral width than that of any electrically insulating material lying along the sides of the patterned layers during the ion implantation of the intermediate dopant; diffusing part of the main impurity of the first conductivity type from the first patterned layer into the primary zone to convert a portion of it into an emitter of the first conductivity type; and ion implanting a further dopant of the second conductivity type into the major regions through parts of their then-existing upper surfaces to establish a surface-adjoining portion of the first region as a base contact zone of the second conductivity type laterally separated from the emitter and to establish a pair of laterally separated surface-adjoining portions of the second region as main source/drain zones of the second conductivity type respectively continuous with the auxiliary source/drain zones using the spacers and the patterned layers as an implantation shield, whereby the intermediate zone is continuous with the primary zone and the base contact zone to form a base of the second conductivity type.
Claim 19
Dependent Claim
56 words
A method as in claim 15 wherein the base comprises the base contact zone, an intrinsic base portion consisting substantially of that part of the primary zone located directly below the emitter, and a base connection zone consisting substantially of that part of intermediate and primary zones extending between the intrinsic portion and the contact zone.
Claim 20
Dependent Claim
78 words
A method as in claim 15 wherein the steps of creating the patterned layers involve: depositing a blanket non-monocrystalline semiconductor layer over the then-existing upper surfaces of the first region and the insulating layer; introducing the main impurity of the first conductivity type into the portion of the blanket layer above the first region; and removing substantially the entire thickness of portions of the blanket layer situated to the sides of the intended locations for the patterned layers.
Claim 21
Dependent Claim
36 words
A method as in claim 17 wherein the step of removing includes etching into the first region along its then-existing upper surface to remove material situated to the sides of the intended location for the emitter.
Claim 22
Dependent Claim
35 words
A method as in claim 17 wherein the steps of ion implanting the intermediate and further dopants of the second conductivity type include ion implanting at least one of them into the second patterned layer.
Claim 23
Dependent Claim
175 words
A method as in claim 15 wherein the steps of introducing the initial dopant of the second conductivity type, providing the insulating layer, and creating the patterned layers involve: forming first and second insulating layers respectively along the then-existing upper surfaces of the first and second regions; depositing an initial blanket layer of non-monocrystalline semiconductive material on the first and second insulating layers and on any material between them; ion implanting the initial dopant of the second conductivity type selectively into the first region but not into the second region; removing the portion of the initial blanket layer over the first insulating layer; removing the first insulating layer; forming a further blanket layer of non-monocrystalline semiconductor material over the then-existing upper surface of the primary zone and over the remainder of the initial blanket layer; introducing the main impurity of the first conductivity type into at least a portion of the further blanket layer above the first region; and removing non-monocrystalline semiconductor material situated to the sides of the intended locations for the patterned layers.
References Cited (Backward Citations)
JPS59114861A
Cited
JPS6050920A
Cited
JPS60103669A
Cited
US4539744A
Cited
US4587718A
Cited
GB2168845A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-08 | 1994-10-08 | 1995-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-08 | 1998-10-08 | 1999-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-08 | 2002-10-08 | 2003-04-09 | $7700.00 | Window Closed / Lapsed |