Lightwave guide produced from special substrate glasses by ion exchange against CS+ ions
Assignee: Schott AG
•
Filing: 1989-11-16
•
Granted: 1991-04-02
•
Expires: 2009-11-16
Abstract
Abstract Production of mono- or multimodal lightwave guides from special substrate glasses of the glass system SiO2-B2O3-Al2O3- K2O-F-, with partial exchange of the Li+, Na+, and/or K+ ions present in the glass against Cs+ ions, the substrate glasses having the following compositions (in mol.-%): SiO2 45-72, B2O3 8-25, Al2O3 1-25, Li2O 0-1, Na2O 0-2, K2O 6-18, MO 0-1 (MO=MgO, CaO, SrO, BaO, ZnO, PbO), in which a portion of the O- ions present in the glass are replaced by 1-15 mol % F- ions.
Inventors
- 👤 Ludwig Ross
- 👤 Werener Schumann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 23:03
CPC Classifications
C; C03; C03C; C03C21/00; C03C21/001; C03C21/002; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C3/00; C03C3/04; C03C3/062; C03C3/064; G; G02; G02B; G02B6/00; G02B6/10; G02B6/12; G02B6/13; G02B6/134; G02B6/1345
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
123 words
Lightwave guide, characterized in that it is produced from a substrate glass consisting essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
45-72
B.sub.2 O.sub.3
8-25
Al.sub.2 O.sub.3
1-25
Li.sub.2 O
0-1
Na.sub.2 O
0-2
K.sub.2 O
6-18
MO 0-1
______________________________________ (MO=MgO, CaO, SrO, BaO, ZnO, PbO), in which a portion of the O 2- ions present in the glass is replaced by 1-15 mol % F - ions to facilitate diffusion of Cs + ions therein, and in which a lightwave conductive zone has been produced by incorporating Cs + ions into the substrate glass by an ion-exchange of K + , Li + and/or Na + ions against Cs + ions to effect a refractive index gradient within the glass.
Claim 2
Dependent Claim
123 words
Lightwave guide, characterized in that it is produced from a substrate glass consisting essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
45-72
B.sub.2 O.sub.3
8-25
Al.sub.2 O.sub.3
1-25
Li.sub.2 O
0-1
Na.sub.2 O
0-2
K.sub.2 O
6-18
MO 0-1
______________________________________ (MO=MgO, CaO, SrO, BaO, ZnO, PbO), in which a portion of the O 2- ions present in the glass is replaced by 1-15 mol % F - ions to facilitate diffusion of Cs + ions therein, and in which a lightwave conductive zone has been produced by incorporating Cs + ions into the substrate glass by an ion-exchange of K + , Li + and/or Na + ions against Cs + ions to effect a refractive index gradient within the glass.
Claim 3
Dependent Claim
88 words
Lightwave guide according to claim 1, wherein the substrate glass additionally contains a combined total of at most 5 mol % of at least one oxide selected from the group consisting of TiO 2 , ZrO 2 , P 2 O 5 , GeO 2 , Y 2 O 3 , La 2 O 3 , Nb 2 O 5 , Ta 2 O 5 , WO 3 , SnO 2 , As 2 O 3 , Sb 2 O 3 , and Bi 2 O 3 .
Claim 4
Dependent Claim
21 words
Lightwave guide according to claim 1, wherein the substrate glass contains less than 10 mol % Al 2 O 3 .
Claim 5
Dependent Claim
19 words
Lightwave guide according to claim 1, wherein the substrate glass contains 10-25 mol % Al 2 O 3 .
Claim 6
Dependent Claim
18 words
Lightwave guide according to claim 1, wherein the substrate glass additionally contains 0.1-2 mol % Cs 2 O.
Claim 7
Dependent Claim
35 words
Lightwave guide according to claim 1, wherein the molar ratio of Al 2 O 3 :M 2 O (M 2 O=Li 2 O, Na 2 O, K 2 O, Cs 2 O) is about 0.8-1.2.
Claim 8
Dependent Claim
16 words
Lightwave guide according to claim 1, wherein the lightwave conducting zone is below the glass surface.
Claim 9
Dependent Claim
57 words
Lightwave guide according to claim 1, wherein the substrate glass consists essentially of the following composition, in mol %: ______________________________________
SiO.sub.2 53-63
B.sub.2 O.sub.3 8-19
Al.sub.2 O.sub.3
5-20
K.sub.2 O 12-18
F.sup.- 5-7.5
Na.sub.2 O + Li.sub.2 O
0-2
______________________________________ wherein the K 2 O content is at least 80% of the Al 2 O 3 content.
Claim 10
Dependent Claim
50 words
Lightwave guide according to claim 8, wherein the substrate glass consists essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
59.3
B.sub.2 O.sub.3
18.0
Al.sub.2 O.sub.3
5.2
K.sub.2 O
17.5
______________________________________ in which a portion of the oxygen ions are replaced by the addition of 6.8% F - ions.
Claim 11
Dependent Claim
56 words
Lightwave guide according to claim 8, wherein the substrate glass consists essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
54.2
B.sub.2 O.sub.3
18.5
Al.sub.2 O.sub.3
9.9
K.sub.2 O
15.6
Na.sub.2 O
1.4
Li.sub.2 O
0.4
______________________________________ in which a portion of the oxygen ions are replaced by the addition of 6.5% F - ions.
Claim 12
Dependent Claim
18 words
Lightwave guide according to claim 10, wherein the lightwave conducting zone is 20-30 um below the glass surface.
Claim 13
Dependent Claim
50 words
Lightwave guide according to claim 8, wherein the substrate, glass consists essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
69.9
B.sub.2 O.sub.3
12.0
Al.sub.2 O.sub.3
12.5
K.sub.2 O
12.5
______________________________________ in which a portion of the oxygen ions are replaced by the addition of 6.26% F - ions.
Claim 14
Dependent Claim
53 words
Lightwave guide according to claim 8, wherein the substrate, glass consists essentially of the following composition, in mol %: ______________________________________
SiO.sub.2
53.5
B.sub.2 O.sub.3
8.03
Al.sub.2 O.sub.3
19.5
K.sub.2 O
18.0
Na.sub.2 O
1.0
______________________________________ in which a portion of the oxygen ions are replaced by the addition of 7.22% F - ions.
Claim 15
Dependent Claim
18 words
Lightwave guide according to claim 13, wherein the lightwave conducting zone is 20-30 um below the glass surface.
Claim 16
Dependent Claim
23 words
Lightwave guide according to claim 1, wherein the K 2 O content is at least 80% of the Al 2 O 3 content.
Claim 17
Dependent Claim
27 words
Lightwave guide according to claim 15, wherein the molar ratio Al 2 O 3 :M 2 O, wherein M 2 O is total alkali metal, is 0.8-1.2.
References Cited (Backward Citations)
US3790430A
Cited
US3923486A
Cited
US3941474A
Cited
US3647406A
Cited
US3607322A
Cited
US3784386A
Cited
US4166795A
Cited
US3827785A
Cited
US4099834A
Cited
US4038090A
Cited
US4452508A
Cited
US4236930A
Cited
US4367012A
Cited
US4472030A
Cited
JPS577402A
Cited
US4375312A
Cited
US4462663A
Cited
US4562161A
Cited
US4526874A
Cited
JPS6015607A
Cited
US4565791A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-01 | 1994-10-01 | 1995-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-01 | 1998-10-01 | 1999-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-01 | 2002-10-01 | 2003-04-02 | $7700.00 | Window Closed / Lapsed |