US5003549A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Semiconductor laser
Assignee: Mitsubishi Electric Corp
•
Filing: 1989-07-12
•
Granted: 1991-03-26
•
Expires: 2009-07-12
Abstract
Abstract A semiconductor laser particularly adapted for operation in the self-pulsation mode and method for production thereof. A central mesa is formed in the upper cladding layer and normally requires relatively thick sections at either side of the mesa in order to form a waveguide of sufficient thickness to cause self-pulsation operation. In order to control the thickness of the upper cladding layer bounding the mesa, the mesa is first formed by etching the regions bounding the mesa to relatively thin sections capable of ready gauging by optical interferometry. A composite upper cladding layer is then formed by utilizing MOCVD crystal growth techniques to form a buffer layer on the upper cladding layer bounding the mesa, the buffer layer having an aluminum content about the same as the aluminum content of the AlGaAs upper cladding layer. The composite layer functions as a comparatively thick waveguide which can be formed to the necessary thickness with adequate accuracy to provide a high yield when producing self-pulsation lasers according to the present invention.
Inventors
- 👤 Shigeru Mitsui
- 👤 Ryo Hattori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:01
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/20; H01S5/22; H01S5/223; H01S5/2231; H01S5/06; H01S5/065; H01S5/0658; H01S5/30; H01S5/32; H01S5/323; H01S5/32308; H01S5/32316; Y; Y10; Y10S; Y10S148/00; Y10S148/025; Y10S148/095
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
234 words
A semiconductor laser comprising: a substrate supporting lower and upper cladding layers separated by an active layer, the cladding layers being of opposite conductivity types; the cladding and active layers all being of AlGaAs, with the aluminum molar proportion of the active layer being lower than that of the cladding layers; a mesa etched in the upper cladding layer forming a central stripe bounded by a pair of etched regions, the etched regions of the upper cladding layer being sufficiently thin to be readily gauged by optical interferometrical techniques; a buffer layer of AlGaAs having substantially the same aluminum molar proportion as the upper cladding layer, the buffer layer being grown over the etched portions of the upper cladding layer to form a composite AlGaAs layer over the active layer of a predetermined thickness, the predetermined thickness being sufficient to cause the laser when completed and energized to oscillate in the self-pulsation mode; and a current blocking layer grown over the buffer layer, a contact layer on the current blocking layer, and electrodes in contact with the contact layer and substrate, respectively, for injecting inject carriers into the portion of the active layer under said mesa, thereby to cause lasing operation guided by the composite AlGaAs layer, said lasing operation being conducted in the self-pulsation mode due to the relationship between the thickness of said composite layer and the width of the mesa stripe.
Claim 2
Dependent Claim
234 words
A semiconductor laser comprising: a substrate supporting lower and upper cladding layers separated by an active layer, the cladding layers being of opposite conductivity types; the cladding and active layers all being of AlGaAs, with the aluminum molar proportion of the active layer being lower than that of the cladding layers; a mesa etched in the upper cladding layer forming a central stripe bounded by a pair of etched regions, the etched regions of the upper cladding layer being sufficiently thin to be readily gauged by optical interferometrical techniques; a buffer layer of AlGaAs having substantially the same aluminum molar proportion as the upper cladding layer, the buffer layer being grown over the etched portions of the upper cladding layer to form a composite AlGaAs layer over the active layer of a predetermined thickness, the predetermined thickness being sufficient to cause the laser when completed and energized to oscillate in the self-pulsation mode; and a current blocking layer grown over the buffer layer, a contact layer on the current blocking layer, and electrodes in contact with the contact layer and substrate, respectively, for injecting inject carriers into the portion of the active layer under said mesa, thereby to cause lasing operation guided by the composite AlGaAs layer, said lasing operation being conducted in the self-pulsation mode due to the relationship between the thickness of said composite layer and the width of the mesa stripe.
Claim 3
Dependent Claim
15 words
The semiconductor laser according to claim 1 in which the mesa is a forward mesa.
Claim 4
Dependent Claim
23 words
The semiconductor laser according to claim 1 in which the buffer layer is of the same conductivity type as the upper cladding layer.
Claim 5
Dependent Claim
222 words
A semiconductor laser comprising: a substrate supporting lower and upper cladding layers separated by an active layer, the cladding layers being of opposite conductivity types; the cladding and active layers all being of AlGAs, with the aluminum molar proportion of the active layer being lower than that of the cladding layers; a mesa etched in the upper cladding layer forming a central stripe bounded by a pair of etched regions, the etched regions of the upper cladding layer being no greater than about 0.3 microns in thickness; a buffer layer of AlGaAs grown over the etched portions of the upper cladding layer to form a composite AlGaAs layer over the active layer of a predetermined thickness greater than 0.3 microns, the predetermined thickness being sufficient to cause the laser when completed and energized to oscillate in the self-pulsation mode; and a current blocking layer grown over the buffer layer, a contact layer on the current blocking layer, and electrodes in contact with the contact layer and the substrate, respectively, for injecting carriers into the portion of the active layer under said mesa, thereby to cause lasing operation guided in part by the composite AlGaAs layer, said lasing operation being conducted in the self-pulsation mode due to the relationship between the thickness of said composite layer and the width of the mesa stripe.
Claim 6
Dependent Claim
222 words
A semiconductor laser comprising: a substrate supporting lower and upper cladding layers separated by an active layer, the cladding layers being of opposite conductivity types; the cladding and active layers all being of AlGAs, with the aluminum molar proportion of the active layer being lower than that of the cladding layers; a mesa etched in the upper cladding layer forming a central stripe bounded by a pair of etched regions, the etched regions of the upper cladding layer being no greater than about 0.3 microns in thickness; a buffer layer of AlGaAs grown over the etched portions of the upper cladding layer to form a composite AlGaAs layer over the active layer of a predetermined thickness greater than 0.3 microns, the predetermined thickness being sufficient to cause the laser when completed and energized to oscillate in the self-pulsation mode; and a current blocking layer grown over the buffer layer, a contact layer on the current blocking layer, and electrodes in contact with the contact layer and the substrate, respectively, for injecting carriers into the portion of the active layer under said mesa, thereby to cause lasing operation guided in part by the composite AlGaAs layer, said lasing operation being conducted in the self-pulsation mode due to the relationship between the thickness of said composite layer and the width of the mesa stripe.
Claim 7
Dependent Claim
15 words
The semiconductor laser according to claim 4 in which the mesa is a forward mesa.
Claim 8
Dependent Claim
23 words
The semiconductor laser according to claim 4 in which the buffer layer is of the same conductivity type as the upper cladding layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-03-25 | 1994-09-24 | 1995-03-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-03-25 | 1998-09-24 | 1999-03-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-03-25 | 2002-09-24 | 2003-03-26 | $7700.00 | Window Closed / Lapsed |