Hydrocarbon conversion with octane-enhancing catalysts
Assignee: Chevron USA Inc
•
Filing: 1990-04-16
•
Granted: 1991-03-19
•
Expires: 2010-04-16
Abstract
Abstract Novel hydrocarbon conversion catalysts and methods for their preparation are disclosed. The catalysts are particularly appropriate for the conversion of hydrocarbon feeds to high octane gasoline, while increasing light cycle oil and decreasing heavy cycle oil yield. The catalyst comprises a zeolite, a cogelled silica-alumina matrix, and clay.
Inventors
- 👤 Theresa A. Pecoraro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:48
CPC Classifications
C; C10; C10G; C10G11/00; C10G11/02; C10G11/04; C10G11/05; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/08; B01J29/084; B01J35/00; B01J35/30; B01J35/31; B01J35/32; B01J35/50; B01J35/51; B01J35/60; B01J35/61; B01J35/615; B01J35/63; B01J35/633; B01J35/638; B01J35/64; B01J35/647; B01J35/66; B01J37/00; B01J37/0009; B01J37/0027; B01J37/0045; B01J2229/00; B01J2229/30; B01J2229/42; B01J35/80
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
145 words
A catalyst composition for increasing the octane and yield of gasoline produced from a fluid catalytic cracking process, comprising: a. large pore zeolite; b. natural or synthetic clay; and, c. an amorphous silica-alumina matrix, said matrix prepared by steps comprising preparing a mixture comprising a silica sol and an aluminum salt while maintaining the pH of said mixture below about 4, and precipitating a cogel from said mixture by adjusting the pH; wherein said composition is prepared by steps comprising: (i) combining said zeolite, clay, and cogel, provided that the pH of said cogel or said combination containing said cogel is adjusted to between about 4 and 7, and conditions are controlled to induce syneresis and viscosity reduction, and further provided that when said zeolite is introduced into said combination the pH is between about 3 and 7; and (ii) forming said combination into particles.
Claim 2
Dependent Claim
145 words
A catalyst composition for increasing the octane and yield of gasoline produced from a fluid catalytic cracking process, comprising: a. large pore zeolite; b. natural or synthetic clay; and, c. an amorphous silica-alumina matrix, said matrix prepared by steps comprising preparing a mixture comprising a silica sol and an aluminum salt while maintaining the pH of said mixture below about 4, and precipitating a cogel from said mixture by adjusting the pH; wherein said composition is prepared by steps comprising: (i) combining said zeolite, clay, and cogel, provided that the pH of said cogel or said combination containing said cogel is adjusted to between about 4 and 7, and conditions are controlled to induce syneresis and viscosity reduction, and further provided that when said zeolite is introduced into said combination the pH is between about 3 and 7; and (ii) forming said combination into particles.
Claim 3
Dependent Claim
24 words
The composition as claimed in claim 1 wherein said catalyst composition has meso and macro pore sizes, high surface area, and high pore volume.
Claim 4
Dependent Claim
56 words
The composition as claimed in claim 2 wherein said micropore sizes are <20Å in diameter, and said mesopore sizes are between 20 to 500Å in diameter and said macro pore sizes are >500Å, said surface area is between about 150 and 450 m 2 /g and said pore volume is between about 0.4 and 1.2 cc/g.
Claim 5
Dependent Claim
60 words
The composition as claimed in claim 2 wherein after exposure to a temperature greater than about 1200° F. and steam, said pore size is retained between 40 to 100Å in diameter, and 100 to 1000Å in diameter, said surface area is between about 100 and 300 m 2 /g and said pore volume is less or equal to 0.7 cc/g.
Claim 6
Dependent Claim
23 words
The composition as claimed in claim 1 wherein said faujasitic or Y-type zeolite comprises between 5 and 50% of the composition by weight.
Claim 7
Dependent Claim
23 words
The composition as claimed in claim 4 wherein said faujasitic or Y-type zeolite comprises between 20 and 40% of the composition by weight.
Claim 8
Dependent Claim
104 words
The composition as claimed in claim 5 wherein said zeolite is selected from the group consisting of: a. a low sodium, super stable Y-type zeolite having a unit cell constant of less than about 24.50Å and an Na 2 O content of less than about 0.5% by weight, b. a low sodium, stabilized Y-type zeolite having a unit cell constant of less than 24.60Å and an Na 2 O content of less than about 0.5% by weight, and c. a stabilized Y-type zeolite having a unit cell constant of less than 24.60Å and an Na 2 O of less than about 3.0% by weight.
Claim 9
Dependent Claim
21 words
The composition as claimed in claim 7 wherein said zeolite is selected from the group consisting of LZ-Y20, LZ-Y82, and LZ-Y72.
Claim 10
Dependent Claim
20 words
The composition as claimed in claim 7 or 8 wherein said zeolite is partially or totally ion-exchanged with polyvalent ions.
Claim 11
Dependent Claim
19 words
The composition as claimed in claim 9 wherein said zeolite is partially or totally ion-exchanged with rare earth ions.
Claim 12
Dependent Claim
45 words
The composition as claimed in claim 5 wherein said zeolite is a low-sodium, ammonium Y-type zeolite having a cell constant less than 24.75Å and a sodium content, as Na 2 O, of less than 3.0% by weight, and which becomes stabilized under FCC reactor conditions.
Claim 13
Dependent Claim
12 words
The composition as claimed in claim 11 wherein said zeolite is LZ-Y82.
Claim 14
Dependent Claim
18 words
The composition as claimed in claim 11 or 12 wherein said zeolite is partially ion-exchanged with polyvalent ions.
Claim 15
Dependent Claim
17 words
The composition as claimed in claim 13 wherein said zeolite is partially ion-exchanged with rare earth ions.
Claim 16
Dependent Claim
22 words
The composition as claimed in claim 1 wherein said cogelled, silica-alumina matrix is comprised of silica between 10 and 90% by weight.
Claim 17
Dependent Claim
17 words
The composition as claimed in claim 15 wherein said silica is between 45 and 65% by weight.
Claim 18
Dependent Claim
15 words
The composition as claimed in claim 16 wherein said silica is about 60% by weight.
Claim 19
Dependent Claim
150 words
The composition as claimed in claim 1 wherein said cogelled, silica-alumina matrix is prepared by the method which comprises: a. mixing a silicate solution with an aqueous solution of an acid aluminum salt and an acid, to form an acidified silica sol in said aluminum salt solution, and adjusting said silica sol/aluminum salt solution mixture to a pH in the range of about 1 to 4; b. slowly adding sufficient base with vigorous stirring, to said acidified silica sol/aluminum salt solution mixture to form a cogel slurry of silica and alumina, and to adjust said slurry to a pH in the range of about 5 to 9; c. aging said cogel slurry for up to about 3 hours at ambient to 95° C.; d. adjusting the pH of said cogel slurry to about 5 to 9; e. recovering a cogelled mass from said slurry; and f. washing said cogelled mass.
Claim 20
Dependent Claim
16 words
The composition as claimed in claim 18 wherein said base in step b. comprises ammonium hydroxide.
Claim 21
Dependent Claim
21 words
The composition as claimed in claim 1 wherein said cogel matrix comprises between 20 and 90% of the composition by weight.
Claim 22
Dependent Claim
21 words
The composition as claimed in claim 20 wherein said cogel matrix comprises between 50 and 60% of the composition by weight.
Claim 23
Dependent Claim
39 words
The composition as claimed in claim 1 or 18 wherein said cogel matrix has a surface area of between about 200 and 450 m 2 /g, and a MAT activity of between about 20 and 80 wt % conversion.
Claim 24
Dependent Claim
23 words
The composition as claimed in claim 22 wherein said cogel matrix has a MAT activity of between 45 and 80 wt % conversion.
Claim 25
Dependent Claim
19 words
The composition as claimed in claim 18 wherein said cogel matrix is partially or totally ion-exchanged with polyvalent ions.
Claim 26
Dependent Claim
20 words
The composition as claimed in claim 24 wherein said cogel matrix is partially or totally ion-exchanged with rare earth ions.
Claim 27
Dependent Claim
27 words
The composition as claimed in claim 1 wherein said clay is selected from the group consisting of talc, smectite, montmorillonite, vermiculite, mica, chlorite, kaolinites, sepiolite, and attapulgite.
Claim 28
Dependent Claim
13 words
The composition as claimed in claim 26 wherein said clay is kaolin-type clay.
Claim 29
Dependent Claim
12 words
The composition as claimed in claim 27 wherein said clay is kaolin.
Claim 30
Dependent Claim
12 words
The composition as claimed in claim 26 wherein said clay is sepiolite.
Claim 31
Dependent Claim
19 words
The composition as claimed in claim 29 wherein said clay is Spanish sepiolite or a material of similar characteristics.
Claim 32
Dependent Claim
19 words
The composition as claimed in claim 1 wherein said clay comprises 40% or less of the composition by weight.
Claim 33
Dependent Claim
20 words
The composition as claimed in claim 31 wherein said clay comprises between 10 and 25% of the composition by weight.
Claim 34
Dependent Claim
24 words
The composition as claimed in claim 1 wherein said clay comprises an aqueous solution of said clay having a pH greater than about 7.
Claim 35
Dependent Claim
24 words
The composition as claimed in claim 26 wherein said clay is pretreated to reduce the amount of extraneous sodium or iron in the clay.
Claim 36
Dependent Claim
40 words
The composition as claimed in claim 1 or 26 wherein said catalyst also comprises a porous inorganic oxide, wherein said inorganic oxide is combined with said zeolite-cogel mixture or said zeolite-cogel-clay mixture, prior to adjusting the pH in step (iii).
Claim 37
Dependent Claim
25 words
The composition as claimed in claim 35 wherein said porous inorganic oxide is selected from the Groups III, IV, V metal oxides, and mixtures thereof.
Claim 38
Dependent Claim
23 words
The composition as claimed in claim 1 or 35 wherein said porous oxide comprises between 0 and 25% of the composition by weight.
Claim 39
Dependent Claim
24 words
The composition as claimed in claim 1 wherein said aging takes place at ambient temperature for a period of between 1 and 24 hours.
Claim 40
Dependent Claim
26 words
The composition as claimed in claim 1 wherein said aging takes place at a temperature <95° C. for a period between about 1 and 3 hours.
Claim 41
Dependent Claim
41 words
The composition as claimed in claim 1 wherein said essentially spherical particles of said catalyst composition have an average particle size of from about 40 to 90 microns, a bulk density of from 0.4 to 0.9 g/cc, and are attrition resistant.
Claim 42
Dependent Claim
18 words
The composition as claimed in claim 40 wherein said average particle size is from 60 to 80 microns.
Claim 43
Dependent Claim
27 words
The composition as claimed in claim 1 wherein said particles are formed by spray-drying after homogenizing the slurry, preferably by passing said slurry through a colloid mill.
Claim 44
Dependent Claim
23 words
The composition as claimed in claim 42 wherein said particles which are formed by spray-drying are exchanged with polyvalent ions subsequent to spray-drying.
Claim 45
Dependent Claim
19 words
The composition as claimed in claim 43 wherein said particles are exchanged with rare earth ions subsequent to spray-drying.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-03-18 | 1994-09-17 | 1995-03-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-03-18 | 1998-09-17 | 1999-03-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-03-18 | 2002-09-17 | 2003-03-19 | $7700.00 | Window Closed / Lapsed |