Alkyd resins and the use thereof for high solids coatings

Claim 2

An air-drying high solids modified alkyd resin having a number average molecular weight of less than about 6,000 consisting essentially of the condensation polymerization product of: (a) from about 45 to 70 parts by weight of at least one drying oil fatty acid comprising at least 52% by weight of linoleic acid and/or linolenic acid, (b) from about 4 to 15 parts by weight of at least one dibasic aromatic acid or anhydride, (c) from about 10 to 28 parts by weight of at least one polyol selected from the group consisting of pentaerythritol, dipentaerythritol and mixtures thereof, (d) from about 4 to 15 parts by weight of at least one unsaturated monocarboxylic acid, and (e) from about 4 to 10 parts by weight of an unsaturated monohydric alcohol.

Claim 3

The air drying high solids modified alkyd resin of claim 1 further characterized as having a number average molecular weight of less than 4,000 and a hydroxyl number of from about 20 to 90.

Claim 4

The air drying high solids modified alkyd resin of claim 2 further characterized in that the unsaturated monocarboxylic acid of crotonic acid.

Claim 5

The air drying high solids modified alkyd resin of claim 3 further characterized in that the unsaturated monohydric alcohol is trimethylolpropane diallyl ether present in amounts of from about 4 to 10 parts by weight.

Claim 6

The air drying high solids modified alkyd resin of claim 3 further characterized in that the drying oil fatty acid contains from about 52% to 70% by weight of linoleic and/or linolenic acid and the dibasic aromatic acid is isophthalic acid.

Claim 7

A process of preparing an air drying high solids modified alkyd resin having a number average molecular weight of less than about 6,000 and consisting essentially of the condensation polymerization product at temperatures ranging up to about 475° F. of (a) from about 45 to 70 parts by weight of at least one drying oil fatty acid comprising at least 52% by weight of linoleic and/or linolenic acid, (b) from about 4 to 15 parts by weight of at least one dibasic aromatic acid or anhydride, (c) from about 10 to 28 parts by weight of at least one polyol selected from the group consisting of pentaerythritol, dipentaerythritol and mixtures thereof, (d) from about 4 to 15 parts by weight of at least one unsaturated monocarboxylic acid, (e) from about 4 to 10 parts by weight of an unsaturated monohydric alcohol.

Claim 8

A process of preparing an air drying high solids modified alkyd resin having a number average molecular weight of less than about 6,000 and consisting essentially of the condensation polymerization product at temperatures ranging up to about 475° F. of (a) from about 45 to 70 parts by weight of at least one drying oil fatty acid comprising at least 52% by weight of linoleic and/or linolenic acid, (b) from about 4 to 15 parts by weight of at least one dibasic aromatic acid or anhydride, (c) from about 10 to 28 parts by weight of at least one polyol selected from the group consisting of pentaerythritol, dipentaerythritol and mixtures thereof, (d) from about 4 to 15 parts by weight of at least one unsaturated monocarboxylic acid, (e) from about 4 to 10 parts by weight of an unsaturated monohydric alcohol.

Claim 9

The process of claim 6 further characterized in that the unsaturated monocarboxylic acid is added to the condensation reaction at temperatures ranging up to about 380° F.

Claim 10

The process of claim 6 further characterized in that the unsaturated monocarboxylic acid is crotonic acid and the dibasic aromatic acid is isophthalic acid or isophthalic anhydride.

Claim 11

The process of claim 6 further characterized in that the unsaturated monohydric alcohol is trimethylolpropane diallyl ether present in amounts ranging from about 4 to 10 parts by weight.

Claim 12

An air drying high solids alkyd coating comprising about 20 to 60 parts by weight of a fatty acid modified alkyd resin, 5 to 20 parts by weight of an organic solvent, 15 to 40 parts by weight of an inorganic pigment, 0 to 30 parts by weight of an inorganic extender, and up to 10 parts by weight of a drier consisting essentially of a metal drier selected from the group consisting of salts of cobalt, copper, lead, zirconium, calcium, nickel, zinc, tin, iron, and mixtures thereof; said alkyd resin having a number average molecular weight of less than about 6,000 and consisting essentially of the condensation polymerization product of: (a) from about 45 to 70 parts by weight of at least one drying oil fatty acid comprising at least 52% by weight of linoleic and/or linolenic acid, (b) from about 4 to 15 parts by weight of at least one dibasic aromatic acid or anhydride, (c) from about 10 to 28 parts by weight of at least one polyol selected from the group consisting of pentaerythritol, dipentaerythritol and mixtures thereof, (d) from about 4 to 15 parts by weight of at least one unsaturated monocarboxylic acid, and (e) from about 4 to 10 parts by weight of an unsaturated monohydric alcohol.

Claim 13

An air drying high solids alkyd coating comprising about 20 to 60 parts by weight of a fatty acid modified alkyd resin, 5 to 20 parts by weight of an organic solvent, 15 to 40 parts by weight of an inorganic pigment, 0 to 30 parts by weight of an inorganic extender, and up to 10 parts by weight of a drier consisting essentially of a metal drier selected from the group consisting of salts of cobalt, copper, lead, zirconium, calcium, nickel, zinc, tin, iron, and mixtures thereof; said alkyd resin having a number average molecular weight of less than about 6,000 and consisting essentially of the condensation polymerization product of: (a) from about 45 to 70 parts by weight of at least one drying oil fatty acid comprising at least 52% by weight of linoleic and/or linolenic acid, (b) from about 4 to 15 parts by weight of at least one dibasic aromatic acid or anhydride, (c) from about 10 to 28 parts by weight of at least one polyol selected from the group consisting of pentaerythritol, dipentaerythritol and mixtures thereof, (d) from about 4 to 15 parts by weight of at least one unsaturated monocarboxylic acid, and (e) from about 4 to 10 parts by weight of an unsaturated monohydric alcohol.

Claim 14

The high solids alkyd coating of claim 10 further characterized in that the unsaturated monocarboxylic acid is crotonic acid and the dibasic aromatic acid or anhydride is isophthalic acid or the anhydride.

Claim 15

The air drying air solids alkyd coating of claim 10 further characterized in that the inorganic pigment is titanium dioxide.

Claim 16

The air drying high solids alkyd coating of claim 10 further characterized in that the alkyd resin has a number average molecular weight of less than 4,000 and a hydroxyl number of from about 20 to 90.

Claim 17

The high solids alkyd coating of claim 13 further characterized in that the unsaturated monocarboxylic acid is crotonic acid.

Claim 18

The air drying high solids alkyd coating of claim 14 further characterized in that the unsaturated monohydric alcohol is trimethylolpropane diallyl ether present in amounts ranging from about 4 to 10 parts by weight.

Claim 19

The air drying high solids alkyd coating of claim 15 further characterized in that the drying oil fatty acid contains from about 52% to 70% by weight of linoleic and/or linolenic acid and the dibasic aromatic acid is isophthalic acid.