Preparation of catalyst for oxidation of carbon monoxide

Claim 2

A process for preparing a composition of matter, being effective as catalyst for the reaction of CO with O 2 to CO 2 at about 20°-30° C., comprising iridium metal, iron oxide and titania, said process comprising the steps of (a) impregnating a titania-containing support material with at least one iron compound and at least one iridium carbonyl compound; (b) substantially drying the material obtained in step (a); and (c) treating the substantially dried material obtained in step (b) with a reducing gas under such conditions as to activate said substantially dried material and to obtain said composition of matter.

Claim 3

A preparation process in accordance with claim 1, wherein said titania-containing support material is a titania-coated porous ceramic material.

Claim 4

A preparation process in accordance with claim 1, wherein said titania-containing support material consists essentially of titania.

Claim 5

A preparation process in accordance with claim 1, wherein said at least one iron compound is iron(III) acetylacetonate and said at least one iridium carbonyl compound is Ir 4 (CO) 12 .

Claim 6

A preparation process in accordance with claim 1, wherein step (a) is carried out with one solution containing said at least one iron compound and said at least one iridium carbonyl compound.

Claim 7

A preparation process in accordance with claim 1, wherein step (a) is carried out by impregnation of said support material with a solution comprising at least one iron compound, heating the obtained iron-impregnated support material under such conditions as to substantially dry said iron-impregnated support material, and then impregnating said substantially dried iron-impregnated support material with a solution comprising at least one iridium carbonyl compound.

Claim 8

A preparation process in accordance with claim 6, wherein said heating of the iron-impregnated support material is carried out at about 100°-500° C. under such conditions as to at least partially convert said at least one iron compound to iron oxide.

Claim 9

A preparation process in accordance with claim 1, wherein drying step (b) is carried out at about 30° to about 200° C.

Claim 10

A preparation process in accordance with claim 1, wherein reducing step (c) is carried out with hydrogen gas at a temperature of about 0° to about 600° C.

Claim 11

A preparation process in accordance with claim 1, wherein the composition of matter obtained in step (c) contains about 0.1-10 weight-% Ir and about 0.1-15 weight-% Fe.

Claim 12

A composition of matter, being effective as catalyst for the reaction of CO and O 2 to CO 2 at about 20°-30° C., comprising iridium metal, iron oxide and titania, said composition of matter having been prepared by a process comprising the steps of (a) impregnating a titania-containing support material with at least one iron compound and at least one iridium carbonyl compound; (b) substantially drying the material obtained in step (a); and (c) treating the substantially dried material obtained in step (b) with a reducing gas under such conditions as to activate said substantially dried material and to obtain said composition of matter.

Claim 13

A composition of matter, being effective as catalyst for the reaction of CO and O 2 to CO 2 at about 20°-30° C., comprising iridium metal, iron oxide and titania, said composition of matter having been prepared by a process comprising the steps of (a) impregnating a titania-containing support material with at least one iron compound and at least one iridium carbonyl compound; (b) substantially drying the material obtained in step (a); and (c) treating the substantially dried material obtained in step (b) with a reducing gas under such conditions as to activate said substantially dried material and to obtain said composition of matter.

Claim 14

A composition of matter in accordance with claim 11, wherein said titania-containing support material is a titania-coated porous ceramic material.

Claim 15

A composition of matter in accordance with claim 11, wherein said titania-containing support material consists essentially of titania.

Claim 16

A composition of matter in accordance with claim 11, wherein said at least one iron compound is iron(III) acetylacetonate and said at least one iridium carbonyl compound is Ir 4 (CO) 12 .

Claim 17

A composition of matter in accordance with claim 11, wherein step (a) is carried out with one solution containing said at least one iron compound and said at -east one iridium carbonyl compound.

Claim 18

A composition of matter in accordance with claim 11, wherein step (a) is carried out by impregnation of said support material with a solution comprising at least iron compound, heating the obtained iron-impregnated support material under such conditions as to substantially dry said iron-impregnated support material, and then impregnating said substantially dried iron-impregnated support material with a solution comprising at least one iridium carbonyl compound.

Claim 19

A composition of matter in accordance with claim 11, wherein drying step (b) is carried out at about 30° to about 200° C.

Claim 20

A composition of matter in accordance with claim 11, wherein reducing step (c) is carried out with hydrogen gas at a temperature of about 0° to about 600° C.

Claim 21

A composition of matter in accordance with claim 11 comprising about 0.1-10 weight-% Ir and about 0.1-15 weight-% Fe.

Claim 22

A composition of matter in accordance with claim 11, consisting essentially of iridium metal, iron oxide, and titania as support material.

Claim 23

A process for oxidizing carbon monoxide comprising the steps of contacting a feed gas comprising carbon monoxide and free oxygen with a catalyst composition comprising iridium metal, iron oxide and a titania-containing support material, under such contacting conditions as to at least partially convert CO and O 2 to CO 2 , wherein said catalyst composition has been prepared by a preparation process comprising the steps of (a) impregnating a titania-containing support material with at least one iron compound and at least one iridium carbonyl compound; (b) substantially drying the material obtained in step (a); and (c) treating the substantially dried material obtained in step (b) with a reducing gas under such conditions as to activate said substantially dried material and to obtain said catalyst composition.

Claim 24

A process for oxidizing carbon monoxide comprising the steps of contacting a feed gas comprising carbon monoxide and free oxygen with a catalyst composition comprising iridium metal, iron oxide and a titania-containing support material, under such contacting conditions as to at least partially convert CO and O 2 to CO 2 , wherein said catalyst composition has been prepared by a preparation process comprising the steps of (a) impregnating a titania-containing support material with at least one iron compound and at least one iridium carbonyl compound; (b) substantially drying the material obtained in step (a); and (c) treating the substantially dried material obtained in step (b) with a reducing gas under such conditions as to activate said substantially dried material and to obtain said catalyst composition.

Claim 25

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said titania-containing support material is a titania-coated porous ceramic material.

Claim 26

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said titania-containing support material consists essentially of titania.

Claim 27

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said at least one iron compound is iron(III) acetylacetonate and said at least one iridium carbonyl compound is Ir 4 (CO) 12 .

Claim 28

A process for oxidizing carbon monoxide in accordance with claim 21, wherein step (a) is carried out with one solution containing said at least one iron compound and said at least one iridium carbonyl compound.

Claim 29

A process for oxidizing carbon monoxide in accordance with claim 21, wherein step (a) is carried out by impregnation of said support material with a solution comprising at least iron compound, heating the obtained iron-impregnated support material under such conditions as to substantially dry said iron-impregnated support material, and then impregnating said substantially dried iron-impregnated support material with a solution comprising at least one iridium carbonyl compound.

Claim 30

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said heating of the iron-impregnated support material is carried out at about 100°-500° C. under such conditions as to at least partially convert said at least one iron compound to iron oxide.

Claim 31

A process for oxidizing carbon monoxide in accordance with claim 21, wherein drying step (b) is carried out at about 30° to about 200° C.

Claim 32

A process for oxidizing carbon monoxide in accordance with claim 21, wherein reducing step (c) is carried out with hydrogen gas at a temperature of about 0° to about 600° C.

Claim 33

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said catalyst composition contains about 0.1-10 weight-% Ir and about 0.1-15 weight-% Fe.

Claim 34

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said catalyst composition consists essentially of iridium metal, iron oxide and titania as support material.

Claim 35

A process for oxidizing carbon monoxide in accordance with claim 21, wherein said contacting conditions comprise a reaction temperature in the range of from about -50° to about 400° C. and a volume ratio of CO to O 2 in the feed gas in the range of from about 1:100 to about 100:1.

Claim 36

A process for oxidizing carbon monoxide in accordance with claim 32, wherein said contacting conditions comprise a reaction temperature in the range of from about -30° to about 170° C., a pressure in the range of from about 1 to about 2,000 psia, and a gas hourly space velocity of the feed gas in the range of from about 1 to about 200,000 cc/cc catalyst.