Fabrication of dual porosity electrode structure
Assignee: United States Department of Energy
•
Filing: 1988-10-21
•
Granted: 1991-02-12
•
Expires: 2008-10-21
Abstract
Abstract A substantially entirely fibrous ceramic which may have dual porosity of both micro and macro pores. Total porosity may be 60-75% by volume. A method of spraying a slurry perpendicularly to an ambient stream of air is disclosed along with a method of removing binders without altering the fiber morphology. Adding fine ceramic particulates to the green ceramic fibers enhances the sintering characteristics of the fibers.
Inventors
- 👤 James L. Smith
- 👤 Eugenia H. Kucera
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:13
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/8605; H01M4/8621; C; C04; C04B; C04B30/00; C04B30/02; C04B35/00; C04B35/01; C04B35/016; C04B35/26; C04B35/2691; C04B35/622; C04B35/62227; C04B35/62231; C04B35/626; C04B35/62605; C04B35/62625; C04B35/6264; C04B35/62645; C04B35/62655; C04B35/63; C04B35/632; C04B35/634; C04B35/63404; C04B35/6342; C04B35/71; C04B35/78; C04B35/80; H01M4/90; H01M4/9016; H01M8/00; H01M8/14; H01M8/141; H01M8/142; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3201; C04B2235/3203; C04B2235/3205; C04B2235/3206; C04B2235/3217; C04B2235/3231; C04B2235/3251; C04B2235/3262; C04B2235/3268; C04B2235/327; C04B2235/3272; C04B2235/3274; C04B2235/3275; C04B2235/3281; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/522; C04B2235/526; C04B2235/5264; H01M2004/8678; H01M2004/8684; H01M2004/8689; H01M2008/147; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M2300/0051; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
21 words
An electrode for a molten carbonate fuel cell, comprising a substantially fibrous, dual porosity structure of randomly positioned electrode-active ceramic fibers.
Claim 2
Dependent Claim
21 words
An electrode for a molten carbonate fuel cell, comprising a substantially fibrous, dual porosity structure of randomly positioned electrode-active ceramic fibers.
Claim 3
Dependent Claim
29 words
An electrode for a molten carbonate fuel cell, comprising a dual porosity structure of randomly positioned electrode-active ceramic fibers, further comprising ceramic fine particles sintered to said ceramic fibers.
Claim 4
Dependent Claim
29 words
An electrode for a molten carbonate fuel cell, comprising a dual porosity structure of randomly positioned electrode-active ceramic fibers, further comprising ceramic fine particles sintered to said ceramic fibers.
Claim 5
Dependent Claim
49 words
The electrode for a molten carbonate fuel cell of claim 2, wherein said electrode is a cathode and said electrode-active ceramic fibers are Li 2 MnO 3 doped with an ion of Mg, Nb, Al and Fe or LiFeO 2 doped with an ion of Mn, Co and Cu.
Claim 6
Dependent Claim
35 words
The cathode of claim 2, wherein the weight ratio of ceramic fibers to ceramic particles is from about 2.5 to 1 to about 5 to 1, and said ceramic particles are substantially submicron in size.
Claim 7
Dependent Claim
29 words
The cathode of claim 2, wherein substantially all of said fibers have an effective length of less than about 100 microns and diameters of less than about 10 microns.
Claim 8
Dependent Claim
47 words
The cathode of claim 4, wherein said ceramic fibers have pore sizes sufficiently small to flood upon contact with an alkali metal carbonate electrolyte suitable for a molten carbonate fuel cell and the pores between said ceramic fibers are sufficiently large to pass an oxidant gas therethrough.
Claim 9
Dependent Claim
39 words
The electrode for a molten carbonate fuel cell of claim 1, wherein the structure has macropores in the range of about 10 microns to about 150 microns, and micropores in the range of from submicron to about 5 microns.
Claim 10
Dependent Claim
17 words
The electrode for a molten carbonate fuel cell of claim 1, wherein said electrode is an anode.
Claim 11
Independent Claim
52 words
A method of forming ceramic fibers comprising: providing a slurry of fine ceramic particles and liquid carrier including a binder material and solvent, forming ceramic fibers from the slurry by spraying the slurry into a moving stream of gas, and treating the ceramic fibers formed from the slurry to remove the carrier.
Claim 12
Independent Claim
52 words
A method of forming ceramic fibers comprising: providing a slurry of fine ceramic particles and liquid carrier including a binder material and solvent, forming ceramic fibers from the slurry by spraying the slurry into a moving stream of gas, and treating the ceramic fibers formed from the slurry to remove the carrier.
Claim 13
Dependent Claim
27 words
The method of claim 9, and further including the step of forming the ceramic fibers into a predetermined shape and wherein the solvent is removed by evaporation.
Claim 14
Dependent Claim
17 words
The method of claim 10, wherein the carrier is removed without altering the morphology of the fibers.
Claim 15
Dependent Claim
13 words
The method of claim 11, wherein the carrier is removed by flash burning.
Claim 16
Dependent Claim
34 words
The method of claim 11, wherein the binder material is partially decomposed by maintaining the ceramic fibers at an elevated temperature below the melting point of the binder for a prolonged period of time.
Claim 17
Dependent Claim
33 words
The method of claim 9, wherein the gas is air at ambient temperature and the slurry is sprayed into the gas stream in a direction substantially perpendicular to the direction of gas flow.
Claim 18
Independent Claim
108 words
A method of forming a thin porous sheet of ceramic material comprising: providing a slurry of fine ceramic particles and liquid carrier including a binder material, forming ceramic fibers from the slurry, calcining the ceramic fibers formed from the slurry at a sufficient temperature to drive off the binder, modifying the length of the ceramic fibers to a predetermined range, forming a slip of the ceramic fibers of modified length in a liquid carrier including a binder material and additional fine ceramic particles, spreading a thin layer of the slip onto a substrate, and heating the slip to sintering temperatures to form a porous sheet of ceramic material.
Claim 19
Independent Claim
108 words
A method of forming a thin porous sheet of ceramic material comprising: providing a slurry of fine ceramic particles and liquid carrier including a binder material, forming ceramic fibers from the slurry, calcining the ceramic fibers formed from the slurry at a sufficient temperature to drive off the binder, modifying the length of the ceramic fibers to a predetermined range, forming a slip of the ceramic fibers of modified length in a liquid carrier including a binder material and additional fine ceramic particles, spreading a thin layer of the slip onto a substrate, and heating the slip to sintering temperatures to form a porous sheet of ceramic material.
Claim 20
Dependent Claim
31 words
The method of claim 15, wherein the weight ratio of ceramic fibers to fine ceramic particles is in the range of from about 2.5 to 1 to about 5 to 1.
Claim 21
Dependent Claim
20 words
The method of claim 15, wherein the fine ceramic particles in the slurry have diameters up to about 1 micron.
Claim 22
Dependent Claim
35 words
The method of claim 15, wherein the fibers are formed by injecting the slurry into a stream of air at ambient temperatures in a direction substantially perpendicular to the direction of flow of the airstream.
Claim 23
Dependent Claim
19 words
The method of claim 15, wherein the lengths of the fibers are modified by chopping in a liquid medium.
Claim 24
Dependent Claim
24 words
The method of claim 15, wherein the lengths of the fibers are modified to be shorter than the thickness of the thin porous sheet.
Claim 25
Dependent Claim
83 words
A fuel cell comprising a fuel electrode and an oxidant electrode and an electrolyte disposed between the electrodes, said oxidant electrode comprising randomly positioned ceramic fibers of a cathode-active material and fine ceramic particles sintered to said ceramic fibers, said oxidant electrode having dual porosity of micropores less than 5 microns and macropores greater than 10 microns, said electrolyte containing an alkali metal carbonate and particles distributed therethrough having sizes to ensure flooding of the micropores of the oxidant electrode with the electrolyte.
Claim 26
Dependent Claim
83 words
A fuel cell comprising a fuel electrode and an oxidant electrode and an electrolyte disposed between the electrodes, said oxidant electrode comprising randomly positioned ceramic fibers of a cathode-active material and fine ceramic particles sintered to said ceramic fibers, said oxidant electrode having dual porosity of micropores less than 5 microns and macropores greater than 10 microns, said electrolyte containing an alkali metal carbonate and particles distributed therethrough having sizes to ensure flooding of the micropores of the oxidant electrode with the electrolyte.
Claim 27
Dependent Claim
39 words
The fuel cell of claim 21, wherein the cathodeactive material is selected from Li 2 MnO 3 doped with an ion of Mg, Nb, Al and Fe and LiFeO 2 doped with an ion of Mn, Co and Cu.
Claim 28
Dependent Claim
36 words
The fuel cell of claim 21, wherein the weight ratio of ceramic fibers to fine ceramic particles in the oxidant electrode is in the range of from about 2.5 to 1 to about 5 to 1.
Claim 29
Dependent Claim
45 words
The fuel cell of claim 21, wherein the size of the oxidant electrode micropores are in the range from submicron to less than about 5 microns and the sizes of the macropores are in the range of from about 10 microns to about 150 microns.
Claim 30
Dependent Claim
30 words
The fuel cell of claim 21, wherein the electrolyte is a mixture of Li 2 CO 3 and K 2 CO 3 the particles distributed therethrough are LiAlO 2 .
Claim 31
Dependent Claim
24 words
A ceramic material wherein more than 50 percent by weight of the ceramic is present as fibers having a porosity of 60%-75% by volume.
Claim 32
Dependent Claim
24 words
A ceramic material wherein more than 50 percent by weight of the ceramic is present as fibers having a porosity of 60%-75% by volume.
Claim 33
Dependent Claim
20 words
The ceramic material of claim 26, wherein at least 90 percent by weight of the ceramic is present as fibers.
Claim 34
Dependent Claim
23 words
The ceramic material of claim 26, wherein the material includes submicron ceramic particles present in an amount up to about 40% by weight.
Claim 35
Dependent Claim
44 words
The ceramic material of claim 26, wherein the ceramic is selected from the group consisting of Li 2 MnO 3 doped with an ion of Mg, Nb, Al and Fe and Li 2 FeO 2 doped with an ion of Mn, Co and Cu.
References Cited (Backward Citations)
US4129633A
Cited
US4151235A
Cited
US4407967A
Cited
US4386960A
Cited
US4410607A
Cited
US4526812A
Cited
US4564567A
Cited
US4652411A
Cited
US4650775A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-11 | 1994-08-13 | 1995-02-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-11 | 1998-08-13 | 1999-02-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-11 | 2002-08-13 | 2003-02-12 | $7700.00 | Window Closed / Lapsed |