Method of laser welding
Assignee: Boeing North American Inc
•
Filing: 1990-02-06
•
Granted: 1991-02-05
•
Expires: 2010-02-06
Abstract
Abstract First and second metallic components are joined along a weld path by providing a beam of coherent electromagnetic energy having sufficient power to melt the first and second components and providing a low turbulent flow of an inert shielding gas over a weld region along a portion of the weld path. The beam is focussed on the weld region such that the beam energy is linearly distributed in the direction of the weld path with an intensity sufficient to form a pool of molten metal in the weld region. Relative motion is then established between the components and the beam to cause the weld region to move along the weld path, thereby joining the first and second components along the weld path.
Inventors
- 👤 Ralph J. Moores
- 👤 Daniel S. Gnanamuthu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:19
CPC Classifications
B; B23; B23K; B23K26/00; B23K26/14; B23K26/1462; B23K26/1464; B23K26/147; B23K26/02; B23K26/06; B23K26/073; B23K26/0738; B23K26/20; B23K26/21; B23K26/24; B23K2103/00; B23K2103/08; B23K2103/10; B23K2103/14
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
124 words
A method of joining first and second metallic components along a weld path, comprising the steps of: providing a beam of coherent electromagnetic energy having sufficient power to melt the first and second components; providing a low turbulent flow of an inert shielding gas over a weld region along a portion of the weld path; focusing the beam on the weld region such that the beam energy is linearly distributed in the direction of the weld path with an intensity sufficient to form a pool of molten metal in the weld region; and establishing relative motion between the components and the beam to cause the weld region to move along the weld path, thereby joining the first and second components along the weld path.
Claim 2
Independent Claim
124 words
A method of joining first and second metallic components along a weld path, comprising the steps of: providing a beam of coherent electromagnetic energy having sufficient power to melt the first and second components; providing a low turbulent flow of an inert shielding gas over a weld region along a portion of the weld path; focusing the beam on the weld region such that the beam energy is linearly distributed in the direction of the weld path with an intensity sufficient to form a pool of molten metal in the weld region; and establishing relative motion between the components and the beam to cause the weld region to move along the weld path, thereby joining the first and second components along the weld path.
Claim 3
Dependent Claim
66 words
The method of claim 1, wherein the step of focusing the beam further comprises: focusing the beam on the weld region by concentrating the beam in a direction perpendicular to the direction of the weld path such that the beam energy is linerarly distributed in the direction of the weld path with an intensity sufficient to form a pool of molten metal in the weld region.
Claim 4
Dependent Claim
72 words
The method of claim 2, wherein the step of focusing further comprises: focusing the beam on the weld region by directing the beam through a cylindrical lens, thereby concentrating the beam in a direction perpendicular to the direction of the weld path such that the beam energy is linearly distributed in the direction of the weld path with an intensity sufficient to form a pool of molten metal in the weld region.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein the components have thicknesses in the range of approximately 0.02 inch to 0.1 inch.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the beam has a power of at least approximately 1000 watts.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein the beam is provided by a continuous wave carbon dioxide laser.
Claim 8
Dependent Claim
25 words
The method of claim 1 wherein the energy of the beam is distributed in a weld region approximately 0.03 inch wide and 0.5 inch long.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein the first and second components further comprise titanium aluminide alloys.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein the relative motion between the components and the beam is at least approximately 5 inches per minute.
Claim 11
Dependent Claim
33 words
The method of claim 1 wherein the step of providing a low turbulent flow of shielding gas further comprises providing a shielding hood having at least one gas outlet over the weld region.
Claim 12
Dependent Claim
104 words
The method of claim 10 wherein the shielding hood further comprises: a plate which is porous with respect to the shielding gas for positioning over the weld region; a cover joined to the porous plate such that the cover and the porous plate define a chamber for receiving the shielding gas; a manifold disposed within the chamber for providing a flow of the shielding gas into the chamber; a first opening in the cover; and a second opening in the porous plate, the first and second openings being positioned such that the beam can pass through the hood and impinge on the weld region.
Claim 13
Independent Claim
134 words
A method of joining first and second titanium aluminide alloy components along a weld path, comprising the steps of: providing a laser beam having sufficient power to melt the first and second components; providing a low turbulent flow of an inert shielding gas over a weld region approximately 0.03 inch wide and approximately 0.5 inch long along a portion of the weld path; focusing the beam on the weld region such that approximately 1000 to 5000 watts of beam energy is linearly distributed in the direction of the weld path over the weld region; and establishing relative motion of at least approximately 5 inches per minute between the components and the beam to cause the weld region to move along the weld path, thereby joining the first and second components along the weld path.
Claim 14
Independent Claim
134 words
A method of joining first and second titanium aluminide alloy components along a weld path, comprising the steps of: providing a laser beam having sufficient power to melt the first and second components; providing a low turbulent flow of an inert shielding gas over a weld region approximately 0.03 inch wide and approximately 0.5 inch long along a portion of the weld path; focusing the beam on the weld region such that approximately 1000 to 5000 watts of beam energy is linearly distributed in the direction of the weld path over the weld region; and establishing relative motion of at least approximately 5 inches per minute between the components and the beam to cause the weld region to move along the weld path, thereby joining the first and second components along the weld path.
References Cited (Backward Citations)
US4128753A
Cited
US4577087A
Cited
JPS6099494A
Cited
US4723063A
Cited
JPS62118994A
Cited
US4803335A
Cited
WO1988008353A1
Cited
JPS63268584A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-04 | 1994-08-06 | 1995-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-04 | 1998-08-06 | 1999-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-04 | 2002-08-06 | 2003-02-05 | $7700.00 | Window Closed / Lapsed |