Process for making a silicon carbide composition

Claim 2

A process for preparing a ceramic composite which is comprised of alpha silicon carbide whiskers and alpha aluminum oxide powder, comprising the steps of sequentially: (a) providing a slurry comprised of from about 80 to about 92 volume percent of solid material and from about 20 to about 8 volume percent of non-aqueous liquid, wherein: 1. said solid material comprises from about 30 to about 38 weight percent of aluminum material, from about 10 to about 14 weight percent of amorphous carbon, and from about 52 to about 62 weight percent of silica; 2. said aluminum material has a specific surface area of from about 0.2 to about 1.1 square meters per gram, has a particle size distribution which ranges from about 4 to about 28 microns, and has at least 80 weight percent of its particles being in the range of from about 6 to about 12 microns; 3. said amorphous carbon has a specific surface area of at least 4 square meters per gram;

Claim 3

said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said non-aqueous liquid is volatile at a temperature of 80 degrees centigrade; 6. said slurry is comprised of from about 1 to about 5 weight percent of a source of carbon monoxide, which, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; 7. said slurry is comprised of from about 1 to about 5 weight percent of a source of hydrogen fluoride which, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride; (b) pelletizing said slurry to provide a multiplicity of pellets comprised of from about 80 to about 92 volume percent of solids; (c) drying said pellets to a moisture content of from about 0.1 to about 2.0 weight percent; (d) preheating said dried pellets to a temperature of from about 200 to about 300 degrees centigrade; and (f) igniting said pellets.

Claim 4

said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said non-aqueous liquid is volatile at a temperature of 80 degrees centigrade; 6. said slurry is comprised of from about 1 to about 5 weight percent of a source of carbon monoxide, which, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; 7. said slurry is comprised of from about 1 to about 5 weight percent of a source of hydrogen fluoride which, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride; (b) pelletizing said slurry to provide a multiplicity of pellets comprised of from about 80 to about 92 volume percent of solids; (c) drying said pellets to a moisture content of from about 0.1 to about 2.0 weight percent; (d) preheating said dried pellets to a temperature of from about 200 to about 300 degrees centigrade; and (f) igniting said pellets.

Claim 5

The process as recited in claim 1, wherein said aluminum material is aluminum, and wherein: (a) said composite comprised of alpha silicon carbide and alumina is heated to a temperature of from about 900 to about 1,100 degrees centigrade at a rate of from about 8 to about 15 degrees per minute and, thereafter, (b) the temperature of said composite is raised from a temperature of from about 900 to about 1,100 degrees centigrade to a temperature of from about 1,250 to about 1,350 degrees centigrade.

Claim 6

The process as recited in claim 1, wherein said source of hydrogen fluoride is selected from the group consisting of potassium hydrogen fluoride, sodium hydrogen fluoride, ammonium hydrogen fluoride, and mixtures thereof.

Claim 7

The process as recited in claim 1, wherein said dried pellets are preheated in the presence of nitrogen.

Claim 8

The process as recited in claim 4, wherein said silica has a specific surface area of from about 50 to about 300 square meters per gram.

Claim 9

The process as recited in claim 5, wherein said source of carbon monoxide is a carboxylic acid containing from about 10 to about 24 carbon atoms.

Claim 10

The process as recited in claim 6, wherein said aluminum material is aluminum flakes with a specific surface area of from about 0.6 to about 0.7 square meters per gram.

Claim 11

The process as recited in claim 6, wherein said carboxylic acid is stearic acid.

Claim 12

The process as recited in claim 8, wherein at least about 90 weight percent of said aluminum flakes have a particle size in the range of from about 6 to about 12 microns.

Claim 13

The process as recited in claim 9, wherein said source of hydrogen fluoride is potassium hydrogen fluoride.

Claim 14

The process as recited in claim 10, wherein said amorphous carbon contains less than about 1.5 weight percent of combined sulfur.

Claim 15

The process as recited in claim 11, wherein said non-aqueous liquid is selected from the group consisting of acetone, benzene, toluene, and n-petroleum ether.

Claim 16

The process as recited in claim 12, wherein said dried pellets are preheated for from about 10 to about 40 minutes.

Claim 17

A pellet comprised of from about 98 to about 99.9 weight percent of solid material, having a density of from about 0.3 to about 1.7 grams per cubic centimeter and having a minimum dimension of at least about 4 millimeters, wherein: 1. said pellet comprises from about 30 to about 38 weight percent of aluminum material, from about 10 to about 14 weight percent of amorphous carbon, and from about 52 to about 62 weight percent of silica, from about 1 to about 5 weight percent of a source in a condensed phase of carbon monoxide, and from about 1 to about 5 weight percent of a source in a condensed phase of hydrogen fluoride; 2. said aluminum material has a specific surface area of from about 0.2 to about 1.1 square meters per gram, has a particle size distribution which ranges from about 4 to about 28 microns, and has at least 80 weight percent of its particles being in the range of from about 6 to about 12 microns; 3. said amorphous carbon has a specific surface area of at least 4 square meters per gram; 4. said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said source of carbon monoxide, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; and 6. said source of hydrogen fluoride, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride.

Claim 18

A pellet comprised of from about 98 to about 99.9 weight percent of solid material, having a density of from about 0.3 to about 1.7 grams per cubic centimeter and having a minimum dimension of at least about 4 millimeters, wherein: 1. said pellet comprises from about 30 to about 38 weight percent of aluminum material, from about 10 to about 14 weight percent of amorphous carbon, and from about 52 to about 62 weight percent of silica, from about 1 to about 5 weight percent of a source in a condensed phase of carbon monoxide, and from about 1 to about 5 weight percent of a source in a condensed phase of hydrogen fluoride; 2. said aluminum material has a specific surface area of from about 0.2 to about 1.1 square meters per gram, has a particle size distribution which ranges from about 4 to about 28 microns, and has at least 80 weight percent of its particles being in the range of from about 6 to about 12 microns; 3. said amorphous carbon has a specific surface area of at least 4 square meters per gram; 4. said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said source of carbon monoxide, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; and 6. said source of hydrogen fluoride, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride.

Claim 19

A pellet comprised of from about 98 to about 99.9 weight percent of solid material, having a density of from about 0.3 to about 1.2 grams per cubic centimeter, and having a minimum dimension of at least about 4 millimeters, wherein: 1. said pellet comprises from about 17 to about 22 weight percent of aluminum material, from about 19 to about 24 weight percent of amorphous carbon, from about 56 to about 65 weight percent of silica, from about 1 to about 5 weight percent of a source in a condensed phase of carbon monoxide, and from about 1 to about 5 weight percent of a source in a condensed phase of hydrogen fluoride; 2. said aluminum material has a specific surface area of from about 0.2 to about 1.1 square meters per gram, has a particle size distribution which ranges from about 4 to about 28 microns, and has at least 80 weight percent of its particles being in the range of from about 6 to about 12 microns; 3. said amorphous carbon has a specific surface area of at least 4 square meters per gram; 4. said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said source of carbon monoxide, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; and 6. said source of hydrogen fluoride, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride.

Claim 20

A pellet comprised of from about 98 to about 99.9 weight percent of solid material, having a density of from about 0.3 to about 1.2 grams per cubic centimeter, and having a minimum dimension of at least about 4 millimeters, wherein: 1. said pellet comprises from about 17 to about 22 weight percent of aluminum material, from about 19 to about 24 weight percent of amorphous carbon, from about 56 to about 65 weight percent of silica, from about 1 to about 5 weight percent of a source in a condensed phase of carbon monoxide, and from about 1 to about 5 weight percent of a source in a condensed phase of hydrogen fluoride; 2. said aluminum material has a specific surface area of from about 0.2 to about 1.1 square meters per gram, has a particle size distribution which ranges from about 4 to about 28 microns, and has at least 80 weight percent of its particles being in the range of from about 6 to about 12 microns; 3. said amorphous carbon has a specific surface area of at least 4 square meters per gram; 4. said silica has a specific surface area of from about 1.2 to about 400 square meters per gram; 5. said source of carbon monoxide, when it is subjected to a temperature of from about 700 to about 1,600 degrees centigrade, generates carbon monoxide; and 6. said source of hydrogen fluoride, when subjected to a temperature of from about 200 to about 400 degrees centigrade, generates hydrogen fluoride.